Characteristics of Sustainable Concrete with Partial Substitutions of Glass Waste as a Binder Material
Source abstract
Abstract
Abstract Manufacturing waste has been quickly increasing over time as a result of the fast-rising population as well as the consumption of foods that are thrown away dishonestly, resulting in environmental contamination. As a result, it has been suggested that industrial waste disposal may be considerably reduced if it could be integrated into cement concrete manufacturing. The aim of this study is to analyze the properties of concrete employing waste glass (WG) as a binding material in proportions of 5%, 10%, 15%, 20%, 25%, and 30% by weight of cement. The fresh property was assessed using a slump cone test, while mechanical performance was assessed using flexural, compressive, splitting tensile, and pull-out strength after 7, 28, and 56 days. Furthermore, microstructure analysis was studied by scan electronic microscopic (SEM), Fourier-transform infrared spectroscopy (FTIR) and thermo-gravimetric analysis (TGA) test. The results reveal that the addition of discarded glass reduces the workability of concrete. Furthermore, mechanical performance was increased up to a 20% substitution of waste glass and then gradually declined. Waste glass can be employed as a micro filler or pozzolanic material without affecting the mechanical performance of concrete, according to microstructure research.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Materials Engineering and Processing · Concrete and Cement Materials Research · Recycling and utilization of industrial and municipal waste in materials production
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (71)
Show source-provided references
1. Abdallah, S., & Fan, M. (2014). Characteristics of concrete with waste glass as fine aggregate replacement. International Journal of Engineering and Technical Research, 2, 11–17.
2. Agency IE, Agency IE (2007) Tracking industrial energy efficiency and CO2 emissions. OECD
3. Ahmad, J., Manan, A., Ali, A., et al. (2020). A study on mechanical and durability aspects of concrete modified with steel fibers (SFs). Civil Engineering and Architecture, 8, 814–823. https://doi.org/10.13189/cea.2020.08050810.13189/cea.2020.080508 ↗
4. Ahmad, J., Tufail, R. F., Aslam, F., et al. (2021). A Step towards sustainable self-compacting concrete by using partial substitution of wheat straw ash and bentonite clay instead of cement. Sustainability, 13, 824. https://doi.org/10.3390/su1302082410.3390/su13020824 ↗
5. Ahmad, J., Zaid, O., Shahzaib, M., et al. (2021). Mechanical properties of sustainable concrete modified by adding marble slurry as cement substitution. AIMS Mater Sci, 8, 343–358. https://doi.org/10.3934/matersci.202102210.3934/matersci.2021022 ↗
6. Alexander, K. M. (1960). Reactivity of ultrafine powders produced from siliceous rocks. ACI J Proc, 57, 557–570. https://doi.org/10.14359/803610.14359/8036 ↗
7. Aly, M., Hashmi, M. S. J., Olabi, A. G., et al. (2012). Effect of colloidal nano-silica on the mechanical and physical behaviour of waste-glass cement mortar. Materials and Design, 33, 127–135.10.1016/j.matdes.2011.07.008 ↗
8. Amin, S. K., Allam, M. E., Garas, G. L., & Ezz, H. (2020). A study of the chemical effect of marble and granite slurry on green mortar compressive strength. Bull Natl Res Cent, 44, 19. https://doi.org/10.1186/s42269-020-0274-810.1186/s42269-020-0274-8 ↗
9. Anwar, A. (2016). The influence of waste glass powder as a pozzolanic material in concrete. Int J Civ Eng Technol, 7, 131–148.
10. Armstrong, T., Bal, M., Bell, P., et al. (2013). The global cement report. International Cement Review 13:
11. Ashby, M. F. (2011). Materials selection in mechanical design. Elsevier.
12. Association WC Oyak Cement. https://www.worldcementassociation.org/about-cement.
13. ASTM C 33/C33M (2008). Stand Specif Concr aggregates Annu B ASTM Stand 4:498–505
14. Baboo, R., Khan, H. N., Kr, A., et al. (2011). Influence of Marble powder/granules in Concrete mix. International Journal of Civil and Structural Engineering, 1, 827–834.
15. Bakharev, T. (2006). Thermal behaviour of geopolymers prepared using class F fly ash and elevated temperature curing. Cement and Concrete Research, 36, 1134–1147. https://doi.org/10.1016/j.cemconres.2006.03.02210.1016/j.cemconres.2006.03.022 ↗
16. Benhelal, E., Zahedi, G., Shamsaei, E., & Bahadori, A. (2013). Global strategies and potentials to curb CO2 emissions in cement industry. Journal of Cleaner Production, 51, 142–161.10.1016/j.jclepro.2012.10.049 ↗
17. Berrocal, C. G., Lundgren, K., & Löfgren, I. (2016). Corrosion of steel bars embedded in fibre reinforced concrete under chloride attack: State of the art. Cement and Concrete Research, 80, 69–85. https://doi.org/10.1016/j.cemconres.2015.10.00610.1016/j.cemconres.2015.10.006 ↗
18. Binici, H., Aksogan, O., Cagatay, I. H., et al. (2007). The effect of particle size distribution on the properties of blended cements incorporating GGBFS and natural pozzolan (NP). Powder Technology, 177, 140–147. https://doi.org/10.1016/j.powtec.2007.03.03310.1016/j.powtec.2007.03.033 ↗
19. Byars, E.A., Zhu, H., Meyer, C. (2003). Use of waste glass for construction products: Legislative and technical issues. In: Recycling and reuse of waste materials, proceedings of the international symposium. Thomas Telford Publishing, pp 827–838
20. C39/C39M A (2003). Standard test method for compressive strength of cylindrical concrete specimens. Annu B ASTM Stand
21. Cement AP ASTM C150 of the following type: 1. Concr which will be contact with Sew Type II, Moderate Sulfate Resist 2:
22. Chikhalikar, S.M., Tande, S.N. (2012). An experimental investigation on characteristics properties of fibre reinforced concrete containing waste glass powder as pozzolona. In: 37th conference on our world in concrete and structures, Singapore, August
23. Deluce JR, Vecchio FJ (2013) Cracking behavior of steel fiber-reinforced concrete members containing conventional reinforcement. ACI Structural Journal 110:10.14359/51685605 ↗
24. Designation A (1976). C496‐71. Stand method test split tensile strength cylind concr specimens
25. Du Plessis, C. (2007). A strategic framework for sustainable construction in developing countries. Construction Management and Economics, 25, 67–76. https://doi.org/10.1080/0144619060060131310.1080/01446190600601313 ↗
26. Federico, L. M., & Chidiac, S. E. (2009). Waste glass as a supplementary cementitious material in concrete–critical review of treatment methods. Cement and Concrete Composites, 31, 606–610.10.1016/j.cemconcomp.2009.02.001 ↗
27. Felixkala, T., & Partheeban, P. (2010). Granite powder concrete. Indian Journal of Science and Technology, 3, 311–317. https://doi.org/10.17485/ijst/2010/v3i3/2970610.17485/ijst/2010/v3i3/29706 ↗
28. Garcia, L.E. (2005). Essential requirements for reinforced concrete buildings. STRUCTURE 43:
29. Grout F ASTM C 476, except with a maximum slump of 4 inches, as measured according to ASTM C 143. C 143M
30. Humphreys, D. (2013). Long-run availability of mineral commodities. Mineral Economics, 26, 1–11. https://doi.org/10.1007/s13563-013-0033-510.1007/s13563-013-0033-5 ↗
31. Imbabi, M. S., Carrigan, C., & McKenna, S. (2012). Trends and developments in green cement and concrete technology. International Journal of Sustainable Built Environment, 1, 194–216. https://doi.org/10.1016/j.ijsbe.2013.05.00110.1016/j.ijsbe.2013.05.001 ↗
32. Isler, J. W. (2012). Assessment of concrete masonry units containing aggregate replacements of waste glass and rubber tire particles. University of Colorado at Denver.
33. Jin, W., Meyer, C., & Baxter, S. (2000). “ Glascrete”-concrete with glass aggregate. ACI Materials Journal, 97, 208–213.
34. Khan, M. U., Ahmad, S., & Al-Gahtani, H. J. (2017). Chloride-induced corrosion of steel in concrete: an overview on chloride diffusion and prediction of corrosion initiation time. Int J Corros, 2017, 1–9. https://doi.org/10.1155/2017/581920210.1155/2017/5819202 ↗
35. Korjakins, A., Shakhmenko, G., & Bumanis, G. (2012). Utilisation of borosilicate glass waste as a micro-filler for concrete. Journal of Civil Engineering Architecture, 6, 876.
36. Kurad, R., Silvestre, J. D., de Brito, J., & Ahmed, H. (2017). Effect of incorporation of high volume of recycled concrete aggregates and fly ash on the strength and global warming potential of concrete. Journal of Cleaner Production, 166, 485–502. https://doi.org/10.1016/j.jclepro.2017.07.23610.1016/j.jclepro.2017.07.236 ↗
37. Lee, H., Hanif, A., Usman, M., et al. (2018). Performance evaluation of concrete incorporating glass powder and glass sludge wastes as supplementary cementing material. Journal of Cleaner Production, 170, 683–693. https://doi.org/10.1016/j.jclepro.2017.09.13310.1016/j.jclepro.2017.09.133 ↗
38. Liu, K.-W., & Mukhopadhyay, A. K. (2016). Accelerated concrete-cylinder test for alkali-silica reaction. Journal of Testing and Evaluation, 44, 1229–1238.10.1520/JTE20140334 ↗
39. McEwan, A.E. (1988). From cottages to’Skyscrapers’: the architecture of AE & ES luttrell in Tasmania and New Zealand
40. Mehta, P. K. (2002). Greening of the Concrete industry for sustainable development. Concrete International, 24, 23–28.
41. Metilda, D. L., Selvamony, C., Anandakumar, R., & Seeni, A. (2015). Investigations on optimum possibility of replacing cement partially by redmud in concrete. Science and Research Essays, 10, 137–143.10.5897/SRE2015.6166 ↗
42. Metwally, I. M. (2007). Investigations on the performance of concrete made with blended finely milled waste glass. Advances in Structural Engineering, 10, 47–53.10.1260/136943307780150823 ↗
43. Mirza, J., Riaz, M., Naseer, A., et al. (2009). Pakistani bentonite in mortars and concrete as low cost construction material. Applied Clay Science, 45, 220–226. https://doi.org/10.1016/j.clay.2009.06.01110.1016/j.clay.2009.06.011 ↗
44. Mohseni, E., Ranjbar, M. M., Yazdi, M. A., et al. (2015). The effects of silicon dioxide, iron(III) oxide and copper oxide nanomaterials on the properties of self-compacting mortar containing fly ash. Magazine of Concrete Research, 67, 1112–1124. https://doi.org/10.1680/macr.15.0005110.1680/macr.15.00051 ↗
45. Müller, N., Harnisch, J. (2008) How to turn around the trend of cement related emissions in the developing world.
46. Mwiti, M.J., Karanja, T.J., Muthengia, W.J. (2018). Thermal resistivity of chemically activated calcined clays-based cements. In: RILEM bookseries. Springer, pp 327–33310.1007/978-94-024-1207-9_53 ↗
47. Naik, T. R. (2008). Sustainability of concrete construction. Practice Periodical on Structural Design and Construction, 13, 98–103. https://doi.org/10.1061/(ASCE)1084-0680(2008)13:2(98)10.1061/(ASCE)1084-0680(2008)13:2(98) ↗
48. Nassar, R.-U.-D., & Soroushian, P. (2011). Field investigation of concrete incorporating milled waste glass. J Solid Waste Technol Manag, 37, 307–319.10.5276/JSWTM.2011.307 ↗
49. Nassar, R.-U.-D., & Soroushian, P. (2012). Green and durable mortar produced with milled waste glass. Magazine of Concrete Research, 64, 605–615. https://doi.org/10.1680/macr.11.0008210.1680/macr.11.00082 ↗
50. Oh, D.-Y., Noguchi, T., Kitagaki, R., & Park, W.-J. (2014). CO2 emission reduction by reuse of building material waste in the Japanese cement industry. Renewable and Sustainable Energy Reviews, 38, 796–810. https://doi.org/10.1016/j.rser.2014.07.03610.1016/j.rser.2014.07.036 ↗
51. Okeke, K.L., Adedeji, A.A. (2016). A review on the properties of concrete incorporated with waste glass as a substitute for cement. 5:396–407
52. Pereira-de-Oliveira, L. A., Castro-Gomes, J. P., & Santos, P. M. S. (2012). The potential pozzolanic activity of glass and red-clay ceramic waste as cement mortars components. Construction and Building Materials, 31, 197–203.10.1016/j.conbuildmat.2011.12.110 ↗
53. Prabhu, G. G., Hyun, J. H., & Kim, Y. Y. (2014). Effects of foundry sand as a fine aggregate in concrete production. Construction and Building Materials, 70, 514–521.10.1016/j.conbuildmat.2014.07.070 ↗
54. Rahma, A., El Naber, N., & Issa Ismail, S. (2017). Effect of glass powder on the compression strength and the workability of concrete. Cogent Engineering, 4, 1373415. https://doi.org/10.1080/23311916.2017.137341510.1080/23311916.2017.1373415 ↗
55. Rashad, A. M. (2014). Recycled waste glass as fine aggregate replacement in cementitious materials based on Portland cement. Construction and Building Materials, 72, 340–357. https://doi.org/10.1016/j.conbuildmat.2014.08.09210.1016/j.conbuildmat.2014.08.092 ↗
56. Ryou, J., Shah, S. P., & Konsta-Gdoutos, M. S. (2006). Recycling of cement industry wastes by grinding process. Advances in Applied Ceramics, 105, 274–279. https://doi.org/10.1179/174367606X12876610.1179/174367606X128766 ↗
57. Šahmenko, G., Korjakins, A., & Būmanis, Ģ. (2009). Bore-silicate glass waste of lamp as a micro-filler for concrete. Rigas Tehniskas Universitates Zinatniskie Raksti, 10, 131.
58. Sankh AC, Biradar PM, Naghathan SJ, Ishwargol MB (2014) Recent trends in replacement of natural sand with different alternatives. In: Proceedings of the International Conference on Advances in Engineering and Technology. pp 59–66
59. Shannag, M. J., Brincker, R., & Hansen, W. (1997). Pullout behavior of steel fibers from cement-based composites. Cement and Concrete Research, 27, 925–936.10.1016/S0008-8846(97)00061-6 ↗
60. Shao, Y., Lefort, T., Moras, S., & Rodriguez, D. (2000). Studies on concrete containing ground waste glass. Cement and Concrete Research, 30, 91–100.10.1016/S0008-8846(99)00213-6 ↗
61. Shi, C., Wu, Y., Riefler, C., & Wang, H. (2005). Characteristics and pozzolanic reactivity of glass powders. Cement and Concrete Research, 35, 987–993. https://doi.org/10.1016/j.cemconres.2004.05.01510.1016/j.cemconres.2004.05.015 ↗
62. Smith, R. A., Kersey, J. R., & Griffiths, P. J. (2002). The Construction industry mass balance: resource use, wastes and emissions. Construction, 4, 680.
63. Soroushian, P. (2012). Strength and durability of recycled aggregate concrete containing milled glass as partial replacement for cement. Construction and Building Materials, 29, 368–377.10.1016/j.conbuildmat.2011.10.061 ↗
64. Specimen CT ASTM C 31; one set of four standard cylinders for each compressive-strength test, unless otherwise directed. Mold store Cylind Lab test specimens Except when field-cured test specimens are required
65. Subramani, T., & Ram, S. B. S. (2015). Experimental study on concrete using cement with glass powder. Department of Civil Engineering VMKV Engg Colleg of Vinayaka Mission University Salem, India, 5, 43–53.
66. Taha, B., & Nounu, G. (2009). Utilizing waste recycled glass as sand/cement replacement in concrete. Journal of Materials in Civil Engineering, 21, 709–721. https://doi.org/10.1061/(ASCE)0899-1561(2009)21:12(709)10.1061/(ASCE)0899-1561(2009)21:12(709) ↗
67. Tamanna, N., Sutan, N. M., Tuladhar, R., et al. (2016). Pozzolanic properties of glass powder in cement paste. Journal of Civil Engineering Science and Technology, 7, 75–81.10.33736/jcest.307.2016 ↗
68. Vasudevan, G. (2013). Seri Ganis Kanapathy pillay, Performance of using waste glass powder in concrete as replacement of cement. American Journal of Engineering and Resarch 847–2320
69. Vigneshpandian, G. V., Shruthi, E. A., Venkatasubramanian, C., & Muthu, D. (2017). Utilisation of waste marble dust as fine aggregate in concrete. IOP Conference Series Earth Environmental Science, 80, 012007. https://doi.org/10.1088/1755-1315/80/1/01200710.1088/1755-1315/80/1/012007 ↗
70. Vizcayno, C., de Gutiérrez, R. M., Castello, R., et al. (2010). Pozzolan obtained by mechanochemical and thermal treatments of kaolin. Applied Clay Science, 49, 405–413. https://doi.org/10.1016/j.clay.2009.09.00810.1016/j.clay.2009.09.008 ↗
71. Wood, K, (2008), Microspheres: fillers filled with possibilities. Compos Technol April