Structural Performances of Reinforced Alkali-Activated Slag Fiber Composite Walls
Source abstract
Abstract
Abstract To reduce carbon emissions in the construction industry, this study attempted to manufacture alkali-activated slag fiber composites (ASFC) without using cement. Synthetic fibers were incorporated into the alkali-activated slag (AAS) binder, and the mechanical properties of ASFC were evaluated through tests on fresh mixture, compressive strength, and direct tensile behavior. The fresh ASFC showed excellent workability with sufficient slump flow, and its 28-day compressive strength averaged 33.7 MPa. In tensile behavior, ASFC exhibited a strain-hardening response with multiple microcracks, similar to cement-based SHCC, with an ultimate tensile strain of approximately 3–5%. Compared with SHCC, ASFC showed slightly lower first cracking stress and tensile strength, but higher ductility. To assess structural performance, reinforced ASFC wall specimens were tested under in-plane lateral loads and compared with conventional RC and SHCC walls. Reinforcing bars were arranged according to both standard design and minimum reinforcement ratios. ASFC walls showed up to 81.9% and 80.6% higher load capacities than RC walls under standard and minimum reinforcement, respectively. Although RC walls failed due to localized cracks, ASFC walls formed widely distributed microcracks controlled by fiber bridging, improving ductility and delaying failure. These results demonstrate that ASFC, without cement, exhibits compressive strength comparable to concrete and superior tensile ductility. Its application in structural walls can enhance resistance to bending and shear cracks while improving overall load-bearing capacity, making it a promising sustainable material.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Innovative concrete reinforcement materials · Concrete and Cement Materials Research · Structural Behavior of Reinforced Concrete
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (35)
Show source-provided references
1. ASTM. (2007). Standard test method for compressive strength of hydraulic cement mortars (using 50 mm [2 in.] cube specimens) ASTM C109/C109M-07
2. Bergmann, R. (1988). A finite element for R/C shear walls under cyclic loads. Structural engineering mechanics and materials, Department of Civil Engineering, University of California
3. Cho, C. G., et al. (2012). Cyclic responses of reinforced concrete composite columns strengthened in the plastic hinge region by HPFRC mortar. Composite Structures, 94, 2246–2253. https://doi.org/10.1016/j.compstruct.2012.01.02510.1016/j.compstruct.2012.01.025 ↗
4. Cho, C. G., et al. (2015). Experiments and failure analysis of SHCC and reinforced concrete composite slabs. Engineering Failure Analysis, 56, 320–331. https://doi.org/10.1016/j.engfailanal.2015.01.00910.1016/j.engfailanal.2015.01.009 ↗
5. Cho, C. G., et al. (2019). Experimental study on seismic capacity of reinforced concrete composite columns based on a high-ductile fiber cementitious composite. International Journal of Concrete Structures and Materials, 13, 16. https://doi.org/10.1186/s40069-018-0324-x10.1186/s40069-018-0324-x ↗
6. Cho, C. G., Kim, Y. Y., & Ha, G. J. (2018). Nonlinear model of reinforced concrete frames retrofitted by in-filled HPFRCC walls. Structural Engineering and Mechanics, 30, 211–223. https://doi.org/10.12989/sem.2008.30.2.21110.12989/sem.2008.30.2.211 ↗
7. Choi, J.I. (2019). Mechanical properties of fiber-reinforced alkali-activated slag composite based on micromechanics. PhD Thesis, Chonnam National University, Gwangju, Korea.
8. Choi, J. I., et al. (2016). Composite properties of high-strength polyethylene fiber-reinforced cement and cementless composites. Composite Structures, 138, 116–121. https://doi.org/10.1016/j.compstruct.2015.11.04610.1016/j.compstruct.2015.11.046 ↗
9. Choi, J. I., Kim, H. K., & Lee, B. Y. (2020). Mechanical and fiber-bridging behavior of slag-based composite with high tensile ductility. Applied Sciences. https://doi.org/10.3390/app1012430010.3390/app10124300 ↗
10. Fischer, G., & Li, V. C. (2003). Design of engineered cementitious composites (ECC) for processing and workability requirement. Brittle Matrix Composites, 7, 29–36. https://doi.org/10.1533/9780857093103.2910.1533/9780857093103.29 ↗
11. Gupta, R. K., et al. (2017). Carbon sequestration potential through agroforestry: A review. International Journal of Current Microbiology and Applied Science, 6(8), 211–220. https://doi.org/10.0546/ijcmas.2017.608.02910.0546/ijcmas.2017.608.029 ↗
12. Huang, B. T., et al. (2022). Ultra-high-strength engineered/strain-hardening cementitious composites (ECC/SHCC): Material design and effect of fiber hybridization. Cement and Concrete Composites. https://doi.org/10.1016/j.cemconcomp.2022.10446410.1016/j.cemconcomp.2022.104464 ↗
13. Ji, J., et al. (2023). Structural application of engineered cementitious composites (ECC): A state-of-the-art review. Construction and Building Materials. https://doi.org/10.1016/j.conbuildmat.2023.13328910.1016/j.conbuildmat.2023.133289 ↗
14. Kanda, T., & Li, V. C. (2006). Practical design criteria for saturated pseudo strain hardening behavior in ECC. Journal of Advanced Concrete Technology., 4, 59–72. https://doi.org/10.3151/jact.4.5910.3151/jact.4.59 ↗
15. Kim, H. G., et al. (2021). Structural performance and reinforcement improvement of structural walls using strain-hardening cementitious composites. Sustainability. https://doi.org/10.3390/su1307360710.3390/su13073607 ↗
16. Kim, J. K., et al. (2007). Tensile and fiber dispersion performance of ECC (engineered cementitious composites) produced with ground granulated blast furnace slag. Cement and Concrete Research, 37(7), 1096–1105.10.1016/j.cemconres.2007.04.006 ↗
17. Kim, J. S., et al. (2017). Experiments on tensile and shear characteristics of amorphous micro steel (AMS) fibre-reinforced cementitious composites. International Journal of Concrete Structures and Materials, 11, 647–655. https://doi.org/10.1007/s40069-017-0214-710.1007/s40069-017-0214-7 ↗
18. Kim, T., & Kang, C. (2020). The mechanical properties of alkali-activated slag-silica fume cement pastes by mixing method. International Journal of Concrete Structures and Materials, 14, 41. https://doi.org/10.1186/s40069-020-00416-x10.1186/s40069-020-00416-x ↗
19. Kumar, N., et al. (2024). Carbon capture and sequestration technology for environmental remediation: A CO2 utilization approach through EOR. Geoenergy Science and Engineering, 234, Article 212619. https://doi.org/10.1016/j.geoen.2023.21261910.1016/j.geoen.2023.212619 ↗
20. Lee, Y., et al. (2017). Effects of a defoamer on the compressive strength and tensile behavior of alkali-activated slag-based cementless composite reinforced by polyethylene fiber. Composite Structures, 172, 166–172. https://doi.org/10.1016/j.compstruct.2017.03.09510.1016/j.compstruct.2017.03.095 ↗
21. Li, V. C., et al. (2002). Interface tailoring for strain-hardening polyvinyl alcohol-engineered cementitious composite (PVA-ECC). ACI Material Journal, 99(5), 463–472. https://doi.org/10.14359/1232510.14359/12325 ↗
22. Li, V. C. (2012). Tailoring ECC for special attributes: A review. International Journal of Concrete Structures and Materials, 6, 135–144. https://doi.org/10.1007/s40069-012-0018-810.1007/s40069-012-0018-8 ↗
23. Li, V. C., Mishra, D. K., & Wu, C. (1995). Matrix design for pseudo strain-hardening fiber reinforced cementitious composites. Materials and Structures, 28, 586–595. https://doi.org/10.1007/BF0247319110.1007/BF02473191 ↗
24. Li, V. C., Wang, S., & Wu, C. (2001). Tensile strain-hardening behavior of PVA-ECC. ACI Materials Journal, 98, 483–492. https://doi.org/10.14359/1085110.14359/10851 ↗
25. Li, V. C., Wang, Y., & Backer, S. (1991). A micromechanical model of tension-softening and bridging toughening of short random fiber reinforced brittle matrix composites. Journal of the Mechanics and Physics of Solids, 39(5), 607–625. https://doi.org/10.1016/0022-5096(91)90043-N10.1016/0022-5096(91)90043-N ↗
26. Lim, H. J., et al. (2022). Mechanical properties of alkali-activated slag fiber composites varying with fiber volume fractions. Materials. https://doi.org/10.3390/ma1518644410.3390/ma15186444 ↗
27. Lương, Q. H., et al. (2023). Extremely-ductile alkali-activated slag-based composite with a tensile strain capacity up to 22%. Ceramics International, 49(8), 12069–12078. https://doi.org/10.1016/j.ceramint.2022.12.05710.1016/j.ceramint.2022.12.057 ↗
28. Lương, Q. H., et al. (2025). Achieving ultra-ductility exceeding 13 % and cost efficiency with rubberized alkali-activated slag-based cement-free composites. Developments in the Built Environment, 22, Article 100677. https://doi.org/10.1016/j.dibe.2025.10067710.1016/j.dibe.2025.100677 ↗
29. Marshall, D. B., & Cox, B. N. (1988). A J-integral method for calculating steady-state matrix cracking stresses in composites. Mechanics of Materials, 8, 127–133. https://doi.org/10.1016/0167-6636(88)90011-710.1016/0167-6636(88)90011-7 ↗
30. Naaman, A. E., El-Tawil, S., & Wille, K. (2014). Properties of strain hardening ultra high performance fiber reinforced concrete (UHP-FRC) under direct tensile loading. Cement and Concrete Composites, 48, 53–66. https://doi.org/10.1016/j.cemconcomp.2013.12.01510.1016/j.cemconcomp.2013.12.015 ↗
31. Nguyễn, H. H., et al. (2023). Mechanical and autogenous healing properties of high-strength and ultra-ductility engineered geopolymer composites reinforced by PE-PVA hybrid fibers. Cement and Concrete Composites, 142, Article 105155. https://doi.org/10.1016/j.cemconcomp.2023.10515510.1016/j.cemconcomp.2023.105155 ↗
32. Pacheco-Torgal, F., Castro-Gomes, J., & Jalali, S. (2008). Alkali-activated binders: A review: Part 1. Historical Background, Terminology, Reaction Mechanisms and Hydration Products, Construction and Building Materials., 22, 1305–1314. https://doi.org/10.1016/j.conbuildmat.2007.10.01510.1016/j.conbuildmat.2007.10.015 ↗
33. Shaw, R., & Mukherjee, S. (2022). The development of carbon capture and storage (CCS) in India: A critical review. Carbon Capture Science & Technology. https://doi.org/10.1016/j.ccst.2022.10003610.1016/j.ccst.2022.100036 ↗
34. Solomon, S., et al. (2009). Irreversible climate change due to carbon dioxide emissions. The Proceedings of the National Academy of Sciences, 106, 1704–1709. https://doi.org/10.1073/pnas.081272110610.1073/pnas.0812721106 ↗
35. Vance, K., et al. (2014). Microstructural, mechanical, and durability related similarities in concretes based on OPC and alkali-activated slag binders. International Journal of Concrete Structures and Materials, 8, 289–299. https://doi.org/10.1007/s40069-014-0082-310.1007/s40069-014-0082-3 ↗