Influence of deposition strategy on the microstructure and fatigue properties of laser metal deposited Ti-6Al-4V powder on Ti-6Al-4V substrate
Source abstract
Abstract
Abstract Fatigue testing was conducted to investigate the potential of applying Laser Metal Deposition (LMD) as a repair method for Ti-6Al-4V aerospace components. Ti-6Al-4V powder was laser deposited on Ti-6Al-4V specimens with two different deposition strategies: a raster pattern with a continuous deposit (LMD-1) and a raster pattern deposit with an inter-track pause (LMD-2). The results showed fatigue lives of LMD-1 were higher when compared to LMD-2. This was mainly due to the high number of defects in LMD-2, mostly lack of fusion (LOF) defects. Despite the high number of defects, fracture surfaces for both LMD-1 and LMD-2 showed initiation to be from oxygen enriched inclusions, which could be related to contamination. This study shows the deposition strategy influences fatigue lives when laser depositing Ti-6Al-4V powder on Ti-6Al-4V substrate and there are possibilities of oxygen and nitrogen related inclusions that introduce brittle regions that are more detrimental to the fatigue performance than LOF defects or gas pores.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Additive Manufacturing Materials and Processes · Welding Techniques and Residual Stresses · Titanium Alloys Microstructure and Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (63)
Show source-provided references
1. Miedlar · 2002
2. The role of laser additive manufacturing methods of metals in repair, refurbishment and remanufacturing – enabling circular economy10.1016/j.phpro.2016.08.077 ↗
3. Plourde · 2004
4. Laser metal deposition as repair technology for stainless steel and titanium alloys10.1016/j.phpro.2012.10.051 ↗
5. Laser cladding of aerospace materials10.1016/S0924-0136(01)01121-9 ↗
6. Near-net-shape rapid manufacture and repair by LENS®
7. Laser cladding as a potential repair technology for damaged aircraft components10.1108/17579861111162914 ↗
8. Component repair using laser direct metal deposition
9. The application of laser cladding to mechanical component repair, renovation and regeneration
10. Fatigue life prediction of additively manufactured material: Effects of surface roughness, defect size, and shape10.1111/ffe.12799 ↗
11. Effect of microstructure and defects on fatigue behaviour of directed energy deposited Ti–6Al–4V10.1179/1362171815Y.0000000050 ↗
12. Analysis of the stress raising action of flaws in laser clad deposits10.1016/j.matdes.2012.10.010 ↗
13. Fatigue behavior of Ti-6Al-4V alloy Additively Manufactured by laser engineered net shaping
14. Microstructure evolution, tensile properties, and fatigue damage mechanisms in Ti-6Al-4V alloys fabricated by two additive manufacturing techniques10.1016/j.proeng.2015.08.007 ↗
15. Fatigue crack growth behavior and microstructural mechanisms in Ti-6Al-4V manufactured by laser engineered net shaping10.1016/j.ijfatigue.2016.08.009 ↗
16. Fatigue behavior and failure mechanisms of direct laser deposited Ti–6Al–4V10.1016/j.msea.2015.12.026 ↗
17. Critical assessment of the fatigue performance of additively manufactured Ti–6Al–4V and perspective for future research10.1016/j.ijfatigue.2015.12.003 ↗
18. Material defects as the basis of fatigue design10.1016/j.ijfatigue.2011.12.001 ↗
19. Jeal · 1988
20. Fatigue characterization of Titanium Ti-6Al-4V samples produced by additive manufacturing10.1016/j.prostr.2016.06.395 ↗
21. Effects of defects in laser additive manufactured Ti-6Al-4V on Fatigue properties10.1016/j.phpro.2014.08.120 ↗
22. The effect of manufacturing defects on the fatigue behaviour of Ti-6Al-4V specimens fabricated using selective laser melting
23. The influence of porosity on fatigue crack initiation in additively manufactured titanium components10.1038/s41598-017-06504-5 ↗
24. Distortion minimization of laser-processed components through control of laser scanning patterns10.1108/13552540210451732 ↗
25. Residual stresses in steel specimens induced by laser cladding and their effect on fatigue strength10.1016/j.phpro.2012.10.048 ↗
26. Additive manufacturing and postprocessing of Ti-6Al-4V for superior mechanical properties10.1557/mrs.2016.215 ↗
27. Phase transformations during cooling in α+β titanium alloys10.1016/S0921-5093(97)00802-2 ↗
28. Microstructure, static properties, and fatigue crack growth mechanisms in Ti-6Al-4V fabricated by additive manufacturing: LENS and EBM10.1016/j.engfailanal.2016.05.036 ↗
29. The effect of laser power and traverse speed on microstructure, porosity and build height in laser-deposited Ti-6Al-4V10.1016/S1359-6462(00)00408-5 ↗
30. Modeling of laser deposition and repair process10.2351/1.1848523 ↗
31. Fabrication of large Ti–6Al–4V structures by direct laser deposition10.1016/j.jallcom.2014.12.234 ↗
32. Microstructures of laser-deposited Ti–6Al–4V10.1016/j.matdes.2003.09.009 ↗
33. An overview of direct laser deposition for additive manufacturing; Part II: mechanical behavior, process parameter optimization and control
34. Mechanical properties and microstructural features of direct laser-deposited Ti-6Al-4V10.1007/s11837-015-1308-9 ↗
35. Amsterdam E, Kool GA. High cycle fatigue of laser beam deposited Ti-6Al-4V and Inconel 718. In: B. MJ, editors. Proceedings of the 25th Symposium of the International Committee on Aeronautical Fatigue Dordrecht: Springer 2009, p. 1261-1274.10.1007/978-90-481-2746-7_71 ↗
36. Thermal stresses and deposition patterns in layered manufacturing10.1016/S0921-5093(01)01179-0 ↗
37. Physics ProcediaInfluence of laser deposition patterns on part distortion, interior quality and mechanical properties by laser solid forming (LSF)10.1016/j.msea.2010.09.078 ↗
38. Effect of building strategy on sample dimensions and properties in direct laser deposition of TI-6Al-4V
39. Build-up strategies for additive manufacturing of three dimensional Ti-6Al-4V parts produced by laser metal deposition10.2351/1.4997852 ↗
40. Fatigue behavior and modeling of additively manufactured Ti-6Al-4V including interlayer time interval effects10.1007/s11837-017-2625-y ↗
41. Laser cladding as repair technology for Ti–6Al–4V alloy: Influence of building strategy on microstructure and hardness10.1016/j.matdes.2015.07.035 ↗
42. Experimental investigation and 3D finite element prediction of the heat affected zone during laser assisted machining of Ti6Al4V alloy10.1016/j.jmatprotec.2010.08.007 ↗
43. ASTM. Standard Test Method for Microindentation Hardness of Materials. ASTM International; 2017.
44. A comparative study of additive manufacturing techniques: Residual stress and microstructural analysis of CLAD and WAAM printed Ti–6Al–4V components10.1016/j.matdes.2015.09.115 ↗
45. Residual stresses in LENS® components using neutron diffraction and contour method10.1016/j.msea.2005.02.019 ↗
46. The contour method
47. Olson · 2018
48. ASTM. Standard Test Methods for Tension Testing of Metallic Materials. ASTM International; 2016.
49. ASTM. Standard Practice for Conducting Force Controlled Constant Amplitude Axial Fatigue Tests of Metallic Materials. United States: ASTM International; 2002.
50. SAE. Titanium Alloy Laser Deposited Products 6Al-4V Annealed. SAE International; 2002.
51. The laser additive manufacture of Ti-6Al-4V10.1007/s11837-001-0068-x ↗
52. Influence of processing on microstructure and mechanical properties of (α+β) titanium alloys10.1016/S0921-5093(97)00778-8 ↗
53. Pederson · 2002
54. Microstructure and mechanical properties of high strength two-phase titanium alloys
55. Material properties of Ti6Al4V parts produced by laser metal deposition10.1016/j.phpro.2012.10.056 ↗
56. Additive manufacturing of strong and ductile Ti–6Al–4V by selective laser melting via in situ martensite decomposition10.1016/j.actamat.2014.11.028 ↗
57. Texture and crystal orientation in Ti6Al4V builds fabricated by shaped metal deposition10.1007/s11661-010-0255-x ↗
58. Improvement of fatigue resistance and ductility of TiAl6V4 processed by selective laser melting10.1016/j.jmatprotec.2015.01.025 ↗
59. Review of mechanical properties of Ti-6Al-4V made by laser-based additive manufacturing using powder feedstock10.1007/s11837-015-1759-z ↗
60. A fractographic study exploring the relationship between the low cycle fatigue and metallurgical properties of laser metal wire deposited Ti–6Al–4V10.1016/j.ijfatigue.2016.02.011 ↗
61. Challenges in additive manufacturing of space parts: powder feedstock cross-contamination and its impact on end products10.3390/ma10050522 ↗
62. Oxidation behavior and microstructural decomposition of Ti-6Al-4V and Ti-6Al-4V-1B sheet10.1016/j.corsci.2016.07.032 ↗
63. Typical fatigue-initiating discontinuities in metallic aircraft structures10.1016/j.ijfatigue.2011.10.017 ↗