Crystallization Behavior, Mechanical Properties, and Chemical Resistance of Leucite–Fluoroapatite Glass‐Ceramic Glazes
Source abstract
Abstract
The roles of Li 2 O and B 2 O 3 and heat‐treatment condition on crystallization behavior and flowability of leucite–fluoroapatite‐based glass‐ceramic glazes were investigated. The thermal expansion coefficient, mechanical, and chemical properties of the optimum specimen were determined. Glaze firing was performed in the 650–1100°C interval, in one and two step processes. Based on the results, B 2 O 3 was more effective than Li 2 O in point of flowability view. Also, the microstructures varied with the adopted firing process, so that the two‐step heat‐treated sample showed superior mechanical properties than the one‐step heat‐treated specimens.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Recycling and utilization of industrial and municipal waste in materials production · Glass properties and applications · Pigment Synthesis and Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Materials engineering Division School of engineering Islamic Azad University Karaj Branch Tehran Iran
Ceramic Division School of Metallurgy & Materials Engineering Iran University of Science & Technology Tehran Iran
References (18)
Show source-provided references
1. Craig R.G. · 2002 · 576
2. Höland W. · 2002 · 32
3. 10.1177/0022034591070002080110.1177/00220345910700020801 ↗
4. 10.1016/j.dental.2005.10.00310.1016/j.dental.2005.10.003 ↗
5. 10.1016/j.dental.2005.02.00110.1016/j.dental.2005.02.001 ↗
6. 10.1023/A:100483821939710.1023/A:1004838219397 ↗
7. 10.1016/j.dental.2008.01.00310.1016/j.dental.2008.01.003 ↗
8. 10.1016/j.jdent.2005.02.00110.1016/j.jdent.2005.02.001 ↗
9. 10.1016/j.dental.2008.03.00210.1016/j.dental.2008.03.002 ↗
10. 10.1016/j.jdent.2008.01.01710.1016/j.jdent.2008.01.017 ↗
11. Oral Health for a Lifetime: Preventive Strategies for the Older Adult
12. 10.1016/S0142-9612(99)00030-710.1016/S0142-9612(99)00030-7 ↗
13. 10.1016/0022-3093(94)00464-110.1016/0022-3093(94)00464-1 ↗
14. 10.1016/S0022-3093(00)00164-210.1016/S0022-3093(00)00164-2 ↗
15. 10.1023/A:100897741683410.1023/A:1008977416834 ↗
16. 10.1007/s10856-006-0441-y10.1007/s10856-006-0441-y ↗
17. 10.1016/j.jeurceramsoc.2006.04.10110.1016/j.jeurceramsoc.2006.04.101 ↗
18. 10.1023/A:100445730597010.1023/A:1004457305970 ↗