A Concise on the Effect of Calcium Oxide on the Properties of Alkali-Activated Materials: A Manual for Civil Engineers
Source abstract
Abstract
Abstract As known, calcium oxide (CaO) is an alkaline material, which can be used widely to increase the clay-containing soils load carrying capacity, to produce aerated concrete and calcium aluminate cement. In the last few years, introducing CaO into alkali-activated materials (AAMs) became a hot topic and attained more attention than other times. Generally, CaO can be incorporated into AAMs as an additive/a part of the main precursor and a sole activator without/with an auxiliary activator. Incorporating CaO into the matrices may improve some properties and worsen others. This mainly depends on the ratio of CaO, curing conditions, activator type and activator concentration, precursor type and testing age. This review collected, summarized and analyzed the available studies focused on the effect of CaO on the fresh (reaction kinetic, workability, setting time) and hardened (mechanical strength, durability and length change) properties of AAMs. In addition, some recommendations for future works were included. The results showed that the inclusion of CaO in AAMs decreased workability and setting time. In spite of there are contradictory results about the effect of CaO on the compressive strength of AAMs, most of them reported higher compressive strength, especially at the early ages. The incorporation of CaO up to 5% in the matrix is more effective than the incorporation of higher ratios. The inclusion of CaO in the matrix decreased water absorption, decreased total porosity, increased wetting/drying as well as acid attack resistivity. The CaO (5–10%) can be used as a sole activator for precursors. Auxiliary activators such as Al2(SO4)3, Na2CO3, Na2SiO3, Na2SO4, CaSO4, NaOH, Ca(NO3)2, NaNO3, Mg(NO3)2, Mg(HCOO)2, Ca(HCOO)2, SO3, gypsum and MgO can be used to enhance the compressive strength of CaO-activated materials, especially at the early ages.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Magnesium Oxide Properties and Applications · Innovative concrete reinforcement materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (64)
Show source-provided references
1. Abriyantoro, D., Dong, J., Hicks, C., & Singh, S. P. (2019). A stochastic optimisation model for biomass outsourcing in the cement manufacturing industry with production planning constraints. Energy, 169, 515–526.10.1016/j.energy.2018.11.114 ↗
2. Alsalman, A., Assi, L. N., Kareem, R. S., Carter, K., & Ziehl, P. (2021). Energy and CO2 emission assessments of alkali-activated concrete and Ordinary Portland Cement concrete: A comparative analysis of different grades of concrete. Cleaner Environmental Systems, 3, 100047.10.1016/j.cesys.2021.100047 ↗
3. Boynton, R. S. (1980). Chemistry and technology of lime and limestone. New York: Wiley. https://lccn.loc.gov/79016140.
4. Burciaga-Díaz, O., Betancourt-Castillo, I., Montes-Escobedo, M., & Escalante-García, J. (2023). One-part pastes and mortars of CaO-Na2CO3 activated blast furnace slag: Microstructural evolution, cost and CO2 emissions. Construction and Building Materials, 368, 130431.10.1016/j.conbuildmat.2023.130431 ↗
5. Chen, Z., & Ye, H. (2022). The role of CaO and MgO incorporation in chloride resistance of sodium carbonate-activated slag. Cement and Concrete Composites. https://doi.org/10.1016/j.cemconcomp.2022.10462510.1016/j.cemconcomp.2022.104625 ↗
6. Chindaprasirt, P., Phoo-ngernkham, T., Hanjitsuwan, S., Horpibulsuk, S., Poowancum, A., & Injorhor, B. (2018). Effect of calcium-rich compounds on setting time and strength development of alkali-activated fly ash cured at ambient temperature. Case Studies in Construction Materials, 9, e00198.10.1016/j.cscm.2018.e00198 ↗
7. Dahal, M., Oinam, Y., Vashistha, P., Oh, J.-E., & Pyo, S. (2023). Cementless ultra-high performance concrete (UHPC) using CaO-activated GGBFS and calcium formate as an accelerator. Journal of Building Engineering. https://doi.org/10.1016/j.jobe.2023.10700010.1016/j.jobe.2023.107000 ↗
8. Dişçi, E., & Polat, R. (2022). The influence of nano-CaO and nano-Al2O3 and curing conditions on perlite based geopolymer concrete produced by the one-part mixing method. Construction and Building Materials, 346, 128484.10.1016/j.conbuildmat.2022.128484 ↗
9. Djayaprabha, H. S., & Nguyen, H.-A. (2023). Utilizing phosphogypsum waste to improve the mechanical and durability performances of cement-free structural mortar containing ground granulated blast furnace slag and calcium oxide. Journal of Building Engineering, 72, 106557.10.1016/j.jobe.2023.106557 ↗
10. Gharieb, M., & Rashad, A. M. (2022). Impact of sugar beet waste on strength and durability of alkali-activated slag cement. Materials Journal, 119(2), 79–90.
11. Greenstein, G. R. (2007). The merck index: An encyclopedia of chemicals, drugs, and biologicals (14th edition). Reference Reviews, 21(6), 40–40. https://doi.org/10.1108/09504120710775534.10.1108/09504120710775534 ↗
12. Gu, K., Jin, F., Al-Tabbaa, A., Shi, B., & Liu, J. (2014). Mechanical and hydration properties of ground granulated blastfurnace slag pastes activated with MgO–CaO mixtures. Construction and Building Materials, 69, 101–108.10.1016/j.conbuildmat.2014.07.032 ↗
13. J. Hilburg, (2019). Concrete production produces eight percent of the world’s carbon dioxide emissions, architecture, international, news, sustainability. Retrieved August 20, 2020, from https://www.archpaper.com/2019/01/concrete-production-eight-percent-co2-emissions/
14. Hossain, M. U., Poon, C. S., Lo, I. M., & Cheng, J. C. (2017). Comparative LCA on using waste materials in the cement industry: A Hong Kong case study. Resources Conservation and Recycling, 120, 199–208.10.1016/j.resconrec.2016.12.012 ↗
15. Jeong, Y., Park, H., Jun, Y., Jeong, J. H., & Oh, J. E. (2016). Influence of slag characteristics on strength development and reaction products in a CaO-activated slag system. Cement and Concrete Composites, 72, 155–167.10.1016/j.cemconcomp.2016.06.005 ↗
16. Ju, C., Liu, Y., Jia, M., Yu, K., Yu, Z., & Yang, Y. (2020). Effect of calcium oxide on mechanical properties and microstructure of alkali-activated slag composites at sub-zero temperature. Journal of Building Engineering. https://doi.org/10.1016/j.jobe.2020.10156110.1016/j.jobe.2020.101561 ↗
17. Jung-Il, S., Yum, W. S., Sim, S., Park, H.-G., & Oh, J. E. (2020). Effect of magnesium formate as compared with magnesium oxide on the strength enhancement and microstructures of CaO-activated Class F fly ash system. Construction and Building Materials, 253, 119140.10.1016/j.conbuildmat.2020.119140 ↗
18. Kim, M. S., Jun, Y., Lee, C., & Oh, J. E. (2013). Use of CaO as an activator for producing a price-competitive non-cement structural binder using ground granulated blast furnace slag. Cement and Concrete Research, 54, 208–214.10.1016/j.cemconres.2013.09.011 ↗
19. Kolhe, S. S., Chang, T.-P., Chen, C.-T., & Shih, J.-Y. (2022). Potential application of thermally treated calcium carbide residue as solid CaO activator for No-cement slag-FGDG composite. Construction and Building Materials, 359, 129530.10.1016/j.conbuildmat.2022.129530 ↗
20. Lee, W., & Van Deventer, J. (2002). The effect of ionic contaminants on the early-age properties of alkali-activated fly ash-based cements. Cement and Concrete Research, 32(4), 577–584.10.1016/S0008-8846(01)00724-4 ↗
21. Liu, Q., He, Q., Li, R., Feng, Y., Lyu, X., Wang, J., & Li, L. (2022a). Influence of colloidal nanosilica on hydration kinetics and properties of CaO/CaSO4-activated slag binder. International Journal of Mining Science and Technology, 32(6), 1407–1418.10.1016/j.ijmst.2022.07.001 ↗
22. Liu, Q., Wang, P., Wang, Z., Lyu, X., & Wang, J. (2022b). Synthesis of nanoparticles from slag and their enhancement effect on hydration properties of CaO/CaSO4-activated slag binder. Advanced Powder Technology, 33(6), 103586.10.1016/j.apt.2022.103586 ↗
23. Madlool, N. A., Saidur, R., Hossain, M. S., & Rahim, N. (2011). A critical review on energy use and savings in the cement industries. Renewable and Sustainable Energy Reviews, 15(4), 2042–2060.10.1016/j.rser.2011.01.005 ↗
24. Matalkah, F., Aqel, R., & Ababneh, A. (2020). Enhancement of the mechanical properties of kaolin geopolymer using sodium hydroxide and calcium oxide. Procedia Manufacturing, 44, 164–171.10.1016/j.promfg.2020.02.218 ↗
25. Menchaca-Ballinas, L., & Escalante-Garcia, J. (2019). Low CO2 emission cements of waste glass activated by CaO and NaOH. Journal of Cleaner Production, 239, 117992.10.1016/j.jclepro.2019.117992 ↗
26. Nguyen, K. T., Le, T. A., Lee, J., Lee, D., & Lee, K. (2017). Investigation on properties of geopolymer mortar using preheated materials and thermogenetic admixtures. Construction and Building Materials, 130, 146–155.10.1016/j.conbuildmat.2016.10.110 ↗
27. Oates, J. A. (2008). Lime and limestone: chemistry and technology, production and uses. John Wiley & Sons.
28. Oates, T. (2000). Lime and limestone, Kirk-Othmer Encyclopedia of Chemical Technology (pp. 1–53). Weinheim: Wiley-VCH Verlag GmbH & Co. KGaA.
29. Oinam, Y., Ju, S., Shin, M., & Pyo, S. (2023). Influence of cellulose micro-fibers on hydration characteristics of cementless UHPC using CaO-activated GGBFS. Construction and Building Materials, 389, 131747.10.1016/j.conbuildmat.2023.131747 ↗
30. Park, H., Jeong, Y., Jun, Y., Jeong, J.-H., & Oh, J. E. (2016a). Strength enhancement and pore-size refinement in clinker-free CaO-activated GGBFS systems through substitution with gypsum. Cement and Concrete Composites, 68, 57–65.10.1016/j.cemconcomp.2016.02.008 ↗
31. Park, H., Jeong, Y., Jun, Y., & Oh, J. E. (2016b). Production of price-competitive bricks using a high volume of stone powder sludge waste and blast furnace slag through cementless CaO activation. Construction and Building Materials, 122, 343–353.10.1016/j.conbuildmat.2016.06.088 ↗
32. Rashad, A. M. (2013a). Metakaolin as cementitious material: History, scours, production and composition–A comprehensive overview. Construction and Building Materials, 41, 303–318.10.1016/j.conbuildmat.2012.12.001 ↗
33. Rashad, A. M. (2013b). A comprehensive overview about the influence of different additives on the properties of alkali-activated slag—a guide for Civil Engineer. Construction and Building Materials, 47, 29–55.10.1016/j.conbuildmat.2013.04.011 ↗
34. Rashad, A. M. (2013c). Alkali-activated metakaolin: A short guide for civil engineer—an overview. Construction and Building Materials, 41, 751–765.10.1016/j.conbuildmat.2012.12.030 ↗
35. Rashad, A. M. (2014). A comprehensive overview about the influence of different admixtures and additives on the properties of alkali-activated fly ash. Materials and Design, 53, 1005–1025.10.1016/j.matdes.2013.07.074 ↗
36. Rashad, A. M. (2015a). A brief on high-volume Class F fly ash as cement replacement–A guide for Civil Engineer. International Journal of Sustainable Built Environment, 4(2), 278–306.10.1016/j.ijsbe.2015.10.002 ↗
37. Rashad, A. M. (2015b). An exploratory study on sodium sulfate activated slag modified with Portland cement. Materials and Structures, 48(12), 4085–4095.10.1617/s11527-014-0468-3 ↗
38. Rashad, A. M. (2018a). An overview on rheology, mechanical properties and durability of high-volume slag used as a cement replacement in paste, mortar and concrete. Construction and Building Materials, 187, 89–117.10.1016/j.conbuildmat.2018.07.150 ↗
39. Rashad, A. M. (2018b). A synopsis about the effect of basalt and natural fibers on geopolymer properties. Natural Resources Conservation and Research, 1, 9.10.24294/nrcr.v1i2.752 ↗
40. Rashad, A. M. (2019a). A synopsis of carbonation of alkali-activated materials. Green Materials, 7(3), 118–136.10.1680/jgrma.18.00052 ↗
41. Rashad, A. M. (2019b). Effect of nanoparticles on the properties of geopolymer materials. Magazine of Concrete Research, 71(24), 1283–1301.10.1680/jmacr.18.00289 ↗
42. Rashad, A. M. (2019c). The effect of polypropylene, polyvinyl-alcohol, carbon and glass fibres on geopolymers properties. Materials Science and Technology, 35(2), 127–146.10.1080/02670836.2018.1514096 ↗
43. Rashad, A. M. (2020). An overview of pumice stone as a cementitious material–the best manual for civil engineer. Silicon. https://doi.org/10.1007/s12633-020-00469-310.1007/s12633-020-00469-3 ↗
44. Rashad, A. M. (2020b). Effect of steel fibers on geopolymer properties—the best synopsis for civil engineer. Construction and Building Materials, 246, 118534.10.1016/j.conbuildmat.2020.118534 ↗
45. Rashad, A. M. (2022a). Effect of limestone powder on the properties of alkali-activated materials—a critical overview. Construction and Building Materials, 356, 129188.10.1016/j.conbuildmat.2022.129188 ↗
46. Rashad, A. M. (2022b). Behavior of steel slag aggregate in mortar and concrete—a comprehensive overview. Journal of Building Engineering, 53, 104536.10.1016/j.jobe.2022.104536 ↗
47. Rashad Alaa M. (2023). Silica fume in geopolymers, A comprehensive review of its effects on properties. SpringerBriefs in Applied Science and Technology. https://doi.org/10.1007/978-3-031-33219-710.1007/978-3-031-33219-7 ↗
48. Rashad, A., Bai, Y., Basheer, P., Collier, N., & Milestone, N. (2012). Chemical and mechanical stability of sodium sulfate activated slag after exposure to elevated temperature. Cement and Concrete Research, 42(2), 333–343.10.1016/j.cemconres.2011.10.007 ↗
49. Rashad, A., Bai, Y., Basheer, P., Milestone, N., & Collier, N. (2013). Hydration and properties of sodium sulfate activated slag. Cement and Concrete Composites, 37, 20–29.10.1016/j.cemconcomp.2012.12.010 ↗
50. Rashad, A. M., & Gharieb, M. (2021). Solving the perpetual problem of imperative use heat curing for fly ash geopolymer cement by using sugar beet waste. Construction and Building Materials, 307, 124902.10.1016/j.conbuildmat.2021.124902 ↗
51. Singh, G. B., & Subramaniam, K. V. (2019). Production and characterization of low-energy Portland composite cement from post-industrial waste. Journal of Cleaner Production, 239, 118024.10.1016/j.jclepro.2019.118024 ↗
52. Suh, J.-I., Yum, W. S., Jeong, Y., Yoon, S., Park, H.-G., & Oh, J. E. (2023). Mechanical and microstructural properties of lightweight CaO-activated fly ash composites in the presence of magnesium nitrate. Journal of Building Engineering, 65, 105641.10.1016/j.jobe.2022.105641 ↗
53. Tang, L., Ruan, J., Bo, X., Mi, Z., Wang, S., Dong, G., & Davis, S. J. (2022). Plant-level real-time monitoring data reveal substantial abatement potential of air pollution and CO2 in China’s cement sector. One Earth, 5(8), 892–906.10.1016/j.oneear.2022.07.003 ↗
54. Temuujin, J. V., Van Riessen, A., & Williams, R. (2009). Influence of calcium compounds on the mechanical properties of fly ash geopolymer pastes. Journal of Hazardous Materials. https://doi.org/10.1016/j.jhazmat.2008.12.12110.1016/j.jhazmat.2008.12.121 ↗
55. Tian, Y., Xing, J., Zhao, Y., Sun, X., Wu, P., & Qiu, J. (2021). Influence of aluminum sulfate on strength of CaO-activated slag system. Construction and Building Materials, 306, 124895.10.1016/j.conbuildmat.2021.124895 ↗
56. Van Deventer, J., Provis, J., Duxson, P., & Lukey, G. (2007). Reaction mechanisms in the geopolymeric conversion of inorganic waste to useful products. Journal of Hazardous Materials, 139(3), 506–513.10.1016/j.jhazmat.2006.02.044 ↗
57. Wang, J., Lyu, X., Wang, L., Cao, X., Liu, Q., & Zang, H. (2018). Influence of the combination of calcium oxide and sodium carbonate on the hydration reactivity of alkali-activated slag binders. Journal of Cleaner Production, 171, 622–629.10.1016/j.jclepro.2017.10.077 ↗
58. Wang, K., Yan, T., Li, R., & Pan, W. (2022). A review for Ca (OH) 2/CaO thermochemical energy storage systems. Journal of Energy Storage, 50, 104612.10.1016/j.est.2022.104612 ↗
59. Wang, S., Xue, Q., Ma, W., Zhao, K., & Wu, Z. (2021). Experimental study on mechanical properties of fiber-reinforced and geopolymer-stabilized clay soil. Construction and Building Materials, 272, 121914.10.1016/j.conbuildmat.2020.121914 ↗
60. Yum, W. S., Suh, J.-I., Jeon, D., & Oh, J. E. (2020). Strength enhancement of CaO-activated slag system through addition of calcium formate as a new auxiliary activator. Cement and Concrete Composites, 109, 103572.10.1016/j.cemconcomp.2020.103572 ↗
61. Yum, W. S., Suh, J.-I., Sim, S., Yoon, S., Jun, Y., & Oh, J. E. (2019). Influence of calcium and sodium nitrate on the strength and reaction products of the CaO-activated GGBFS system. Construction and Building Materials, 215, 839–848.10.1016/j.conbuildmat.2019.04.240 ↗
62. Zhao, Y., Qiu, J., Zhang, S., Guo, Z., Ma, Z., Sun, X., & Xing, J. (2020b). Effect of sodium sulfate on the hydration and mechanical properties of lime-slag based eco-friendly binders. Construction and Building Materials, 250, 118603.10.1016/j.conbuildmat.2020.118603 ↗
63. Zhao, Z., Qu, X., & Li, J. (2020a). Microstructure and properties of fly ash/cement-based pastes activated with MgO and CaO under hydrothermal conditions. Cement and Concrete Composites, 114, 103739.10.1016/j.cemconcomp.2020.103739 ↗
64. Zheng, D., Ji, T., & Wang, G. (2021). Effect of CaO on the autogenous shrinkage of alkali-activated slag mortar. Advances in Materials Science and Engineering. https://doi.org/10.1155/2021/991883410.1155/2021/9918834 ↗