Silica‐based ceramic core for aviation applications: Facile pore filling and flexural strength improvement
Source abstract
Abstract
Abstract The effect of alumina addition on the pore filling process, crystallization behavior and mechanical properties of silica‐based ceramic cores was investigated. The sintered samples at 1250°C were treated at 1550°C for 0.5 hour in order to simulate a casting process condition. The microstructure analysis indicated that an appropriate alumina addition enhanced the pore filling process by supplying a substantial liquid viscous flow. With an increase in the liquid viscous flow, smaller pores were filled first, and larger pores were filled later. The results also indicated that the pore filling process could be enhanced by adding small powder additives to decrease the pore size between the particles in the ceramic material. However, an excessive alumina addition in the silica‐based ceramic cores had a negative effect on the flexural strength and leaching rate. As the alumina content increased from 8 to 12 wt%, the flexural strength of the ceramic core decreased from 16.37 to 4.60 MPa, respectively, and the leaching rate also decreased obviously. These results were explained by an acceleration in crystallization trend of the fused silica particle surface and the merging of connected pores in the sintered body.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Recycling and utilization of industrial and municipal waste in materials production · Concrete and Cement Materials Research
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Materials Science and Engineering Northeastern University Shenyang, Liaoning Peoples R China
School of Metallurgy Northeastern University Shenyang, Liaoning Peoples R China
School of materials science and technology Shenyang Ligong University Shenyang, Liaoning Peoples R China
References (27)
Show source-provided references
1. 10.1016/j.ceramint.2013.06.10810.1016/j.ceramint.2013.06.108 ↗
2. 10.1023/A:102006050831110.1023/A:1020060508311 ↗
3. 10.1016/j.jmatprotec.2012.06.00310.1016/j.jmatprotec.2012.06.003 ↗
4. 10.1016/j.msea.2008.12.01610.1016/j.msea.2008.12.016 ↗
5. 10.1016/j.jmatprotec.2015.01.01010.1016/j.jmatprotec.2015.01.010 ↗
6. 10.1111/jace.1350510.1111/jace.13505 ↗
7. RobbRR YakerC BurdL.Ceramic cores for manufacturing hollow metal castings. 4190450 US Patent.1980.
8. 10.1016/j.ceramint.2016.09.12710.1016/j.ceramint.2016.09.127 ↗
9. 10.1016/j.jnoncrysol.2009.03.00210.1016/j.jnoncrysol.2009.03.002 ↗
10. 10.1111/ijac.1287910.1111/ijac.12879 ↗
11. 10.1016/j.jeurceramsoc.2018.07.05410.1016/j.jeurceramsoc.2018.07.054 ↗
12. 10.1016/j.ceramint.2017.09.18910.1016/j.ceramint.2017.09.189 ↗
13. 10.1016/j.jeurceramsoc.2010.12.01610.1016/j.jeurceramsoc.2010.12.016 ↗
14. 10.1016/S0921-5093(97)00125-110.1016/S0921-5093(97)00125-1 ↗
15. 10.1016/j.jmst.2016.02.01210.1016/j.jmst.2016.02.012 ↗
16. 10.1016/j.jeurceramsoc.2013.06.02510.1016/j.jeurceramsoc.2013.06.025 ↗
17. 10.1017/S088571560001868610.1017/S0885715600018686 ↗
18. 10.1016/S1359-6454(97)00489-810.1016/S1359-6454(97)00489-8 ↗
19. 10.1016/0272-8842(95)90909-310.1016/0272-8842(95)90909-3 ↗
20. Viscous flow of crystalline bodies under the action of surface tension
21. 10.1016/j.ceramint.2016.06.10010.1016/j.ceramint.2016.06.100 ↗
22. Kingery WD · 1976
23. Viscosity and structure of iron‐ and aluminum‐bearing calcium silicate melts at 1 atm
24. 10.1111/j.1551-2916.2005.00430.x10.1111/j.1551-2916.2005.00430.x ↗
25. Preparation and crystallization behavior of oxygen‐deficient
26. 10.1016/j.msea.2006.10.07310.1016/j.msea.2006.10.073 ↗
27. 10.1111/ijac.1272110.1111/ijac.12721 ↗