Evolution of damage under combined low and high cycle fatigue loading in a type 316LN stainless steel at different temperatures
Source abstract
Abstract
Abstract The present study investigates the effect of different damage modes like low cycle fatigue (LCF), high cycle fatigue (HCF), creep and ratcheting during combined cycling at various temperatures ranging from ambient to 923 K, in a type 316LN austenitic stainless steel. The experiments were designed with multi-step load sequences where specific number of small amplitude HCF cycles (referred to as blocks ) were introduced at the stabilized cyclic load under LCF for a given strain amplitude and repeated until failure. Cyclic life was found to decrease with increase in temperature as well as block-size. The decrease in cyclic life with block-size is more significant at 923 K where multiple damage modes like creep and ratcheting are activated. Dynamic strain aging (DSA) was found to operate in the temperature range, 823–873 K where the decrease in cyclic life with block-size gets saturated. Typically, transgranular fatigue fracture, intergranular creep fracture or dimpled rupture was identified when failure was dictated by LCF, creep and ratcheting respectively. However, synergistic interaction between the above damage modes leading to a mixed mode fracture carrying signatures of fatigue striations, intergranular facets and dimples occurred at specific combinations of block size and temperature. HCF damage played an important role for some specific loading conditions by acting as a link between intergranular (creep) cracks, thus facilitating the crack propagation and final failure. The regimes of dominant failure modes and interactions among them were suitably mapped as a function of temperature and block size.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High Temperature Alloys and Creep · Fatigue and fracture mechanics · Fire effects on concrete materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (47)
Show source-provided references
1. Chellapandi · Trans Indian Inst Met · 2005 · 58 · 207
2. Chellapandi P. Report No. TWF-FR/144, IAEA Workshop on codes and standards of Fast reactors, Beijing, China; 2010.
3. Bhoje SB, Chellapandi P. Proc. technical committee meeting, IAEA Tech. Doc 933, Manchester, UK; 1997. p. 97–115.
4. Mathew · Ener Proc · 2011 · 7 · 25010.1016/j.egypro.2011.06.032 ↗
5. Chellapandi · Nucl Eng Des · 2009 · 239 · 274510.1016/j.nucengdes.2009.08.014 ↗
6. Schweizer · Int J Fract · 2011 · 33 · 194
7. Sarkar · High Temp Mater Proc · 2015 · 34 · 43510.1515/htmp-2014-0090 ↗
8. Sarkar · Met Mater Trans A · 2017 · 48 · 95310.1007/s11661-016-3909-5 ↗
9. Sarkar · Mater Sci Eng A · 2017 · 683 · 2410.1016/j.msea.2016.11.062 ↗
10. Zheng · Mater Sci Eng A · 2013 · 560 · 79210.1016/j.msea.2012.10.037 ↗
11. Jelaska · Facta Universitatis, Series: Mechanics, Automatic Control and Robotics · 2003 · 3 · 635
12. Geldemin · Proc Eng · 2010 · 2 · 134310.1016/j.proeng.2010.03.146 ↗
13. Okazaki M, Muzvidizawa M, Iwasaki A, Kasahara N. Adv Maintenance, Jpn Soc Maintainology 2014; 6: 24–32.
14. Beck · Mater Sci Eng A · 2007 · 468–470 · 18410.1016/j.msea.2006.05.177 ↗
15. Powell · Int J Fatigue · 1997 · 19 · S16710.1016/S0142-1123(97)00016-9 ↗
16. Bhanu Sankara Rao K. PhD Thesis, University of Madras; 1989.
17. Srinivasan · Scr Mater · 1997 · 37 · 159310.1016/S1359-6462(97)00282-0 ↗
18. Srinivasan · Int J Fatigue · 1991 · 13 · 47110.1016/0142-1123(91)90482-E ↗
19. Prasad Reddy · Procedia Eng · 2010 · 2 · 218110.1016/j.proeng.2010.03.234 ↗
20. Ganesan · Mater High Temp · 2014 · 31 · 16210.1179/1878641314Y.0000000009 ↗
21. Srinivasan · Int J Fatigue · 1999 · 21 · 1110.1016/S0142-1123(98)00052-8 ↗
22. Sarkar Aritra, Nagesha A, Sandhya R, Laha K, Okazaki M. (Unpublished results).
23. Sarkar · Trans Indian Inst Met · 2015 · 69 · 39910.1007/s12666-015-0748-9 ↗
24. Haupt · ASME J Eng Mater Technol · 1996 · 118 · 28110.1115/1.2806806 ↗
25. Mizuno · Trans ASME J Eng Mater Technol · 2000 · 122 · 2910.1115/1.482761 ↗
26. Ohno · Int J Plast · 1998 · 14 · 35510.1016/S0749-6419(98)00009-6 ↗
27. Paul · Mater Sci Eng A · 2011 · 528 · 487310.1016/j.msea.2011.03.048 ↗
28. Sarkar · Mater Sci Eng A · 2013 · 564 · 35910.1016/j.msea.2012.11.115 ↗
29. Sarkar · Proc Eng · 2013 · 55 · 65010.1016/j.proeng.2013.03.309 ↗
30. Sarkar · Mater High Temp · 2012 · 29 · 35110.3184/096034012X13493571408802 ↗
31. Ray · Proc Eng · 2010 · 2 · 180510.1016/j.proeng.2010.03.194 ↗
32. Kang · Theor Appl Fract Mech · 2005 · 43 · 19910.1016/j.tafmec.2005.01.005 ↗
33. Bochet · Int J Plast · 2001 · 17 · 149110.1016/S0749-6419(01)00013-4 ↗
34. Paul · Theor Appl Fract Mech · 2010 · 54 · 6310.1016/j.tafmec.2010.06.016 ↗
35. Kang · 2005
36. Paul · Theor Appl Fract Mech · 2010 · 54 · 6310.1016/j.tafmec.2010.06.016 ↗
37. Kang · Nucl Eng Des · 2002 · 216 · 1310.1016/S0029-5493(02)00062-6 ↗
38. Kang · J Iron Steel Res Int · 2007 · 14 · 5310.1016/S1006-706X(07)60012-0 ↗
39. Feaugas · Int J Plast · 2005 · 20 · 64310.1016/S0749-6419(03)00076-7 ↗
40. Gao · Theor Appl Fract Mech · 2003 · 40 · 10510.1016/S0167-8442(03)00038-7 ↗
41. Kang · Mech Mater · 2002 · 34 · 14510.1016/S0167-6636(01)00099-0 ↗
42. Kang · Theor Appl Fract Mech · 2005 · 43 · 19910.1016/j.tafmec.2005.01.005 ↗
43. Kang · Fatigue Fract Eng Mater Struct · 2006 · 29 · 9310.1111/j.1460-2695.2006.00964.x ↗
44. Kang · Int J Fatigue · 2008 · 30 · 144810.1016/j.ijfatigue.2007.10.002 ↗
45. Dieter · 1988
46. Rider · Int J Fatigue · 1995 · 17 · 50710.1016/0142-1123(95)00046-V ↗
47. Kwofie · Mater Sci Eng A · 2006 · 427 · 26310.1016/j.msea.2006.04.105 ↗