High temperature fatigue crack growth behaviour of Inconel 718 under hold time and overload conditions
Bibliographic record
Abstract
No abstract is available for this record. The assistant can identify its topic from the title, but cannot infer the study’s results.
Source: Not provided · Quality: missing
Research context
OpenAlex topics: Fatigue and fracture mechanics · High Temperature Alloys and Creep · Mechanical Failure Analysis and Simulation
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (41)
Show source-provided references
1. Reed · 2006
2. High temperature of nickel-base superalloys – a review with special emphasis on deformation modes and oxidation10.1016/j.engfailanal.2009.01.010 ↗
3. Fatigue crack growth behaviour of Inconel 718 with high temperature hold times10.1016/j.proeng.2010.03.118 ↗
4. Effects of loading waveform and stress field on high temperature fatigue crack growth of alloy 71810.1002/mawe.200300663 ↗
5. The effect of microstructure and environment on the crack growth behaviour of Inconel 718 alloy at 650°C under fatigue, creep and combined loading10.1016/0025-5416(82)90167-7 ↗
6. Elevated temperature fatigue crack growth under dwell conditions in Waspaloy10.1016/S0142-1123(97)00056-X ↗
7. Influence of high temperature hold times on the fatigue crack propagation in Inconel 71810.1016/j.ijfatigue.2011.05.011 ↗
8. Fatigue crack growth behaviour of Inconel 718 – the concept of a damaged zone caused by high temperature hold times10.1016/j.proeng.2011.04.469 ↗
9. Effects of the environment on the crack propagation behavior of IN718 in the temperature range of the dynamic embrittlement10.1520/JAI103569 ↗
10. Hold-time effect on the thermo-mechanical fatigue crack growth behaviour of Inconel 71810.1016/j.msea.2011.08.027 ↗
11. Weerasooriya T. Effect of frequency on fatigue crack growth rate of Inconel 718 at high temperature. In: Fracture mechanics: 19th symp. ASTM. 969; 1988. p. 907–23.10.1520/STP33112S ↗
12. Creep crack initiation and growth in Inconel 718 alloy at 650°C10.1111/j.1460-2695.1987.tb01156.x ↗
13. Gas phase embrittlement and time dependent cracking of nickel based superalloys10.1179/174892306X99679 ↗
14. Oxygen-induced intergranular cracking of a Ni-based alloy at elevated temperatures – an example of dynamic embrittlement10.1016/S1359-6454(01)00005-2 ↗
15. Elevated temperature fatigue crack growth in alloy 718 – Part II: Effects of environmental and material variables10.1111/j.1460-2695.1993.tb00103.x ↗
16. Intergranular crack tip oxidation mechanisms in nickel-based superalloy10.1016/0921-5093(92)90358-8 ↗
17. Oxidation effects on the fatigue crack growth behavior of alloy 718 at high temperature10.1016/S1359-6454(96)00192-9 ↗
18. Fatigue crack propagation of nickel-base superalloys at 650°C
19. A model for predicting the effect of frequency on fatigue crack growth behaviour at elevated temperature10.1111/j.1460-2695.1980.tb01364.x ↗
20. A model for representing and predicting the influence of hold time on fatigue crack growth behaviour at elevated temperature
21. Depth of intergranular oxygen diffusion during environment-dependent fatigue crack propagation in alloy 71810.1016/0921-5093(92)90107-C ↗
22. Prediction of time dependent crack growth with retardation effects in nickel base alloys
23. High temperature fatigue crack growth rate in Inconel 718: dwell effect annihilations10.1016/S1566-1369(02)80082-6 ↗
24. Dynamic embrittlement – time-dependent quasi-brittle intergranular fracture at high temperatures10.1179/174328005X14320 ↗
25. The effect of grain-boundary-engineering-type processing on oxygeninduced cracking of IN718
26. High temperature fatigue crack growth in Inconel 71810.1179/mht.2000.058 ↗
27. Influence of stress state on high temperature fatigue crack growth in Inconel 718
28. Fatigue behaviour of the nickel-based superalloy IN718 at elevated temperature10.1080/09603409.1994.11752529 ↗
29. ASME E647-08. Standard test method for measurement of fatigue crack growth rates. Annual Book of ASME Standards, vol. 03.01, West Conshohocken (PA): ASM International 2008.
30. ASTM E740-03. Standard practice for fracture testing with surface-crack tension specimens, Annual Book of ASME Standards, vol. 03.01, West Conshohocken (PA): ASM International 2003.
31. Sulfur-induced dynamic embrittlement in a low-alloy steel10.1016/0956-7151(94)00388-X ↗
32. Fatigue crack propagation of Ni-based superalloys
33. A critical assessment of fatigue crack nucleation and growth models for Ni- and Ni,Fe-based superalloys10.1179/095066010X12777205875796 ↗
34. Irwin GR. Plastic zone near a crack and fracture mechanics. In: Proceedings of the 7th Sagamore research conference on fracture, vol. 4; 1960. p. 63.
35. Janssen · 2004
36. On the finite element analysis of fatigue crack closure 1. Basic modeling issues10.1016/0013-7944(89)90027-1 ↗
37. Finite element analysis of plasticity-induced fatigue crack closure: an overview10.1016/S0013-7944(03)00099-7 ↗
38. Numerical simulation of plasticity-induced fatigue crack closure with emphasis on the crack growth scheme: 2d and 3d analyses10.1016/j.engfracmech.2007.10.017 ↗
39. Abaqus Software. Abaqus theory manual (6.10). Dassault Systémes Simulia Corp., Providence; 2010.
40. Fatigue crack propagation and closure behavior of modified 1070 steel: finite element study10.1016/S0013-7944(96)00104-X ↗
41. A critical analysis of crack propagation laws10.1115/1.3656900 ↗