Effect of stress ratio on VHCF behavior for a compressor blade titanium alloy
Source abstract
Abstract
Abstract Effect of stress ratio on fatigue properties of a titanium alloy (TC-17) in the high cycle fatigue (HCF) and very high cycle fatigue (VHCF) were investigated by electromagnetic and ultrasonic fatigue testing. The S – N curves at R = −1, 0.1, 0.5 and 0.7 at 110 Hz and 20 kHz were obtained and discussed. The effects of frequency on fatigue strength was also investigated. It was concluded that the fatigue strength with 50% fatigue failure probability at R = 0.1, 0.5 and 0.7 is lower to the Goodman line and shows a bilinear decreasing trend. Cleavage fracture of primary grains in the surface and interior initiation zone were observed. The formation of the facets induced by the basal or prismatic slips of the H.C.P grains decreased the fatigue strength with variation in mean stress.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Fatigue and fracture mechanics · Hydrogen embrittlement and corrosion behaviors in metals · High Temperature Alloys and Creep
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (30)
Show source-provided references
1. Fatigue limit – material property as an opened or closed system? Practical view on the aircraft components failures in GCF area10.1016/j.ijfatigue.2005.12.008 ↗
2. Critical issues in high cycle fatigue10.1016/S0142-1123(99)00074-2 ↗
3. Bathias · 2005
4. Piezoelectric fatigue testing machines and devices10.1016/j.ijfatigue.2005.09.020 ↗
5. Ultrasonic fatigue tests on bearing steel AISI-SAE 52100 at frequency of 20 and 30kHz10.1016/S0142-1123(03)00161-0 ↗
6. New experimental method for measuring life time and crack growth of materials under multi-stage and random loadings10.1016/0041-624X(81)90017-2 ↗
7. Development of a new device to perform torsional ultrasonic fatigue testing10.1016/j.ijfatigue.2007.03.016 ↗
8. Ultrasonic torsion and tension–compression fatigue testing: measuring principles and investigations on 2024-T351 aluminium alloy10.1016/j.ijfatigue.2005.05.020 ↗
9. Development of a three-point bending fatigue testing methodology at 20kHz frequency10.1016/j.ijfatigue.2007.03.018 ↗
10. Inducing very high cycle fretting-fatigue in the ultrasonic regime10.1016/j.triboint.2013.10.023 ↗
11. On the effects of particle strengthening and temperature on the VHCF behavior at high frequency10.1016/j.ijfatigue.2010.05.007 ↗
12. Very high cycle fatigue of a high strength steel under sea water corrosion: a strong corrosion and mechanical damage coupling10.1016/j.ijfatigue.2015.01.004 ↗
13. Effect of precipitation condition, prestrain and temperature on the fatigue behaviour of wrought nickel-based superalloys in the VHCF range10.1016/j.actamat.2011.05.005 ↗
14. Influence of mean stresses on fatigue life and damage of a turbine blade steel in the VHCF-regime10.1016/j.ijfatigue.2012.12.012 ↗
15. Mechanical properties of alloys consisting of two ductile phases10.1016/j.pmatsci.2005.10.003 ↗
16. Study of thermal effects associated with crack propagation during very high cycle fatigue tests10.1016/j.actamat.2008.04.023 ↗
17. Characteristic SN properties of high-carbon–chromium-bearing steel under axial loading in long-life fatigue10.1046/j.1460-2695.2002.00574.x ↗
18. Effects of stress ratio on high-cycle and very-high-cycle fatigue behavior of a Ti–6Al–4V alloy10.1016/j.msea.2014.09.115 ↗
19. Effects of strength level and loading frequency on very-high-cycle fatigue behavior for a bearing steel10.1016/j.ijfatigue.2011.11.014 ↗
20. Mughrabi · Int J Fract · 1981 · 17 · 19310.1007/BF00053520 ↗
21. Influence of loading frequency on high cycle fatigue properties of b.c.c. and h.c.p. metals10.1016/S0921-5093(00)01978-X ↗
22. Life time and cyclic slip of copper in the VHCF regime10.1016/j.ijfatigue.2007.03.010 ↗
23. Deformation heterogeneities and their role in life-limiting fatigue failures in a two-phase titanium alloy10.1016/j.actamat.2014.08.034 ↗
24. Slip and fatigue crack formation processes in an α/β titanium alloy in relation to crystallographic texture on different scales10.1016/j.actamat.2008.04.036 ↗
25. TEM observations of fatigue damage accumulation at the surface of the near-α titanium alloy IMI 83410.1016/1359-6454(96)00024-9 ↗
26. Microstructural influences on very-high-cycle fatigue-crack initiation in Ti-624610.1007/s11661-008-9633-z ↗
27. Phenomenological and microstructural analysis of room temperature creep in titanium alloys10.1016/S1359-6454(99)00426-7 ↗
28. Statistical duplex S–N characteristics of high carbon chromium bearing steel in rotating bending in very high cycle regime10.1016/j.ijfatigue.2009.08.001 ↗
29. Effect of stress ratio on long life fatigue behavior of high carbon chromium bearing steel under axial loading10.1016/j.ijfatigue.2005.04.018 ↗
30. Gigacycle fatigue properties of Ti–6Al–4V alloy under tensile, mean stress10.1016/j.msea.2014.01.019 ↗