Effect of volume fraction of phases and precipitates on the mechanical behavior of UNS S31803 duplex stainless steel
Source abstract
Abstract
Abstract Mechanical properties of a grade UNS S31803 duplex stainless steel were studied. Samples were annealed at three different temperatures, 1060 °C, 1200 °C, and 1300 °C, to change the α/γ proportion, to precipitate undesirable phases (for example, α′, σ and chromium nitrides), and to study the effect of the microstructure on the mechanical behavior. Specimens with a thickness of 1.8 mm were prepared according to ASTM standards and tested at room temperature. Tensile tests were conducted using displacement control at a rate of 5 mm/min. Force-controlled constant amplitude axial fatigue tests were conducted at a frequency of 30 Hz and an R stress ratio of 0.1. Microstructural analyses, performed by optical microscopy and scanning electron microscopy, showed the following modifications to the microstructure: changes in the phase volume fractions, the phase grain growths, and the morphology of the γ-phase and the precipitation of chromium nitrides in the α-phase. The mechanical properties of the steel were significantly changed due to the changed microstructure. The results demonstrate the sensitivity of the steel to the annealing temperature.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Hydrogen embrittlement and corrosion behaviors in metals · Microstructure and Mechanical Properties of Steels · Metal and Thin Film Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (54)
Show source-provided references
1. Soluções sustentáveis em aço inoxidável para toda a cadeia de óleo e gás. APERAM South America; www.aperam.com (accessed 3.04.2013).
2. Charles J, Faria RA. Aços inoxidáveis duplex e aplicações em óleo e gás; www.nucleoinox.org.br/upfiles/arquivos/downloads/inox08/pg_247-254.pdf (accessed 03.04.2013).10.4236/ojst.2013.34043 ↗
3. Davis · 1996
4. Effect of intermetallic precipitations on the properties of duplex stainless steel10.1016/j.matchar.2006.03.015 ↗
5. Tankers – a composition in duplex stainless steels
6. Influence of thermal cycling on the microstructure of a ferritic–austenitic duplex stainless steel10.1016/1044-5803(95)80082-4 ↗
7. Duplex – a new generation of stainless steels for desalination plants10.1016/j.desal.2006.02.051 ↗
8. Erosion–corrosion of 2205 duplex stainless steel in flowing seawater containing sand particles10.1016/j.corsci.2006.08.023 ↗
9. IMOA (International Molybdenum Association). Practical Guidelines for the Fabrication of Duplex Stainless Steel, 2nd ed. London; 2009. 64 page.
10. Moreno JRS. Degradação da resistência à corrosão de aços inoxidáveis duplex devido ao envelhecimento em baixas temperaturas por tempos prolongados. Thesis. UFSCar, Brazil; 2004. 196 page.
11. Pinto TB. Comportamento mecânico de um aço inoxidável duplex do tipo 2205 sob a influência da temperatura e da precipitação de fases frágeis. Thesis. Unicamp, Brazil, 2001. 214 page.
12. Fontes TF. Efeito da fase α′ nas propriedades mecânicas e de resistência à corrosão do aço inoxidável duplex UR 52N+. Dissertation. IPEN, Brazil; 2009. 93 page.
13. Qualitative and quantitative analysis of σ and χ phases in 2205 duplex stainless steel10.1016/j.matchar.2005.11.003 ↗
14. Sigma phase precipitation in duplex stainless steel 220510.1016/j.msea.2006.08.107 ↗
15. Kinetics of sigma phase formation in a duplex stainless steel10.1590/S1516-14392009000300012 ↗
16. Magnabosco R, Bruno D. Efeito do envelhecimento a 475 C na microestrutura e corrosão por pite do aço inoxidável dúplex UNS S31803 (SAF 2205). In: 62 Congresso Internacional Anual da ABM, Vitória, Brazil; 2007.10.5151/2594-5327-2005-14833-0030 ↗
17. Estudo das transformações de fase do aço inoxidável duplex UNS S31803 quando submetido a altas temperaturas
18. Phase tansformation and mechanical behavior in annealed 2205 duplex stainless steel welds10.1016/j.matchar.2007.03.004 ↗
19. Microstructural characterization and the effect of phase transformations on toughness of the UNS S31803 duplex stainless steel age treated at 850°C10.1590/S1516-14392002000300026 ↗
20. Effect of the annealing temperature on the mechanical properties, formability and corrosion resistance of hot-rolled duplex stainless steel10.1016/j.jmatprotec.2008.04.026 ↗
21. The low-temperature aging embrittlement in a 2205 duplex stainless steel10.1016/j.msea.2003.12.051 ↗
22. Study of decomposition of ferrite in a duplex stainless steel cold worked and aged at 450–500°C10.1016/j.msea.2008.09.021 ↗
23. Phase transformations evaluation on a UNS S31803 duplex stainless steel based on non-destructive testing10.1016/j.msea.2009.03.004 ↗
24. Low-temperature embrittlement of duplex stainless steel: correlation between mechanical and electrochemical behavior10.1016/j.msea.2010.02.069 ↗
25. ASTM E8M. Standard Test Methods for Tension Testing of Metallic Materials.
26. ASTM E466-07. Standard Practice for Conducting Force Controlled Constant Amplitude Axial Fatigue Tests of Metallic Materials.
27. Reis TJA, Andrade MS, Godefroid LB. Efeito de tratamentos isotérmicos a 475 C e a 850 C na resistência à fadiga de um aço inoxidável duplex UNS S32304. In: 68 Congresso Internacional Anual da ABM, Belo Horizonte, Brazil; 2012.
28. Influence of the microstructure on the toughness of a duplex stainless steel UNS S3180310.1007/s10853-005-5700-7 ↗
29. Godefroid · 2012
30. Llanes L, Mateo A, Anglada M. Cyclic response of duplex stainless steel – an intrinsic two-phase description. In: Proceedings of the Sixth International Fatigue Conference. Berlin/Germany, Pergamon; 1996. p. 87–92.
31. Mateo A, Violan P, Llanes L, Mendez J, Anglada M. Fatigue life of duplex stainless steel – influence of ageing and environment. In: Proceedings of the Sixth International Fatigue Conference. Berlin/Germany, Pergamon; 1996. p. 209–214.
32. Chai G, Sundqvist M. Fatigue strength and crack behavior of duplex stainless steel. In: Proceedings of the Seventh International Fatigue Conference. Beijing/China, EMAS, 1999. p. 175–180.
33. Baffie N, Gironès A, Mateo A, Anglada M, Stolarz J. Influence of interfaces on LCF short crack propagation in the bulk in single phase and in duplex stainless steels. In: Proceedings of the Seventh International Fatigue Conference. Beijing/China, EMAS, 1999. p. 359–364.
34. High cycle fatigue behaviour of a standard duplex stainless steel plate and bar10.1016/S0921-5093(01)01096-6 ↗
35. Microstructure and damage initiation in duplex stainless steels10.1016/S0921-5093(01)01196-0 ↗
36. Role of microstructure on fatigue properties of 475C aged duplex stainless steel10.1016/S0142-1123(01)00187-6 ↗
37. Mateo A, Gironès A, Llanes L, Anglada, M. Cyclic deformation and fatigue behavior of duplex stainless steel. In: Proceedings of the Eighth International Fatigue Conference. Stockholm/Sweden, EMAS; 2002. p. 461–472.
38. Stolarz J, Baffie N. Low cycle fatigue of aged duplex steels. In: Proceedings of the Eighth International Fatigue Conference. Stockholm/Sweden, EMAS; 2002. p. 2831–2838.
39. Anisotropy effects on the fatigue behaviour of rolled duplex stainless steels10.1016/S0142-1123(02)00173-1 ↗
40. EBSD studies on the influence of texture on the surface damage mechanisms developed in cyclically loaded aged duplex stainless steels10.1016/j.msea.2004.01.105 ↗
41. Fatigue behavior of duplex stainless steels in the very high cycle regime10.1016/j.ijfatigue.2005.06.054 ↗
42. Düber O, Künkler B, Krupp U, Christ HJ, Fritzen CP. Short crack propagation in duplex stainless steel. In: Proceedings of the Ninth International Fatigue Conference. Atlanta/USA, Elsevier; 2006, CD_ROM.
43. Microstructure associated with crack initiation during low-cycle fatigue in a low nitrogen duplex stainless steel10.1016/j.ijfatigue.2006.06.002 ↗
44. The influence of temperature on the cyclic behavior of aged and unaged super duplex stainless steels10.1016/j.msea.2008.02.028 ↗
45. Identification and analysis of slip systems activated during low-cycle fatigue in a duplex stainless steel10.1016/j.scriptamat.2008.07.044 ↗
46. Microcrack growth and fatigue behavior of a duplex stainless steel10.1016/j.ijfatigue.2008.12.007 ↗
47. Surface observation and measurement techniques to study the fatigue damage micromechanisms in a duplex stainless steel10.1016/j.ijfatigue.2008.11.003 ↗
48. Activated slip systems and microcrack path in LCF of a duplex stainless steel10.1016/j.msea.2009.01.012 ↗
49. Low cycle fatigue behavior of duplex stainless steel – influence of isothermal aging treatment10.1111/j.1460-2695.2009.01413.x ↗
50. Propagation behaviour of microstructural short fatigue cracks in the high-cycle fatigue regime10.1016/j.commatsci.2009.01.019 ↗
51. Experimental characterization of short fatigue crack kinetics in an austeno-ferritic duplex steel10.1016/j.proeng.2011.04.249 ↗
52. Fatigue crack initiation behavior in embrittled austenitic–ferritic stainless steel10.1016/j.ijfatigue.2012.06.018 ↗
53. Short crack nucleation and growth in lean duplex stainless steel fatigue at room temperature10.1016/j.ijfatigue.2012.01.011 ↗
54. Growth of short cracks during low and high cycle fatigue in a duplex stainless steel10.1016/j.ijfatigue.2012.01.010 ↗