Effect of laser peening with different power densities on vibration fatigue resistance of hydrogenated TC4 titanium alloy
Source abstract
Abstract
Abstract Laser peening (LP) treatment with different power densities was used to improve the vibration fatigue resistance of hydrogenated TC4 titanium alloy. Compressive residual stress (CRS), micro-hardness and micro-structure of hydrogenated LPed specimens were firstly measured. Vibration fatigue test was then carried out to compare the fatigue life and fractures of LPed and non-LPed hydrogenated specimens. It was found that LP-induced high level CRS suppressed the permeation of hydrogen atoms through material surface, which may reduce the hydrogen embrittlement sensitivity. The CRS also prohibited the fatigue crack initiation and propagation by increasing the fatigue limit and crack propagation threshold of hydrogenated specimen. Grain morphologies of α phase and β phase were refined after LP. Beneficial crystal defects inside the α phase and β phase tangled more free hydrogen atoms, which was believed to be crucial factors to inhibit the generation of initial hydrogen-induced crack. Fracture morphologies further confirmed that LP changed the location of fatigue crack initiation (FCI) and slowed down the fatigue crack growth (FCG) rate of hydrogenated specimens. Finally, a strengthening mechanism of LP on the vibration fatigue resistance of hydrogenated specimen was proposed.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Surface Treatment and Residual Stress · Metal and Thin Film Mechanics · Erosion and Abrasive Machining
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (37)
Show source-provided references
1. A state-of-the-art review on passivation and biofouling of Ti and its alloys in marine environments10.1016/j.jmst.2017.11.021 ↗
2. Titanium alloys for marine application10.1016/S0921-5093(98)01180-0 ↗
3. Characterization of titanium alloy Ti-6Al-4V for chemical, marine and industrial applications10.1016/j.matchar.2003.10.006 ↗
4. Compatibility of materials with hydrogen particular case: hydrogen embrittlement of titanium alloys10.1016/j.ijhydene.2009.01.058 ↗
5. Hydrogen embrittlement in different materials: a review10.1016/j.ijhydene.2018.09.201 ↗
6. Effect of cathodic protection potentials on susceptibility to hydrogen embrittlement of E550 steel
7. Hydrogen embrittlement under cathodic protection of friction stir welded UNS S32760 super duplex stainless steel10.1016/j.msea.2017.08.117 ↗
8. Comparison of hydrogen embrittlement susceptibility of three cathodic protected subsea pipeline steels from a point of view of hydrogen permeation10.1016/j.corsci.2017.11.013 ↗
9. Multiaxial fatigue investigation of titanium alloy annular discs by a vibration-based fatigue test10.1016/j.ijfatigue.2016.10.006 ↗
10. Multiaxial fatigue property of Ti-6Al-4V using hollow cylinder specimen under push-pull and cyclic inner pressure loading10.1016/j.ijfatigue.2016.02.019 ↗
11. On the influence of laser peening with different coverage areas on fatigue response and fracture behavior of Ti–6Al–4V alloy10.1016/j.engfracmech.2015.08.026 ↗
12. Effects of laser peening on residual stresses and fatigue crack growth properties of Ti–6Al–4V titanium alloy10.1016/j.optlaseng.2013.06.011 ↗
13. Friction and wear on laser textured Ti6Al4V surface subjected to laser shock peening with contacting foil10.1016/j.optlastec.2017.12.044 ↗
14. Effect of laser shock peening on wear behaviors of TC11 alloy at elevated temperature10.1016/j.optlastec.2018.07.070 ↗
15. Effect of laser peening on friction and wear behavior of medical Ti6Al4V alloy10.1016/j.optlastec.2018.08.005 ↗
16. Laser shock peening for suppression of hydrogen-induced martensitic transformation in stress corrosion cracking10.1115/1.4036530 ↗
17. Zaleski · 2008
18. Hackel LA, Zaleski TM, Chen HL. Laser peening for reducing hydrogen embrittlement. U.S Patent 7,723,643; 2010, p. 5–25.
19. Strengthening mechanism and hydrogen-induced crack resistance of AISI 316L stainless steel subjected to laser peening at different power densities10.1016/j.ijhydene.2018.05.037 ↗
20. Influence of laser peening on the hydrogen embrittlement resistance of 316L stainless steel10.1016/j.surfcoat.2017.08.037 ↗
21. Effects of laser peening with different laser power densities on the mechanical properties of hydrogenated TC4 titanium alloy10.1016/j.ijhydene.2019.05.002 ↗
22. Experiment investigation of laser shock peening on TC6 titanium alloy to improve high cycle fatigue performance10.1016/j.msea.2013.11.073 ↗
23. Effect of laser peening and shot peening on fatigue striations during FCGR study of Ti6Al4V10.1016/j.ijfatigue.2016.08.005 ↗
24. Mechanism of hydrogen embrittlement cracking produced by residual stress from indentation impression10.1016/j.msea.2014.11.008 ↗
25. Effects of laser energy on fatigue crack growth properties of 6061–T6 aluminum alloy subjected to multiple laser peening10.1016/j.engfracmech.2013.01.011 ↗
26. Lee · 2005
27. Hydrogen-induced hardening of Ti–6Al–4V alloy in β phase field10.1016/j.matdes.2013.09.035 ↗
28. The effects of laser peening on high-cycle fatigue in 7085–T7651 aluminum alloy10.1016/j.msea.2007.05.024 ↗
29. Iron GH2036 alloy residual stress thermal relaxation behavior in laser shock processing10.1016/j.optlastec.2015.05.009 ↗
30. Effects of grain size on hydrogen embrittlement in a Fe-22Mn TWIP steel10.1016/j.ijhydene.2015.06.112 ↗
31. Effect of hydrogen on the collective behavior of dislocations in the case of nanoindentation10.1016/j.actamat.2018.01.053 ↗
32. Effect of repeated impacts on mechanical properties and fatigue fracture morphologies of 6061–T6 aluminum subject to laser peening10.1016/j.msea.2012.01.125 ↗
33. Investigation on mechanical properties and microstructural evolution of TC6 titanium alloy subjected to laser peening at cryogenic temperature10.1016/j.msea.2018.07.093 ↗
34. Hydrogen migration and hydrogen-dislocation interaction in austenitic steels and titanium alloy in relation to hydrogen embrittlement10.1016/j.ijhydene.2016.09.212 ↗
35. Improvement in fatigue properties of 2024–T351 aluminum alloy subjected to cryogenic treatment and laser peening10.1016/j.surfcoat.2018.03.088 ↗
36. Microstructure dependent fatigue crack growth in aged hardened aluminium alloys10.1016/j.ijfatigue.2004.04.004 ↗
37. Electron fractography-a tool for the study of micro-mechanisms of fracturing processes