Fully sintered alumina with a higher Vickers hardness prepared using a gel‐casting process

Kuo‐Yang Lee, Chih‐Cheng Chen, Hsing‐I Hsiang, Fu‐Su Yen, Chi‐Yuen Huang

Publisher page

Abstract

Abstract The dispersant (commercial ammonium polyacrylate), sintering additive (Mg 2+ ), and chelating agent (EDTA) effects on the Zeta potential and rheological behavior of alumina slurry with high solid content were investigated. The alumina ceramic green microstructures and sintered microstructures prepared using slurries with different additives using the gel‐casting process were also studied. It was observed that the dispersion deteriorated after adding Mg 2+ . Slurry simultaneously added with dispersant and EDTA‐chelated Mg 2+ produced higher absolute Zeta potential value and low viscosity due to EDTA chelating with Mg 2+ . The sample added with dispersant and EDTA‐chelated Mg 2+ exhibited a uniform green microstructure, high relative sintered density (99.5% theoretical density), and a nearly pore‐free microstructure with an average grain size of about 1.5 μm. For the first time to our knowledge, the maximum Vickers hardness (22 GPa) was obtained for alumina simultaneously added with Mg 2+ and EDTA, pressureless sintered at 1500°C in air.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Advanced ceramic materials synthesis · Advanced materials and composites · Aluminum Alloys Composites Properties

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Particulate Materials Research Center, Department of Resources Engineering National Cheng Kung University Tainan Taiwan

Department of Mechanical Engineering Far East University Tainan Taiwan

Funding

Ministry of Science and Technology, Taiwan

References (29)

Show source-provided references
1. 10.1111/j.1151-2916.1991.tb04068.x10.1111/j.1151-2916.1991.tb04068.x ↗
2. 10.1111/jace.1225610.1111/jace.12256 ↗
3. 10.1111/j.1151-2916.2003.tb03339.x10.1111/j.1151-2916.2003.tb03339.x ↗
4. 10.1111/j.1151-2916.1988.tb05792.x10.1111/j.1151-2916.1988.tb05792.x ↗
5. Janney MA · 1999 · 1493
6. 10.1016/j.jeurceramsoc.2011.11.03810.1016/j.jeurceramsoc.2011.11.038 ↗
7. 10.1111/j.1151-2916.1994.tb04634.x10.1111/j.1151-2916.1994.tb04634.x ↗
8. 10.1016/0021-9797(88)90193-210.1016/0021-9797(88)90193-2 ↗
9. 10.1016/j.jeurceramsoc.2010.11.00110.1016/j.jeurceramsoc.2010.11.001 ↗
10. 10.1016/j.ceramint.2008.04.00410.1016/j.ceramint.2008.04.004 ↗
11. 10.1016/S0927-7757(99)00429-X10.1016/S0927-7757(99)00429-X ↗
12. 10.1111/j.1551-2916.2004.00181.x10.1111/j.1551-2916.2004.00181.x ↗
13. 10.1002/adem.20140009910.1002/adem.201400099 ↗
14. 10.1016/j.ceramint.2003.09.01410.1016/j.ceramint.2003.09.014 ↗
15. 10.1016/j.ceramint.2011.08.01010.1016/j.ceramint.2011.08.010 ↗
16. 10.1002/9780470917145.ch4510.1002/9780470917145.ch45 ↗
17. 10.1016/j.ceramint.2017.10.09810.1016/j.ceramint.2017.10.098 ↗
18. Smith AL · 99
19. 10.1111/j.1151-2916.1988.tb05855.x10.1111/j.1151-2916.1988.tb05855.x ↗
20. 10.1016/j.jcis.2003.12.02510.1016/j.jcis.2003.12.025 ↗
21. 10.1111/j.1551-2916.2010.03795.x10.1111/j.1551-2916.2010.03795.x ↗
22. 10.1111/j.1151-2916.2003.tb03270.x10.1111/j.1151-2916.2003.tb03270.x ↗
23. 10.1111/j.1151-2916.1995.tb08452.x10.1111/j.1151-2916.1995.tb08452.x ↗
24. 10.1111/j.1151-2916.1979.tb19059.x10.1111/j.1151-2916.1979.tb19059.x ↗
25. 10.1111/j.1551-2916.2005.00370.x10.1111/j.1551-2916.2005.00370.x ↗
26. 10.1016/j.jeurceramsoc.2008.03.02410.1016/j.jeurceramsoc.2008.03.024 ↗
27. 10.1016/j.ceramint.2013.05.05810.1016/j.ceramint.2013.05.058 ↗
28. 10.1111/j.1151-2916.1996.tb08741.x10.1111/j.1151-2916.1996.tb08741.x ↗
29. 10.1016/j.scriptamat.2013.05.01710.1016/j.scriptamat.2013.05.017 ↗