Strain energy density to assess mode II fracture in U-notched disk-type graphite plates
Source abstract
Abstract
The brittle fracture criterion, namely the strain energy density (SED) over a control volume, which embraces the notch edge, is utilized in the present research to assess the experimentally obtained fracture loads of several U-notched Brazilian disk (UNBD) specimens made of a type of commercial graphite under pure mode II loading. The results show that the SED criterion could successfully predict the fracture loads of graphite specimens for different notch tip radii with an average discrepancy of about ±10%. It is proved in this investigation that not only the SED criterion works well on brittle fracture of notched graphite components under pure mode I, mixed mode I/II and pure mode III loading conditions, but also under pure mode II loading.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Fatigue and fracture mechanics · Graphite, nuclear technology, radiation studies · Nuclear and radioactivity studies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Fracture Research Laboratory, Faculty of New Science and Technologies, University of Tehran, Tehran, Iran
Department of Management and Engineering, University of Padova, Stradella, Vicenza, Italy
References (47)
Show source-provided references
1. 10.1016/j.engfracmech.2004.05.00210.1016/j.engfracmech.2004.05.002 ↗
2. 10.1016/j.ijsolstr.2005.07.04910.1016/j.ijsolstr.2005.07.049 ↗
3. 10.1016/j.carbon.2008.05.00810.1016/j.carbon.2008.05.008 ↗
4. 10.1111/j.1460-2695.2011.01583.x10.1111/j.1460-2695.2011.01583.x ↗
5. 10.1016/j.engfracmech.2010.10.00110.1016/j.engfracmech.2010.10.001 ↗
6. 10.1016/j.carbon.2011.02.01510.1016/j.carbon.2011.02.015 ↗
7. 10.1016/j.ijrmms.2011.04.01710.1016/j.ijrmms.2011.04.017 ↗
8. 10.1016/j.carbon.2010.02.04110.1016/j.carbon.2010.02.041 ↗
9. 10.1016/j.ijsolstr.2009.10.01210.1016/j.ijsolstr.2009.10.012 ↗
10. 10.1016/j.msea.2011.04.06610.1016/j.msea.2011.04.066 ↗
11. 10.1016/0008-6223(69)90524-710.1016/0008-6223(69)90524-7 ↗
12. 10.1016/j.tafmec.2009.10.00110.1016/j.tafmec.2009.10.001 ↗
13. 10.1016/j.carbon.2011.12.04510.1016/j.carbon.2011.12.045 ↗
14. 10.1016/j.mser.2013.11.00110.1016/j.mser.2013.11.001 ↗
15. 10.1016/j.carbon.2013.06.04510.1016/j.carbon.2013.06.045 ↗
16. Berto F, Lazzarin P and Gallo P (2014) High-temperature fatigue strength of a copper cobalt-beryllium alloy. The Journal of Strain Analysis for Engineering Design 49: 244-256.10.1177/0309324713511804 ↗
17. 10.1111/j.1460-2695.2010.01518.x10.1111/j.1460-2695.2010.01518.x ↗
18. 10.1111/j.1460-2695.2011.01647.x10.1111/j.1460-2695.2011.01647.x ↗
19. 10.1016/j.matdes.2012.05.02210.1016/j.matdes.2012.05.022 ↗
20. 10.1016/j.carbon.2006.05.01110.1016/j.carbon.2006.05.011 ↗
21. 10.1016/S0921-5093(04)00915-310.1016/S0921-5093(04)00915-3 ↗
22. 10.1007/s10704-010-9449-x10.1007/s10704-010-9449-x ↗
23. Jae HK, Young SL, Duck HK, et al. (2004) Evaluation of thermal shock strengths for graphite materials using a laser irradiation method. Material Science and Engineering Part A 387–389: 385–389.10.1016/j.msea.2004.01.136 ↗
24. 10.3327/jaesj.27.35710.3327/jaesj.27.357 ↗
25. 10.1016/j.engfracmech.2010.04.00810.1016/j.engfracmech.2010.04.008 ↗
26. 10.1007/s10704-005-3943-610.1007/s10704-005-3943-6 ↗
27. 10.1111/ffe.1205710.1111/ffe.12057 ↗
28. 10.1111/j.1460-2695.2009.01373.x10.1111/j.1460-2695.2009.01373.x ↗
29. 10.1016/j.ijfatigue.2007.10.01210.1016/j.ijfatigue.2007.10.012 ↗
30. 10.1016/j.ijfatigue.2010.02.01710.1016/j.ijfatigue.2010.02.017 ↗
31. 10.1023/A:101359593061710.1023/A:1013595930617 ↗
32. 10.1007/s10704-011-9613-y10.1007/s10704-011-9613-y ↗
33. 10.1007/BF0152287010.1007/BF01522870 ↗
34. 10.1111/j.1460-2695.2012.01648.x10.1111/j.1460-2695.2012.01648.x ↗
35. 10.1016/j.carbon.2013.03.02510.1016/j.carbon.2013.03.025 ↗
36. 10.1007/s10853-012-6785-410.1007/s10853-012-6785-4 ↗
37. Neuber H · 1958
38. 10.1016/0008-6223(81)90116-010.1016/0008-6223(81)90116-0 ↗
39. 10.1016/j.jnucmat.2007.02.01210.1016/j.jnucmat.2007.02.012 ↗
40. 10.1007/BF0003549310.1007/BF00035493 ↗
41. 10.1046/j.1460-2695.2001.00377.x10.1046/j.1460-2695.2001.00377.x ↗
42. 10.1007/s10704-012-9799-710.1007/s10704-012-9799-7 ↗
43. 10.1007/s10704-013-9832-510.1007/s10704-013-9832-5 ↗
44. 10.1016/j.engfracmech.2013.08.01510.1016/j.engfracmech.2013.08.015 ↗
45. Torabi AR · International Journal of Damage Mechanics · 2013
46. 10.1023/B:FRAC.0000022244.31825.3b10.1023/B:FRAC.0000022244.31825.3b ↗
47. Yamauchi Y · Zairyo/Journal of the Society of Materials Science · 2001 · 50 · 224