Synthesis and Properties of a New Dental Material Based on Nano‐Structured Highly Active Calcium Silicates and Calcium Carbonates
Source abstract
Abstract
A synthesis of a new dental material, based on nano‐structured highly active calcium silicates and calcium carbonates, is described in this paper. Phase analysis of this material, before and after hydration, was performed by X‐ray diffraction and showed that active silicate phases were transformed into tobermorite phase, while carbonates remained unchanged. The mechanism of hydration was fully described. The morphology of the sample was studied by SEM , and typical appearance of the present phases was particularly discussed. The mechanical properties and setting time of this material make it very promising for potential application in dental practice.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Endodontics and Root Canal Treatments · Dental materials and restorations · Building materials and conservation
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Institute for Nuclear Sciences “Vinča” University of Belgrade 11001 Belgrade Serbia
Faculty of Stomatology University of Belgrade 11000 Belgrade Serbia
References (19)
Show source-provided references
1. 10.1111/j.1365-2591.2008.01415.x10.1111/j.1365-2591.2008.01415.x ↗
2. 10.1097/00004770-200402000-0001510.1097/00004770-200402000-00015 ↗
3. 10.1097/01.don.0000145429.04231.e210.1097/01.don.0000145429.04231.e2 ↗
4. 10.1016/j.joen.2006.11.00210.1016/j.joen.2006.11.002 ↗
5. 10.1016/j.joen.2009.03.00610.1016/j.joen.2009.03.006 ↗
6. 10.1111/j.1365-2591.2007.01248.x10.1111/j.1365-2591.2007.01248.x ↗
7. V.Jokanovic Nanomedicine the greatest challenge of 21. century 193–230 DATASTATUS Belgrade Serbia 2012.
8. 10.1016/j.jallcom.2006.11.15110.1016/j.jallcom.2006.11.151 ↗
9. SiO2 Thin Films Obtained from Silica Sols by Thermal Spraying
10. 10.1016/j.dental.2005.06.00510.1016/j.dental.2005.06.005 ↗
11. 10.1111/j.1365-2591.2007.01330.x10.1111/j.1365-2591.2007.01330.x ↗
12. 10.5395/JKACD.2010.35.5.34410.5395/JKACD.2010.35.5.344 ↗
13. 10.1016/j.dental.2007.06.00410.1016/j.dental.2007.06.004 ↗
14. 10.1111/j.1744-7402.2011.02635.x10.1111/j.1744-7402.2011.02635.x ↗
15. 10.1111/j.1151-2916.1986.tb07446.x10.1111/j.1151-2916.1986.tb07446.x ↗
16. 10.1021/cm034227f10.1021/cm034227f ↗
17. Chemical Composition of C‐S‐H Gel Formed in the Hydration of Calcium Silicate Pastes
18. J. J.Chen “The Nanostructure of Calcium Silicate Hydrate” Ph.D. Thesis Department of Materials Science and Engineering Northwestern University Evanston IL 2003.
19. Fundamental Hydration Kinetic Features of the Major Cement Constituents: Ca3SiO5 and h‐Ca2SiO4