The effects of adding nano‐alumina filler on the properties of polymer‐derived SiC coating
Source abstract
Abstract
Abstract In this paper, SiC coating was prepared using the polymer‐derived ceramic method; then the effect of nano‐alumina as a filler material was studied. First of all, polycarbosilane(PCS) was dissolved in xylene; after that, different amounts of nano‐alumina particles were added to the solution. The coating was deposited on the alumina substrate using the dip‐coating method; this was followed by sintering at 1200℃. The phase content and microstructure of the samples were studied by X‐ray diffraction and scanning electron microscope methods, respectively. Nanohardness, Young's modulus, and coating adhesion were investigated by a nanoindentation method. The sheet resistance was evaluated using the four‐point probe technique; also, the wear resistance of the coating was studied by applying the pin‐on‐disk method. It was found that the addition of the nano‐alumina filler up to 20 wt% drastically improved the adhesion and wear resistance of the SiC coating.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Metal and Thin Film Mechanics · Diamond and Carbon-based Materials Research · Advanced ceramic materials synthesis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Materials Science and Engineering Shahrood University of Technology Shahrood Iran
References (72)
Show source-provided references
1. 10.1016/j.matlet.2018.03.03210.1016/j.matlet.2018.03.032 ↗
2. 10.1007/s10904-011-9481-y10.1007/s10904-011-9481-y ↗
3. 10.1016/j.ast.2006.01.00110.1016/j.ast.2006.01.001 ↗
4. 10.1016/S0043-1648(01)00844-410.1016/S0043-1648(01)00844-4 ↗
5. 10.1016/S1359-835X(98)00143-210.1016/S1359-835X(98)00143-2 ↗
6. 10.1016/0376-7388(94)00322-P10.1016/0376-7388(94)00322-P ↗
7. 10.1016/j.tsf.2007.06.07210.1016/j.tsf.2007.06.072 ↗
8. 10.1111/j.1551-2916.1987.tb00069.x10.1111/j.1551-2916.1987.tb00069.x ↗
9. 10.1016/j.surfcoat.2006.07.20410.1016/j.surfcoat.2006.07.204 ↗
10. 10.1016/j.jallcom.2017.09.28110.1016/j.jallcom.2017.09.281 ↗
11. 10.1016/j.ceramint.2018.02.03310.1016/j.ceramint.2018.02.033 ↗
12. 10.1016/j.jeurceramsoc.2011.03.00210.1016/j.jeurceramsoc.2011.03.002 ↗
13. 10.1016/j.surfcoat.2009.03.05710.1016/j.surfcoat.2009.03.057 ↗
14. 10.1016/S0927-796X(00)00008-510.1016/S0927-796X(00)00008-5 ↗
15. 10.1111/ijac.1357210.1111/ijac.13572 ↗
16. 10.1002/1527-2648(200006)2:6<339::AID-ADEM339>3.0.CO;2-K10.1002/1527-2648(200006)2:6<339::AID-ADEM339>3.0.CO;2-K ↗
17. 10.2109/jcersj.114.52410.2109/jcersj.114.524 ↗
18. 10.1111/j.1151-2916.1997.tb03124.x10.1111/j.1151-2916.1997.tb03124.x ↗
19. 10.2109/jcersj.114.56710.2109/jcersj.114.567 ↗
20. 10.1111/j.1151-2916.1976.tb10975.x10.1111/j.1151-2916.1976.tb10975.x ↗
21. 10.1023/A:101794282665710.1023/A:1017942826657 ↗
22. 10.1007/BF0037627110.1007/BF00376271 ↗
23. 10.1111/j.1551-2916.2007.02019.x10.1111/j.1551-2916.2007.02019.x ↗
24. 10.1007/s10904-006-9030-210.1007/s10904-006-9030-2 ↗
25. 10.1002/pssr.20060003610.1002/pssr.200600036 ↗
26. 10.2109/jcersj2.115.98210.2109/jcersj2.115.982 ↗
27. 10.1007/s10853-006-0242-110.1007/s10853-006-0242-1 ↗
28. 10.1016/j.mseb.2007.09.02510.1016/j.mseb.2007.09.025 ↗
29. 10.1177/00219983910250040410.1177/002199839102500404 ↗
30. 10.1016/0955-2219(92)90022-610.1016/0955-2219(92)90022-6 ↗
31. 10.1016/0955-2219(96)00066-010.1016/0955-2219(96)00066-0 ↗
32. 10.1016/S1359-6462(99)00403-010.1016/S1359-6462(99)00403-0 ↗
33. 10.1016/j.jeurceramsoc.2005.01.04910.1016/j.jeurceramsoc.2005.01.049 ↗
34. 10.1111/ijac.1340610.1111/ijac.13406 ↗
35. 10.2109/jcersj.99.97410.2109/jcersj.99.974 ↗
36. 10.1016/j.jeurceramsoc.2010.09.01310.1016/j.jeurceramsoc.2010.09.013 ↗
37. 10.1016/j.matdes.2009.08.03410.1016/j.matdes.2009.08.034 ↗
38. 10.1016/j.jeurceramsoc.2006.09.00710.1016/j.jeurceramsoc.2006.09.007 ↗
39. 10.1557/JMR.1993.163510.1557/JMR.1993.1635 ↗
40. 10.1111/j.1151-2916.1982.tb10460.x10.1111/j.1151-2916.1982.tb10460.x ↗
41. 10.1111/j.1151-2916.2001.tb00636.x10.1111/j.1151-2916.2001.tb00636.x ↗
42. 10.1016/j.matlet.2012.02.00610.1016/j.matlet.2012.02.006 ↗
43. 10.2109/jcersj.99.9410.2109/jcersj.99.94 ↗
44. 10.1016/j.jeurceramsoc.2014.05.00210.1016/j.jeurceramsoc.2014.05.002 ↗
45. 10.1016/j.matdes.2013.07.00110.1016/j.matdes.2013.07.001 ↗
46. 10.1002/app.3813210.1002/app.38132 ↗
47. 10.1002/app.1979.07023031910.1002/app.1979.070230319 ↗
48. 10.1021/ma400036810.1021/ma4000368 ↗
49. 10.1111/j.1151-2916.1995.tb07965.x10.1111/j.1151-2916.1995.tb07965.x ↗
50. 10.1016/j.ceramint.2016.06.09910.1016/j.ceramint.2016.06.099 ↗
51. 10.1557/JMR.1992.156410.1557/JMR.1992.1564 ↗
52. 10.1016/j.jeurceramsoc.2006.05.05710.1016/j.jeurceramsoc.2006.05.057 ↗
53. 10.1557/JMR.1994.009610.1557/JMR.1994.0096 ↗
54. 10.1016/j.jnucmat.2009.05.00110.1016/j.jnucmat.2009.05.001 ↗
55. 10.1016/j.compscitech.2007.04.02210.1016/j.compscitech.2007.04.022 ↗
56. 10.1016/j.jallcom.2017.03.10010.1016/j.jallcom.2017.03.100 ↗
57. 10.1016/j.jeurceramsoc.2006.09.01210.1016/j.jeurceramsoc.2006.09.012 ↗
58. High temperature nanoindentation testing of amorphous SiC and B4C thin films. Defect and Diffusion Forum
59. 10.1016/j.surfcoat.2003.10.14010.1016/j.surfcoat.2003.10.140 ↗
60. 10.1016/S0925-9635(00)00497-010.1016/S0925-9635(00)00497-0 ↗
61. 10.1016/S0022-3093(96)00569-810.1016/S0022-3093(96)00569-8 ↗
62. 10.1016/0257-8972(91)90101-210.1016/0257-8972(91)90101-2 ↗
63. 10.1088/0022-3727/38/24/R0110.1088/0022-3727/38/24/R01 ↗
64. 10.1007/s11837-017-2496-210.1007/s11837-017-2496-2 ↗
65. 10.1016/S0924-0136(03)00300-510.1016/S0924-0136(03)00300-5 ↗
66. 10.1016/0254-0584(96)80046-010.1016/0254-0584(96)80046-0 ↗
67. 10.1016/j.jeurceramsoc.2012.07.02110.1016/j.jeurceramsoc.2012.07.021 ↗
68. 10.1007/s11664-003-0134-y10.1007/s11664-003-0134-y ↗
69. 10.1007/BF0265562610.1007/BF02655626 ↗
70. 10.1016/j.sse.2017.10.04210.1016/j.sse.2017.10.042 ↗
71. 10.1016/S0257-8972(99)00319-910.1016/S0257-8972(99)00319-9 ↗
72. 10.1016/S0257-8972(02)00486-310.1016/S0257-8972(02)00486-3 ↗