Low‐Temperature Sintering and Microwave Dielectric Properties of ZnNb 2 O 6 – TiO 2 Ceramics with BaCu ( B 2 O 5 ) Additions
Source abstract
Abstract
The influence of BaCu ( B 2 O 5 ) ( BCB ) on densification, phases, microstructure and microwave dielectric properties of ZnNb 2 O 6 – x TiO 2 ( x = 1.70–1.90) composite ceramics have been investigated. Undoped ZnNb 2 O 6 –1.8 TiO 2 ceramics sintered at 1200°C exhibit temperature coefficient of resonant frequency ( τ f ) ~9.25 ppm/°C. When BaCu ( B 2 O 5 ) was added, the sintering temperature of the ZnNb 2 O 6 –1.8 TiO 2 composite ceramics was effectively reduced to 950°C. The results indicated that the permittivity and Q × f were dependent on the sintering temperature and the amounts of BaCu ( B 2 O 5 ). Addition of 3.0 wt% BaCu ( B 2 O 5 ) in ZnNb 2 O 6 –1.8 TiO 2 ceramics sintered at 950°C showed excellent dielectric properties of ε r = 40.9, Q × f = 12,200 GHz ( f = 5.015 GHz) and τ f = +0.3 ppm/°C.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Microwave Dielectric Ceramics Synthesis · Ferroelectric and Piezoelectric Materials · Dielectric properties of ceramics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Electronic Science and Technology Huazhong University of Science and Technology Wuhan 430074 People's Republic of China
References (29)
Show source-provided references
1. 10.1016/j.jallcom.2008.04.09910.1016/j.jallcom.2008.04.099 ↗
2. 10.1111/j.1551-2916.2009.03060.x10.1111/j.1551-2916.2009.03060.x ↗
3. 10.1111/j.1551-2916.2004.00871.x10.1111/j.1551-2916.2004.00871.x ↗
4. 10.1016/B978-0-08-045330-9.00008-X10.1016/B978-0-08-045330-9.00008-X ↗
5. 10.1111/j.1551-2916.2008.02919.x10.1111/j.1551-2916.2008.02919.x ↗
6. Dielectric Properties of AB2O6 Compounds at Microwave Frequencies (A=Ca, Mg, Mn, Co, Ni, Zn and B=Nb,Ta)
7. 10.1016/S0025-5408(97)00034-210.1016/S0025-5408(97)00034-2 ↗
8. 10.1016/j.matlet.2005.08.01610.1016/j.matlet.2005.08.016 ↗
9. 10.1016/j.jeurceramsoc.2008.06.01910.1016/j.jeurceramsoc.2008.06.019 ↗
10. 10.1557/JMR.2000.019310.1557/JMR.2000.0193 ↗
11. 10.1016/S0955-2219(03)00133-X10.1016/S0955-2219(03)00133-X ↗
12. 10.1016/j.matchemphys.2009.06.00510.1016/j.matchemphys.2009.06.005 ↗
13. 10.1016/j.jallcom.2010.04.13110.1016/j.jallcom.2010.04.131 ↗
14. 10.1016/j.ceramint.2007.07.00810.1016/j.ceramint.2007.07.008 ↗
15. 10.1111/j.1151-2916.1997.tb03081.x10.1111/j.1151-2916.1997.tb03081.x ↗
16. 10.1016/j.jeurceramsoc.2006.11.04310.1016/j.jeurceramsoc.2006.11.043 ↗
17. 10.1111/j.1551-2916.2006.01157.x10.1111/j.1551-2916.2006.01157.x ↗
18. 10.1109/TMTT.1960.112474910.1109/TMTT.1960.1124749 ↗
19. 10.1109/TMTT.1970.112727110.1109/TMTT.1970.1127271 ↗
20. Blachnik R. · 1997
21. 10.1016/0925-8388(94)90827-310.1016/0925-8388(94)90827-3 ↗
22. West A. R. · 1988 · 377
23. 10.1007/BF0167202810.1007/BF01672028 ↗
24. 10.1016/j.ceramint.2007.09.04910.1016/j.ceramint.2007.09.049 ↗
25. 10.1143/JJAP.40.599410.1143/JJAP.40.5994 ↗
26. 10.1111/j.1151-2916.1997.tb03066.x10.1111/j.1151-2916.1997.tb03066.x ↗
27. 10.1111/j.1151-2916.2000.tb01154.x10.1111/j.1151-2916.2000.tb01154.x ↗
28. 10.1111/j.1551-2916.2005.00458.x10.1111/j.1551-2916.2005.00458.x ↗
29. 10.1111/j.1551-2916.2010.03999.x10.1111/j.1551-2916.2010.03999.x ↗