Reactions and emissivity of cerium oxide with phosphate binder coating on basic refractory brick

Jindaporn Juthapakdeeprasert, Oriol Gavalda Diaz, Wirat Lerdprom, Domingos De Sousa Meneses, Doni D. Jayaseelan, William E. Lee

Publisher page

Abstract

Abstract High emissivity coatings which aim to help the cement industry reduce heat loss in its production process have been developed with different CeO 2 and AlH 6 O 12 P 3 ratios (1:3, 1:5, and 1:12 by volume). The coating slurries were shear thinning and after heat treatment in air at 1300°C, 1°C/min, dwell 3 hours, XRD revealed that CePO 4 forms more easily as the Ce/P ratio decreases. The composition with a 1:5 ratio of CeO 2 :AlH 6 O 12 P 3 was gun sprayed on basic refractory bricks, then heat treated under the same conditions as the slurries. SEM, (S)TEM and EDX were used to study thickness, microstructure, and chemical composition of the coatings which revealed that the coating was composed of pores, CeO 2 grains, CePO 4 grains, and M‐P‐O glass. SEM images show that CePO 4 was nucleated from a reaction between CeO 2 and AlH 6 O 12 P 3 . Consequently, CePO 4 grains (~2 µm diameter) were smaller than CeO 2 (~10 µm diameter). The emissivities of un‐coated and coated basic refractory bricks were measured at 1100 and 1300°C over the wave number range of 700‐12 000 cm −1 . At both temperatures, the emissivity of the coated bricks was higher than the uncoated bricks and the emissivity was measured to be higher at a higher temperature for both samples. The coated bricks gave the highest emissivity of 0.81 from 1050 to 11 000 cm −1 which is about twice the un‐coated bricks for the same conditions. This demonstrates that the developed high emissivity coating has potential to be used with basic refractory brick.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Pigment Synthesis and Properties · Magnesium Oxide Properties and Applications · Recycling and utilization of industrial and municipal waste in materials production

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Centre for Advanced Structural Ceramics (CASC) Department of Materials Imperial College London London UK

CNRS, CEMHTI UPR3079, University Orléans Orléans France

Department of Aerospace and Aircraft Engineering Kingston University London London UK

References (21)

Show source-provided references
1. 10.1016/j.rser.2012.10.04610.1016/j.rser.2012.10.046 ↗
2. 10.1016/j.enconman.2004.04.00710.1016/j.enconman.2004.04.007 ↗
3. ChengJ‐JA MartinezWA HaleAP.Lightweight tundish refractory composition. United States PatentOffice 3150989;1991.
4. 10.1016/j.proeng.2016.07.07710.1016/j.proeng.2016.07.077 ↗
5. MaceyCL KnaussRJ.Low thermal conductivity magnesite‐spinel brick and method. United States Patent 4833109;1989.
6. 10.1016/B978-0-12-386944-9.50023-610.1016/B978-0-12-386944-9.50023-6 ↗
7. 10.1016/j.apsusc.2013.05.03410.1016/j.apsusc.2013.05.034 ↗
8. 10.1016/j.matlet.2012.06.08410.1016/j.matlet.2012.06.084 ↗
9. 10.1016/j.tsf.2013.03.10510.1016/j.tsf.2013.03.105 ↗
10. HolcombeCEJr ChapmanLR.High emissivity coating. United States Patents 5668072;1997.
11. 10.1016/j.jeurceramsoc.2016.04.01310.1016/j.jeurceramsoc.2016.04.013 ↗
12. 10.1111/j.1151-2916.2000.tb01477.x10.1111/j.1151-2916.2000.tb01477.x ↗
13. 10.1016/j.jmatprotec.2005.02.09810.1016/j.jmatprotec.2005.02.098 ↗
14. 10.1016/j.infrared.2015.01.01110.1016/j.infrared.2015.01.011 ↗
15. Juthapakdeeprasert J · 2018
16. 10.1246/bcsj.52.103410.1246/bcsj.52.1034 ↗
17. 10.1016/j.jallcom.2019.01.11410.1016/j.jallcom.2019.01.114 ↗
18. 10.1039/C8CP01442F10.1039/C8CP01442F ↗
19. 10.1103/PhysRevB.83.20510410.1103/PhysRevB.83.205104 ↗
20. 10.1063/1.484607710.1063/1.4846077 ↗
21. 10.1007/s10765-005-6726-410.1007/s10765-005-6726-4 ↗