Damage and Deterioration Mechanism of Coal Gangue Mixed Pumice Aggregate Concrete Under Freeze–Thaw Cycles
Source abstract
Abstract
Abstract The world is facing the problem of depletion of natural sand and gravel resources, and a large amount of coal gangue solid waste is produced in Inner Mongolia, China, which has low utilization rate and causes ecological pollution. In order to improve the gangue in the mining infrastructure construction of a wide range of application prospects, the use of coal gangue as the coarse aggregate of pumice concrete is of great significance. Inner Mongolia is a cold region, and gangue mixed aggregate concrete (MFC) will certainly face the damage caused by freeze–thaw cycles. Therefore, design gangue by different volume replacement rate (0%, 20%, 40%, 60%, 80%, 100%) to replace pumice coarse aggregate. The results show that with the increase of gangue substitution rate, the mass loss rate, relative dynamic elastic modulus, and peak stress of MFC decrease, but the trend of peak strain increases. It is mainly attributed to the less Al2O3 and SiO2 content of gangue, which makes the MFC hydration products decrease with the increase of substitution rate and more original microcracks and pores in the specimens. In addition, the damage model of MFC was established by using Weibull statistical distribution theory and the principle of LEMAITRE equivalent effect variation assumption, and the damage evolution characteristics were explored by combining the experimental results. It can provide the theoretical basis for the application of MFC in cold regions.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Rock Mechanics and Modeling · Innovations in Concrete and Construction Materials · Innovative concrete reinforcement materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (15)
Show source-provided references
1. Guo, K., Ma, H. H., Yang, F. S., & Zhao, T. Y. (2020). Micromechanical properties of the transition region of the GO-RC interface under the freeze–melting cycle. Journal of Building Materials, 23(1), 230–238. (in Chinese).
2. Lemaitre, J. (1984). How to use damage mechanics. Nuclear Engineering and Design, 80(2), 233–245.10.1016/0029-5493(84)90169-9 ↗
3. Liu H. F., Ma Y. C., Zhang R. Q., Shao W., & Ma J. R. (2021). Effect of desert sand on compression mechanical properties of concrete shaft in freeze–thaw environment. Journal of Harbin Institute of Technology, 53(3), 01–109 + 117. (in Chinese).
4. Long, G. C., Liu, H., Ma, K. L., & Xie, X. J. (2018). Constitutive model of concrete considering freeze and thaw. Journal of Central South University (Natural Science Edition), 49(8), 1884–1892. (in Chinese).
5. Ma K. L., Huang X. Y., Hu M. M., Peng L. M., & Zhang X. Q. (2021). Constitutive relationship of damaged coarse aggregate concrete. Journal of Building Materials, 25(2):1–15. (in Chinese).
6. Qin, Y. J., Zhang, L. L., Cui, Z., & Xing, G. H. (2021). Analysis of compression stress–strain curve of desert sand concrete axis. Science and Technology, and Engineering, 21(10), 4184–4190. (in Chinese).
7. Shang, X. Y., Zheng, S. S., Xu, Q., & Liu, C. C. (2015). Cognitive relationship model of axial compression brick masonry damage under freeze–thaw cycle. Journal of Building Materials, 94(6), 1045–1049 + 1054.
8. Sun, W., Zhang, Y. M., Yan, H. D., et al. (1999). Damage and damage resistance of high strength concrete under the action of load and freeze–thaw cycles. Cement and Concrete Research, 29(9), 1519–1523. (in Chinese).10.1016/S0008-8846(99)00097-6 ↗
9. Wang, B., Wang, F., & Wang, Q. (2018). Damage constitutive models of concrete under the coupling action of freeze–thaw cycles and load based on Lemaitre assumption. Construction & Building Materials, 173, 332–341.10.1016/j.conbuildmat.2018.04.054 ↗
10. Wang, X. X., Shen, X. D., Wang, H. L., Gao, C., Zhao, H. H., & Gao, M. L. (2014). Frozen resistance of natural pumice concrete under salt corrosion–freeze–thaw cycle. Journal of Portland, 308(11), 1414–1421. (in Chinese).
11. Wawrzeńczyk, J., & Molendowska, A. (2017). Evaluation of concrete resistance to freeze–thaw based on probabilistic analysis of damage. Procedia Engineering, 193, 35–41.10.1016/j.proeng.2017.06.183 ↗
12. Xie, R. F., Wu, Y. F., & Tang, B. X. (2021). Study on the extraction behavior of steel fibers in ultrahigh performance concrete after freeze–melting action. Journal of Materials Research, 35(6), 433–440. (in Chinese).
13. Yi, C., Ma, H. Q., Zhu, H. G., Dong, Z. C., Su, Z. J., Zhang, Y. T., & Chu, Z. (2017). Study on carbonization of coal gangue aggregate concrete. Journal of Building Materials, 105(5), 787–793. (in Chinese).
14. Zhang, T., Huang, W., & Rong, C. (2015). Study on the constitutive model of polypropylene fiber regeneration concrete damage. Material Guide, 29(22), 6. (in Chinese).
15. Zhu, Z., Zhang, C., & Meng, S. (2019). A statistical damage constitutive model based on the Weibull distribution for alkali-resistant glass fiber reinforced concrete. Materials, 12(12), 1908.10.3390/ma12121908 ↗