The effect of heat treatment on tensile properties of 2D C/SiC composites

Hui Mei, Mingyang Lu, Shixiang Zhou, Laifei Cheng

Publisher page

Abstract

Abstract Two‐dimensional (2D) carbon fiber reinforced silicon carbide (C/SiC) composites with different initial strength were prepared by chemical vapor infiltration (CVI). After tensile property testing, results exhibited that as the heat‐treatment temperature (HTT) increases to 1900°C, the tensile strength and toughness of the low strength specimen (LSS) increased by 110% and 530%, while the high strength specimen (HSS) increased by 5.4% and 550%, respectively. As observed from morphologies, the heat treatment increases the graphitization of the amorphous PyC interphase, which leads to the weakening of interfacial bonding strength (IBS). Meanwhile, the defects arising from heat treatment cause thermal residual stress relaxation. Therefore, the tensile strength and toughness of LSS with relatively high initial IBS increase significantly as HTT increases. For HSS with moderate initial IBS, the heat treatment slightly improves the tensile strength, but significantly improves the toughness. Consequently, the post‐heat‐treatment tensile properties of 2D C/SiC composites can be regulated by varying HTTs and different initial strength.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Advanced ceramic materials synthesis · MXene and MAX Phase Materials · Advanced materials and composites

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Science and technology on Thermostructural Composite Materials Laboratory School of Materials Science and Engineering Northwestern Polytechnical University Xi’an PR China

References (29)

Show source-provided references
1. 10.1016/j.actaastro.2004.05.05210.1016/j.actaastro.2004.05.052 ↗
2. 10.1111/j.1744-7402.2005.02009.x10.1111/j.1744-7402.2005.02009.x ↗
3. 10.1016/S0921-5093(00)01533-110.1016/S0921-5093(00)01533-1 ↗
4. 10.1016/j.msea.2008.07.01110.1016/j.msea.2008.07.011 ↗
5. 10.1016/j.carbon.2012.11.00110.1016/j.carbon.2012.11.001 ↗
6. 10.1016/j.ceramint.2005.08.01110.1016/j.ceramint.2005.08.011 ↗
7. 10.1016/j.jmatprotec.2008.08.01410.1016/j.jmatprotec.2008.08.014 ↗
8. 10.1016/j.carbon.2013.01.07610.1016/j.carbon.2013.01.076 ↗
9. 10.1016/S0266-3538(00)00124-X10.1016/S0266-3538(00)00124-X ↗
10. 10.1016/j.ceramint.2018.04.25510.1016/j.ceramint.2018.04.255 ↗
11. 10.1016/j.compositesb.2017.04.00210.1016/j.compositesb.2017.04.002 ↗
12. 10.1016/j.jallcom.2019.07.16310.1016/j.jallcom.2019.07.163 ↗
13. 10.1016/j.compositesb.2017.07.07910.1016/j.compositesb.2017.07.079 ↗
14. Effect of heat‐treatment on the strength of C/C‐SiC joints
15. 10.1016/j.jallcom.2018.08.10410.1016/j.jallcom.2018.08.104 ↗
16. 10.2320/matertrans.45.30710.2320/matertrans.45.307 ↗
17. 10.1016/j.ceramint.2018.05.16010.1016/j.ceramint.2018.05.160 ↗
18. Effect of high temperature treatment on the microstructure and mechanical properties of binary layer textured 2D C/C composites
19. 10.1016/0955-2219(95)00095-C10.1016/0955-2219(95)00095-C ↗
20. Damage evolution and fracture events sequence in various composites by acoustic emission technique
21. Longitudinal splitting and fiber breakage characterization in graphite epoxy using acoustic emission data
22. 10.1007/BF0298436510.1007/BF02984365 ↗
23. 10.1016/j.compscitech.2005.07.01210.1016/j.compscitech.2005.07.012 ↗
24. 10.1016/j.ceramint.2005.02.01410.1016/j.ceramint.2005.02.014 ↗
25. 10.1016/j.compositesa.2012.06.01110.1016/j.compositesa.2012.06.011 ↗
26. 10.1016/j.carbon.2005.07.00310.1016/j.carbon.2005.07.003 ↗
27. 10.1016/S0008-6223(03)00125-810.1016/S0008-6223(03)00125-8 ↗
28. 10.1016/j.carbon.2010.01.05610.1016/j.carbon.2010.01.056 ↗
29. 10.1016/j.msea.2006.06.06010.1016/j.msea.2006.06.060 ↗