The influence of cyclic ageing on the fatigue performance of bonded joints
Source abstract
Abstract
Although the cyclical environment can significantly influence the fatigue performance of the bonded joints, however, the interactions of cyclic ageing and fatigue loading on the mechanical performance of bonded joints have not been studied yet. Accordingly, the aim of the current study is to investigate the influence of cyclic ageing on the fatigue behaviour of epoxy adhesive joints using Arcan samples. Accordingly, different ageing frequencies, different ageing and drying cycles, and different loading conditions are analysed. As a result, performing a single ageing analysis overestimates the life of adhesive joints if they are exposed to cyclic environments. Results also showed that the life cycle decreases with the ageing frequency.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Mechanical Behavior of Composites · Structural Load-Bearing Analysis · Fatigue and fracture mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (28)
Show source-provided references
1. da Silva, L.F.M., A. Öchsner, and R.D. Adams, Handbook of adhesion technology. Vol. 2018: Springer.10.1007/978-3-319-55411-2 ↗
2. Adhesively bonded joints in composite materials: an overview10.1243/14644207JMDA219 ↗
3. Fatigue behavior of carbon fibre reinforced plastic and aluminum single-lap adhesive joints after the transverse pre-impact10.1016/j.ijfatigue.2020.105973 ↗
4. Evaluation of multiaxial fatigue life prediction approach for adhesively bonded hollow cylinder butt-joints10.1016/j.ijfatigue.2021.106692 ↗
5. Fatigue life evaluation of adhesive joints in a real structural component10.1016/j.ijfatigue.2021.106504 ↗
6. Environmental effect on the fatigue degradation of adhesive joints: a review10.1080/00218464.2016.1179117 ↗
7. Effects of temperature and moisture on the fracture behaviour of composite adhesive joints10.1016/j.ijadhadh.2020.102607 ↗
8. Moisture absorption–desorption effects in adhesive joints10.1016/j.ijadhadh.2009.05.001 ↗
9. Effect of humidity on the mechanical properties of adhesively bonded aluminium joints Proceedings of the Institution of Mechanical Engineers, Part L:
10. A review on the environmental degradation effects on fatigue behaviour of adhesively bonded joints10.1111/ffe.13239 ↗
11. Effect of hygrothermal aging on the quasi-static behaviour of CFRP joints varying the overlap length10.1016/j.compstruct.2019.02.035 ↗
12. Effects of cyclic ageing on the tensile properties and diffusion coefficients of an epoxy-based adhesive Proceedings of the Institution of Mechanical Engineers, Part L:
13. Experimental and numerical analysis of cyclic aging in an epoxy-based adhesive10.1016/j.polymertesting.2020.106789 ↗
14. Houjou, K., et al., Effect of cyclic moisture absorption/desorption on the strength of epoxy adhesive joints and moisture diffusion coefficient. The Journal of Adhesion, 2021: p. 1-17.10.1080/00218464.2021.1926242 ↗
15. Effect of cyclic hygrothermal aging on mechanical behaviours of adhesive bonded aluminum joints10.1080/01694243.2020.1794205 ↗
16. Effects of hygrothermal aging on the mechanical properties of aluminum alloy adhesive joints for high-speed train applications
17. Effect of hygrothermal aging and cyclic thermal shocks on the mechanical performance of single-lap adhesive joints10.1016/j.ijadhadh.2020.102584 ↗
18. Fatigue performance of single lap joints with CFRP and aluminium substrates prior and after hygrothermal aging10.1111/ffe.13067 ↗
19. Mu, W.-L., et al., Influence of temperature and humidity on the fatigue behaviour of adhesively bonded CFRP/aluminium alloy joints. The Journal of Adhesion, 2021: p. 1-19.
20. Interfacial toughness: dependence on surface roughness and test temperature10.1007/s10704-019-00419-0 ↗
21. Fracture mechanics approach to stress singularity in adhesive joints10.1007/s10704-021-00594-z ↗
22. Residual static strength and the fracture initiation path in adhesively bonded joints weakened with interfacial edge pre-crack10.1080/01694243.2018.1458812 ↗
23. The influence of interfacial failure on the tensile S-N response of aged Arcan joints10.1002/app.51991 ↗
24. da Costa, J.A., et al., Cyclic ageing of adhesive materials. The Journal of Adhesion, 2021: p. 1-17.
25. Heat/mass transfer analogy in the case of convective fluid flow through minichannels10.1016/j.ijthermalsci.2020.106467 ↗
26. Cranck, J., The mathematics of diffusion, 2nd edn. Clarendon. 1975, Oxford.
27. da Silva, L.F.M., A. Öchsner, and R.D. Adams, Handbook of adhesion technology. Vol. 1. 2011: Springer.10.1007/978-3-642-01169-6_1 ↗
28. da Costa, J.A., et al., Effects of ageing frequency on the interfacial failure and tensile properties of adhesively bonded Arcan joints exposed to cyclic ageing environments. Proceedings of the Institution of Mechanical Engineers, Part E: Journal of Process Mechanical Engineering, 2022: p. 09544089221089703.10.1177/09544089221089703 ↗