Very high cycle fatigue measuring techniques
Source abstract
Abstract
Abstract Ever since high-strength steels were found to fail below the traditional fatigue limit when loaded with more than 108 cycles, the investigation of metals’ and alloys’ very high cycle fatigue properties has received increased attention. A lot of research was invested in developing methods and machinery to reduce testing times. This overview outlines the principles and testing procedures of very high cycle fatigue tests and reports findings in the areas of crack formation, non-propagating small cracks, long crack propagation and thresholds. Furthermore, superimposed and variable amplitude loading as well as frequency effects are reported.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Fatigue and fracture mechanics · Structural Health Monitoring Techniques · Ultrasonics and Acoustic Wave Propagation
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (83)
Show source-provided references
1. A 1 kHz servohydraulic fatigue testing system
2. Experimentelle Herausforderungen bei der Versuchsführung zur Charakterisierung des Ermüdungsverhaltens im Übergang von HCF zu VHCF
3. Development of a novel vibration-based fatigue testing technology10.1016/j.ijfatigue.2003.10.012 ↗
4. Klubberg F. Schwingfestigkeit der Hochleistungs-Aluminiumlegierung ALSI17Fe5Cu3,5Mg1,1ZR0,6T6X unter Wechselbelastung bei RT und 150 C, in: Rheinisch-Westfälische Technische Hochschule, editor Bericht Nr. 554, Aachen; 2003.
5. Step loading for very high cycle fatigue10.1046/j.1460-2695.2002.00555.x ↗
6. Morrissey R, Nicholas T. Staircase testing of a titanium alloy in the gigacycle regime, Int J Fatigue 2006;28:1577–1582, 11.10.1016/j.ijfatigue.2005.10.007 ↗
7. Schmidt M, Friedman A, Drögemüller T, Melz T. Hybride Prüftechnik zur dynamischen Charakterisierung von Elastomerbauteilen, In: Pohl M. editor, Tagung Werkstoffprüfung, Konstruktion, Werkstoffentwicklung und Schadensanalyse, Neu-Ulm; 2010. p. 161–6.
8. Piezoelectric driven testing facilities to research the very high cycle fatigue regime
9. Versuche über die Festigkeit der Eisenbahnwagenachsen, Zeitschrift für Bauwesen 10
10. Mechanism of fatigue failure in ultralong life regime10.1046/j.1460-2695.2002.00576.x ↗
11. Very high cycle fatigue behavior of shot-peened high carbon-chromium bearing steel10.1046/j.1460-2695.2002.00567.x ↗
12. Characteristic S–N properties of high-carbon-chromium-bearing steel under axial loading in long-life fatigue10.1046/j.1460-2695.2002.00574.x ↗
13. Fatigue crack propagation behaviour derived from S–N data in very high cycle regime10.1046/j.1460-2695.2002.00547.x ↗
14. Mitchell · 2007 · vol. 19
15. Schijve · 2001
16. Tschegg EK, Stanzl SE. Fatigue crack propagation under rotating bending. In: Kitagawa H, Tanaka T. editors. Proc Int Fatigue Series “Fatigue 90”, vol. 2; 1990. p. 1217–1222.
17. An efficient method to investigate short crack growth behaviour by reverse bending testing10.1016/j.ijfatigue.2006.04.005 ↗
18. Effect of frequency on giga-cycle fatigue properties for low-temperature-tempered SNCM439 steel10.1016/S1359-6462(01)01213-1 ↗
19. Stanzl-Tschegg S. Ultrasonic fatigue. In: Encyclopedia of materials: science and technology; 2001. p. 9444–50, ISBN: 0-08-0431526.10.1016/B0-08-043152-6/01707-1 ↗
20. VHCF-Prüftechnik
21. A new experimental method for measuring life time and crack growth of materials under multi-stage and random loadings10.1016/0041-624X(81)90017-2 ↗
22. Koster M, Wagner G, Walther F, Eifler D. New measuring methods for the fatigue assessment of metals in the very high cycle regime. In: Allison JE, Jones W, Larsen JM, Ritchie RO. editors. Fourth Int Conf on Very High Cycle Fatigue, TMS, (VHCF-4); 2007. p. 347–52.
23. Bathias C. Piezo-electric fatigue testing machines and devices. In: Sakai T, Ochi Y. editors. VHCF-3, Proc of the Third Intern Conf on Very High Cycle Fatigue; 2004. p. 472–83.
24. Mechanism of strain localisation, crack initiation and fracture of polycrystalline copper in the VHCF regime10.1016/j.ijfatigue.2009.03.016 ↗
25. Crack initiation and endurance limit of a hard steel under multiaxial cyclic loads10.1111/j.1460-2695.2009.01423.x ↗
26. Shear mode threshold for a small fatigue crack in a bearing steel10.1111/j.1460-2695.2010.01495.x ↗
27. High frequency method for torsion fatigue loading10.1016/0041-624X(93)90021-Q ↗
28. Fatigue strength of spring steel under axial and torsional loading in the very high cycle regime10.1016/j.ijfatigue.2008.07.004 ↗
29. Stanzl SE, Czegley M, Mayer HR, Tschegg EK. Fatigue crack growth under combined mode I and mode II loading. In: Wei RP, Gangloff RP. editors. Fracture mechanics, perspectives and directions, Amercian Society for Testing and Materials, ASTM STP 1020; 1989. p 479–96.10.1520/STP18839S ↗
30. Tschegg EK, Mayer HR, Czegley M, Stanzl SE. Influence of a constant mode III load on mode I fatigue crack growth thresholds. In: Kussmaul K, McDiarmid D, Socie D. editors, Fatigue under Biaxial/Multiaxial Loading, ESIS 10, Mech. Eng. Publ. London, 1991. pp. 213–222.
31. ASTM E 647–99: Standard test method for measurement of fatigue crack growth rates. In: Annual Book of ASTM Standards, Sect. 3, Vol. 03.01, USA; 2001.
32. Krupp · 2007
33. Life time and cyclic slip of copper in the VHCF regime
34. Roth I, Krupp H, Christ HJ, Kübbeler M, Fritzen C-P. Deformation induced martensite formation in metastable austenitic steel during in situ fatigue loading in a scanning electron microscope. In: 8th European symposium on martensitic transformation ESOMAT, Prag, September 7–11, 2009.10.1051/esomat/200906030 ↗
35. Stanzl-Tschegg SE, Schönbauer B. PSB threshold and fatigue limit of polycrystalline copper in the VHCF-Regime. In: Allison JE. editor. Proc VHCF-4, Fourth Int Conf on Very High Cycle Fatigue, August 19–22; 2007. p. 15–22.
36. AFM evidence of surface relief formation and models of fatigue crack nucleation10.1016/S0142-1123(03)00114-2 ↗
37. ASTM E 647-81: Standard test method for constant-load-amplitude fatigue crack growth rates above 10–8m/cycle, in: Annual Book of ASTM Standards, part 10, USA; 1981.
38. Sharpe Jr. WN. A 20kilohertz optical strain gage. In: Allison JE, Jones W, Larsen JM, Ritchie RO. editors, Fourth Int Conf on Very High Cycle Fatigue (VHCF-4), TMS; 2007. p. 341–6.
39. H.-J. Christ, P. Köster, H. Knobbe, C.-P. Fritzen, U. Krupp, M. Riedler, Bedeutung, experimentelle Charakterisierung und Simulation des Ausbreitungsverhaltens kurzer Risse in metallischen Konstruktionswerkstoffen, in: Pohl M. editor. Tagung Werkstoffprüfung, Konstruktion, Werkstoffentwicklung und Schadensanalyse, Neu-Ulm; 2010. p. 1-10.
40. Very high cycle fatigue behaviour of austenitic stainless steel and the effect of strain-induced martensite10.1016/j.ijfatigue.2009.05.007 ↗
41. Fatigue life calculation of SAE 1050 and SAE 1065 steel under random loading10.1016/j.ijfatigue.2007.01.005 ↗
42. Thermographic analysis in ultrasonic fatigue tests10.1111/j.1460-2695.2006.01024.x ↗
43. Mechanisms of strain localization, crack initiation and fracture of polycrystalline copper in the VHCF-Regime10.1016/j.ijfatigue.2009.03.016 ↗
44. High cycle fatigue of metals10.1016/0025-5416(74)90057-3 ↗
45. Stanzl SE, Tschegg EK. Fatigue crack growth and threshold behavior at ultrasonic frequencies. In: Lewis JC, Sines G. editors. Fracture mechanics: fourteenth symposium-vol. 2: testing and applications, ASTM STP 791, ASTM; 1983. p. 3–18.10.1520/STP791B1983001 ↗
46. Overstraining effects on the crack opening displacement of microstructurally short cracks10.1016/j.msea.2004.08.013 ↗
47. Fatigue damage in copper polycrystals subjected to ultrahigh-cycle fatigue below the PSB threshold10.1016/j.ijfatigue.2009.04.004 ↗
48. Very high cycle fatigue – is there a fatigue limit10.1016/j.ijfatigue.2010.05.009 ↗
49. On ‘multi-stage’ fatigue life diagrams and the relevant life-controlling mechanisms in ultrahigh–cycle Fatigue10.1046/j.1460-2695.2002.00550.x ↗
50. Role of impurities and PSBs on microcracking of polycrystalline copper at very high numbers of cycles10.4028/www.scientific.net/KEM.465.29 ↗
51. A theory of fatigue crack initiation at inclusions10.1007/BF02642422 ↗
52. Fatigue of structures and materials in the 20th century and the state of the art10.1016/S0142-1123(03)00051-3 ↗
53. Demonstration of a fatigue limit in cast 319 aluminium
54. Fatigue properties of spray formed hypereutectic aluminium silicon alloy DISPAL©S232 at high and very high numbers of cycles10.1016/j.msea.2012.01.052 ↗
55. Murakami · 2002
56. Statistical characteristics of propagation of small fatigue cracks in smooth specimens of aluminium alloy 2024–T310.1016/0025-5416(88)90411-9 ↗
57. Crack initiation and propagation in 12% steam turbine steel
58. S.E. Stanzl-Tschegg, Ultraschall-Ermüdung und Bruchmechanik, in: DGM (Ed.), Hauptversammlung, Berlin, June 8, 2006.
59. Lu, Subsurface crack initiation and propagation mechanism in high-strength steel in a very high cycle fatigue regime10.1016/j.ijfatigue.2005.08.015 ↗
60. Near-threshold crack propagation and internal cracks in steel10.1016/j.proeng.2010.03.167 ↗
61. Nakajima · Int J Fatigue · 2006 · 28 · 154010.1016/j.ijfatigue.2005.05.017 ↗
62. Ishida W, Yamamoto T, Kaneda S, Ogawa T. Fatigue strength and internal crack growth behavior of high strength steel under variable amplitude stressing in very high cycle regime, Transaction of Japan Society of Mechanical Engineers A, Vol. 78(785); 2012-1. p. 23–33 [in Japanese].10.1299/kikaia.78.23 ↗
63. Internal fatigue cracks are growing in vacuum10.1016/0013-7944(76)90031-X ↗
64. In situ characterization of fatigue damage in a cast Al alloy via nonlinear ultrasonic measurements10.1016/j.actamat.2009.11.055 ↗
65. Course of S-N curves especially in the high-cycle fatigue regime with regard to component design and safety10.1016/j.ijfatigue.2006.11.015 ↗
66. Schijve J. Fatigue crack growth under variable-amplitude loading. In: ASM Handbook, Fatigue and Fracture, vol. 19. ASM, Ohio, USA; 2007. p. 110–33.10.31399/asm.hb.v19.a0002356 ↗
67. The prediction of fatigue life in the crack initiation and propagation stages–a state of the art survey10.1016/0013-7944(79)90015-8 ↗
68. Dowling NE. Estimating fatigue life. In: ASM Handbook, vol. 19 Fatigue and Fracture, ASM, Ohio, USA; 2007. p. 251–62.
69. Zenner H, Pöting S. A method for lifetime calculation in the high cycle regime. In: Stanzl-Tschegg SE, Mayer H editors, Proc of the Intern Conference on Fatigue in the very high cycle regime (later named VHCF-2), July 2–4; 2001. p. 353–61.
70. 2. Sitzung des Arbeitskreises Betriebsfestigkeit DVM, Häufigkeitsverteilung zur Beurteilung der Betriebsfestigkeit von Werkstoffen und Bauteilen, DVM, Darmstadt, 23./24.2; 1977.
71. 3. Sitzung des Arbeitskreises Betriebsfestigkeit DVM: Anwendung bruchmechanischer Verfahren auf Fragen der Betriebsfestigkeit, DVM, Berlin, 14. 10; 1977.
72. Lifetime measurements for random loading in the very high cycle fatigue range10.1016/0142-1123(86)90021-6 ↗
73. Haibach E. Modifizierte lineare Schadensakkumulationshypothese zur Berücksichtigung des Dauerfestigkeitsabfalls mit fortschreitender Schädigung, LBF TM No. 50/70, Darmstadt; 1970.
74. Fatigue crack growth of Al 2024-T3 under low amplitude two-step loading10.1111/j.1460-2695.1992.tb01269.x ↗
75. Very high cycle fatigue properties of bainitic high-carbon-chromium steel under variable amplitude conditions10.1016/j.ijfatigue.2009.02.038 ↗
76. Ultrasonic fatigue testing of 2024-T351 aluminium alloy at different load ratios under constant and variable amplitude
77. Führing H, Seeger T. Structural memory of cracked components under irregular loading. In: Smith CW. editor, Fracture mechanics ASTM STP 677 1979. p. 1144–67.10.1520/STP34911S ↗
78. Critical parameters for fatigue damage10.1016/S0142-1123(01)00171-2 ↗
79. Fatigue life scatter in 7xxx Series aluminum alloys10.1016/j.ijfatigue.2009.07.016 ↗
80. Near threshold fatigue crack growth in aluminium alloys at low and ultrasonic frequency: influences of specimen thickness, strain Rate, slip behaviour and air humidity10.1016/S0142-1123(02)00163-9 ↗
81. Ultra slow fatigue crack propagation in TA6V titanium alloy
82. Cyclic plastic deformation of tantalum and niobium at very high number of cycles10.1016/S0921-5093(01)01446-0 ↗
83. Influence of loading frequency on high cycle fatigue properties of b.c.c. and h.c.p. metals