In situ SEM studies of the low cycle fatigue behavior of DZ4 superalloy at elevated temperature: Effect of partial recrystallization
Source abstract
Abstract
Abstract The influence of partial recrystallization (RX) on the low cycle fatigue (LCF) behavior of directionally solidified DZ4 superalloy was studied using in situ scanning electron microscopy. Three typical recrystallization microstructures were prepared on the fatigue samples, via shot peening and subsequent heat treatment. The effect of RX on LCF life is evidently related to the specific RX microstructure. The RX layer does not necessarily reduce the LCF life. The fatigue crack initiation and short crack propagation behaviors for both raw DZ4 and recrystallized samples were in situ examined, which rationalized the observed effect of recrystallization on the LCF life variation.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High Temperature Alloys and Creep · Microstructure and mechanical properties · Nuclear Materials and Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (27)
Show source-provided references
1. Recrystallization and fatigue failure of DS alloy blades10.1016/j.engfailanal.2003.05.014 ↗
2. Temperature effect on low-cycle fatigue behavior of nickel-based single crystalline superalloy10.1007/s10338-008-0833-2 ↗
3. Recrystallisation of single crystal superalloy CMSX-410.1179/026708303225010731 ↗
4. Effect of recrystallisation on microstructural evolution and mechanical properties of single crystal nickel based superalloy CMSX-2 – Part 2 – creep behaviour of surface recrystallised single crystal10.1179/026708303225008347 ↗
5. Damage repair in CMSX-4 alloy without fatigue life reduction penalty10.1007/s11661-004-0364-5 ↗
6. Influence of recrystallization on the high-temperature properties of a directionally solidified Ni-base superalloy10.1007/s11661-007-9387-z ↗
7. Influence of recrystallization on high-temperature stress rupture property and fracture behavior of single crystal superalloy10.1016/j.msea.2012.04.109 ↗
8. Effects of recrystallization on the low cycle fatigue behavior of directionally solidified superalloy DZ40M10.1016/S1001-0521(08)60156-4 ↗
9. Bürgel · 2000 · 229
10. Recrystallization of Ni base superalloy DZ4
11. Recrystallization in a directionally solidified cobalt-base superalloy10.1016/j.msea.2007.07.028 ↗
12. Effect of recrystallization on low-cycle fatigue behavior of DZ4 directionally-solidified superalloy10.4028/www.scientific.net/KEM.306-308.175 ↗
13. Influence of recrystallization layer at surface on fatigue behaviors of directionally solidified DZ4 superalloy
14. In situ observations of the effects of orientation and carbide on low cycle fatigue crack propagation in a single crystal superalloy10.1016/j.proeng.2010.03.245 ↗
15. In situ scanning electron microscopy studies of small fatigue crack growth in recrystallized layer of a directionally solidified superalloy10.1016/j.matlet.2010.06.044 ↗
16. An evaluation on the growth rate of small fatigue cracks in cast AM50 magnesium alloy at different temperatures in vacuum conditions10.1016/j.ijfatigue.2005.03.004 ↗
17. On the fatigue small crack behaviors of directionally solidified superalloy DZ4 by in situ SEM observations10.1016/j.ijfatigue.2010.11.010 ↗
18. Influence of the characteristic of recrystallization grain boundary on the formation of creep cracks in a directionally solidified Ni-base superalloy10.1016/j.msea.2011.10.124 ↗
19. Effects of recrystallization on the low cycle fatigue behavior of directionally solidified superalloy DZ40M10.1016/S1001-0521(08)60156-4 ↗
20. A critical analysis of crack propagation laws10.1115/1.3656900 ↗
21. Tada · 1973
22. The deformation and ageing of mild steel: 3. discussion of results10.1088/0370-1301/64/9/303 ↗
23. Interaction of short cracks with the local microstructure10.1016/j.proeng.2010.03.018 ↗
24. Higher fatigue cracking resistance of twin boundaries than grain boundaries in Cu bicrystals10.1016/j.scriptamat.2011.06.009 ↗
25. Fatigue-life improvement of K417 alloy by shot peening and recrystallization
26. The analysis on the low cycle fatigue behavior of a directionally solidified superalloy with recrystallized surface layers10.4028/www.scientific.net/AMR.44-46.43 ↗
27. Deformation twinning10.1016/0079-6425(94)00007-7 ↗