Reactive air brazing of 3YSZ ceramic to aluminized Crofer22H stainless steel using Ag–CuO fillers
Source abstract
Abstract
Abstract In this work, an effective protected Al 2 O 3 layer was fabricated first on the surface of Crofer22H by reactive air aluminization to suppress cathodic poisoning in solid oxide fuel cells. Then, the reactive air brazing of aluminized Crofer22H to 3YSZ ceramics was carried out by using Ag–CuO fillers. The effects of CuO content and brazing temperature on the interfacial microstructure and mechanical properties of the joints were studied in detail. The results indicated that maintaining a continuous Al 2 O 3 layer was the prerequisite for achieving a reliable joint. And the interfacial reaction gradually became intense with the increase of CuO content, and the continuity of the Al 2 O 3 layer was disrupted as it was increased to 6 mol%. The well‐connected joints could be achieved when brazing at 970–1100°C with Ag–2CuO filler. The interfacial microstructure did not obviously change with increasing temperature, and the joint strength was stable at ∼35 MPa. While the interfacial reaction gradually weakened with increasing temperature as brazing with Ag–4CuO filler, the well‐connected joints were obtained when brazing above 1000°C, and the maximum shear strength of ∼44.3 MPa was obtained when brazing at 1050°C for 30 min.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Advancements in Solid Oxide Fuel Cells · Advanced ceramic materials synthesis · Nuclear materials and radiation effects
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
State Key Laboratory of Advanced Welding and Joining Harbin Institute of Technology Harbin China
Shandong Provincial Key Lab of Special Welding Technology Harbin Institute of Technology at Weihai Weihai China
Shandong Institute of Shipbuilding Technology Weihai China
References (43)
Show source-provided references
1. 10.1016/j.ceramint.2018.01.01510.1016/j.ceramint.2018.01.015 ↗
2. 10.1016/j.ijhydene.2017.12.13210.1016/j.ijhydene.2017.12.132 ↗
3. Non‐crystallising glass sealants for SOFC: Effect of Y2O3 addition
4. 10.1007/s11666-020-01096-510.1007/s11666-020-01096-5 ↗
5. 10.1016/j.ceramint.2021.02.04610.1016/j.ceramint.2021.02.046 ↗
6. 10.1016/j.ijhydene.2020.12.05910.1016/j.ijhydene.2020.12.059 ↗
7. 10.1016/j.jeurceramsoc.2021.03.03010.1016/j.jeurceramsoc.2021.03.030 ↗
8. 10.1016/j.ceramint.2019.01.22710.1016/j.ceramint.2019.01.227 ↗
9. Microstructural evolution of Si3N4/Ti6Al4V joints brazed with nano‐Si3N4 reinforced AgCuTi composite filler
10. 10.1016/j.msea.2015.12.00910.1016/j.msea.2015.12.009 ↗
11. 10.1016/j.ijhydene.2014.11.02810.1016/j.ijhydene.2014.11.028 ↗
12. 10.1016/j.msea.2007.08.03210.1016/j.msea.2007.08.032 ↗
13. 10.1016/j.jeurceramsoc.2019.03.01310.1016/j.jeurceramsoc.2019.03.013 ↗
14. 10.1016/j.ijhydene.2012.05.13010.1016/j.ijhydene.2012.05.130 ↗
15. Glass–ceramic sealant for solid oxide fuel cells application: Characterization and performance in dual atmosphere
16. 10.1016/j.ijhydene.2016.02.12010.1016/j.ijhydene.2016.02.120 ↗
17. 10.1016/j.jpowsour.2008.06.02010.1016/j.jpowsour.2008.06.020 ↗
18. 10.1016/j.ijhydene.2011.03.03610.1016/j.ijhydene.2011.03.036 ↗
19. 10.1016/j.jeurceramsoc.2007.05.00610.1016/j.jeurceramsoc.2007.05.006 ↗
20. 10.1016/j.ijhydene.2011.04.08310.1016/j.ijhydene.2011.04.083 ↗
21. 10.1557/jmr.2006.017810.1557/jmr.2006.0178 ↗
22. 10.1016/j.ijhydene.2006.08.05410.1016/j.ijhydene.2006.08.054 ↗
23. 10.1016/j.ijhydene.2010.06.06310.1016/j.ijhydene.2010.06.063 ↗
24. 10.1111/j.1551-2916.2012.05094.x10.1111/j.1551-2916.2012.05094.x ↗
25. 10.1016/j.actamat.2015.01.02910.1016/j.actamat.2015.01.029 ↗
26. 10.1111/j.1551-2916.2005.00492.x10.1111/j.1551-2916.2005.00492.x ↗
27. 10.1016/j.jallcom.2010.01.13110.1016/j.jallcom.2010.01.131 ↗
28. 10.1002/fuce.20140019210.1002/fuce.201400192 ↗
29. 10.1016/j.ijhydene.2013.10.04210.1016/j.ijhydene.2013.10.042 ↗
30. 10.1016/j.jpowsour.2006.08.01310.1016/j.jpowsour.2006.08.013 ↗
31. Effect of coating density on oxidation resistance and Cr vaporization from solid oxide fuel cell interconnects
32. ChoiJ‐P ChouYS StevensonJW.Reactive air aluminization.2011. PNNL‐20859.10.2172/1029868 ↗
33. The role of Al diffusion behavior in the process of forming a super‐reliable Al2O3 protective layer during reactive air aluminization
34. 10.1016/j.ijhydene.2017.01.10510.1016/j.ijhydene.2017.01.105 ↗
35. 10.1016/j.jeurceramsoc.2020.10.00810.1016/j.jeurceramsoc.2020.10.008 ↗
36. 10.1016/j.matdes.2016.10.06210.1016/j.matdes.2016.10.062 ↗
37. 10.1016/j.ceramint.2019.10.26210.1016/j.ceramint.2019.10.262 ↗
38. Evidence of a high‐temperature wetting transition between Ag–CuO liquid alloys and yttria‐stabilized zirconia substrates
39. 10.1111/j.1151-2916.1998.tb02604.x10.1111/j.1151-2916.1998.tb02604.x ↗
40. Development of a copper oxide–silver braze for ceramic joining10.1002/9781118405802.ch6 ↗
41. Wetting and mechanical characteristics of the reactive air braze for yttria‐stabilized zirconia (YSZ) joining10.1002/9781118407141.ch11 ↗
42. 10.1007/s12540-017-7160-410.1007/s12540-017-7160-4 ↗
43. 10.1111/j.1151-2916.1993.tb03996.x10.1111/j.1151-2916.1993.tb03996.x ↗