Damage mechanisms in a short glass fiber reinforced polyamide under fatigue loading
Source abstract
Abstract
Abstract This paper presents a damage investigation on a short glass fiber reinforced polyamide (PA66-GF35) under fatigue loading. Plain and notched specimens were tested at room temperature and humidity with load ratio R = 0. Electron microscopy was used to analyze the fracture surface of failed specimens and the crack path of specimens subjected to interrupted fatigue tests. Damage mechanisms were studied investigating the following fractographic features: ductile/brittle matrix fracture behavior, fiber failure/pull-out, degree of fibermatrix interfacial adhesion. The aim of the present paper is to understand the nature of damage initiation and propagation in order to lay the foundations for the development of a multi-scale, mechanism-based lifetime prediction model for short fiber reinforced plastics.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Mechanical Behavior of Composites · Composite Material Mechanics · Structural Behavior of Reinforced Concrete
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (41)
Show source-provided references
1. Fatigue design of highly loaded short-glass-fibre reinforced polyamide parts in engine compartments10.1016/j.ijfatigue.2007.08.017 ↗
2. Modelling of fatigue strength data for a short fiber reinforced polyamide 6.6 based on local strain energy density
3. Life estimation methodology for short fiber reinforced polymers under thermo-mechanical loading in automotive applications10.1002/mawe.201400377 ↗
4. A study of the fatigue behavior of fiber reinforced nylons10.1002/pen.760150403 ↗
5. Fatigue behavior of glass-fiber fortified thermoplastics10.1002/pen.760090610 ↗
6. Hoffmann S. Computational homogenization of short fiber reinforced thermoplastic materials; 2012.
7. Mechanisms of fatigue fracture in short glass fibre-reinforced polymers10.1007/BF01133353 ↗
8. Crack propagation modes in injection molded fiber reinforced thermoplastics
9. Multi-scale modeling in damage mechanics of composite materials10.1007/s10853-006-0210-9 ↗
10. Bridging the length-scale gap-short fibre composite material as an example10.1007/s10853-006-0212-7 ↗
11. Hertzberg · 1980
12. Fatigue of glass and carbon fiber reinforced engineering thermoplastics10.1002/pc.750020311 ↗
13. Effects of fiber orientation and anisotropy on tensile strength and elastic modulus of short fiber reinforced polymer composites10.1016/j.compositesb.2014.11.041 ↗
14. Fatigue fracture mechanisms and fractography of short-glassfibre-reinforced polyamide 610.1023/A:1018634530869 ↗
15. Multiaxial fatigue of a short glass fibre reinforced polyamide 6.6 – fatigue and fracture behaviour10.1016/j.ijfatigue.2009.02.009 ↗
16. Fatigue strength of a clutch pedal made of reprocessed short glass fibre reinforced polyamide10.1016/j.ijfatigue.2009.02.001 ↗
17. Micro-CT investigation on fatigue damage evolution in short fibre reinforced polymers10.1016/j.compscitech.2013.02.008 ↗
18. An experimental investigation of the combined influence of notch size and fibre orientation on the fatigue strength of a short glass fibre reinforced polyamide 610.1016/j.polymertesting.2015.08.002 ↗
19. Effects of processing induced microstructure on the fatigue crack propagation of unfilled and short fibre-reinforced PA-610.1016/0010-4361(90)90239-S ↗
20. Fracture behavior of injection-molded short and long glass fiber—polyamide 6.6 composites10.1016/0266-3538(88)90067-X ↗
21. Fatigue failure mechanisms of short glass-fiber reinforced nylon 66 based on nonlinear dynamic viscoelastic measurement10.1016/S0032-3861(00)00897-1 ↗
22. Roughness-induced crack closure in short fibre-reinforced plastics10.1007/BF00720109 ↗
23. Microfailure behaviour of randomly dispersed short fibre reinforced thermoplastic composites obtained by direct SEM observation10.1007/BF01184987 ↗
24. Microstructure and fracture mechanical properties of short fiber reinforced thermoplastic P.E.T10.1007/BF01388084 ↗
25. Multiaxial fatigue behaviour of a short-fibre reinforced polyamide 6.6 in the presence of notches
26. Fatigue crack propagation in short and long fibre-reinforced injection-moulded PA 6.6 composites10.1016/0010-4361(88)90720-3 ↗
27. Fatigue crack propagation in glass-fibre and glass-sphere filled PBT composites10.1016/0142-1123(88)90015-1 ↗
28. Effect of short fibre reinforcement on the fatigue crack propagation and fracture of PEEK-matrix composites10.1016/0010-4361(86)91004-9 ↗
29. Influence of temperature and thickness on the off-axis behaviour of short glass fibre reinforced polyamide 6.6 – cyclic loading10.1016/j.compositesa.2010.02.004 ↗
30. Fatigue behavior and modeling of short fiber reinforced polymer composites including anisotropy and temperature effects10.1016/j.ijfatigue.2015.02.020 ↗
31. Microstructural efficiency and fracture toughness of short fiber/thermoplastic matrix composites10.1016/0266-3538(85)90090-9 ↗
32. Multiscale fatigue damage characterization in short glass fiber reinforced polyamide-6610.1016/j.compositesb.2014.01.019 ↗
33. Effect of fibre orientation on the fatigue behaviour of a short glass fibre reinforced polyamide-610.1016/j.ijfatigue.2006.04.001 ↗
34. Influence of temperature and thickness on the off-axis behaviour of short glass fibre reinforced polyamide 6.6 – quasi-static loading10.1016/j.compositesa.2010.02.018 ↗
35. In situ damage mechanisms investigation of PA66/GF30 composite: effect of relative humidity10.1016/j.compositesb.2013.11.001 ↗
36. Fatigue damage mechanisms in short fiber reinforced PBT+PET GF3010.1016/j.msea.2010.10.081 ↗
37. Local microstructure and stress distributions at the crack initiation site in a short fiber reinforced polyamide under fatigue loading10.1016/j.polymertesting.2016.06.013 ↗
38. Effects of fiber orientation and moisture on the crack growth in short glass fiber reinforced polyamide10.1002/adem.201100337 ↗
39. The effect of short carbon fibre reinforcement on fatigue crack growth in PEEK10.1016/1359-835X(96)00015-2 ↗
40. Belmonte E, De Monte M, Hoffmann C, Quaresimin M. Influence of fiber loading on the fatigue damage mechanisms in short glass fiber reinforced polyamide, 2016 (in press).10.1016/j.ijfatigue.2016.09.008 ↗
41. Damage mechanisms in short glass fibre reinforced thermoplastic during in situ microtomography tensile tests10.1016/j.compositesb.2015.12.021 ↗