Role of CeAl 11 O 18 in reinforcing Al 2 O 3 /Ti composites by adding CeO 2
Source abstract
Abstract
Abstract This work discusses the reinforcement effect of elongated CeAl 11 O 18 phase on multifunctional Al 2 O 3 /Ti composites by adding CeO 2 to inhibit interfacial reaction and strengthen interface for inducing optimized performances. For this purpose, Al 2 O 3 /Ti composite with different contents of CeO 2 was fabricated and the microstructure, mechanical and electrical properties were studied. Results indicated that after CeO 2 was added, elongated CeAl 11 O 18 phase was formed within these composites. Owing to inhibited interfacial reaction between Al 2 O 3 and Ti, Ti content was increased and compositions of composites were calculated using Rietveld method based on X‐ray diffraction patterns. Attributed to the strengthening and toughening effects of CeAl 11 O 18 phase, 2 mol% CeO 2 added composite showed the highest flexural strength and fracture toughness of 576 MPa and 5.15 MPa·m 1/2 , which increased by 21% and 20% compared to Al 2 O 3 /Ti composite without CeO 2 addition. In this case, crack bridging by both Ti and CeAl 11 O 18 particles was the major toughening mechanism and the additional fracture toughness caused by CeAl 11 O 18 toughening effect reached a maximum. The role (crack bridging or particle pull‐out mechanism) of CeAl 11 O 18 in toughening Al 2 O 3 /Ti composites depended on the aspect ratio of these elongated particles, which was directly related to CeO 2 content. Because of the inhibition of interfacial reaction and the increase in Ti content, excellent electrical resistivity of composites after CeO 2 addition was maintained in spite of the formation of insulated CeAl 11 O 18 phase. All samples showed relatively low electrical resistivity of ~10 −3 Ωcm.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Aluminum Alloys Composites Properties · Advanced materials and composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
The Institute of Scientific and Industrial Research Osaka University Osaka Ibaraki Japan
Funding
Japan Society for the Promotion of Science
References (42)
Show source-provided references
1. 10.1111/ijac.1256910.1111/ijac.12569 ↗
2. 10.1016/0965-9773(95)00145-X10.1016/0965-9773(95)00145-X ↗
3. 10.1016/S0925-8388(02)01120-910.1016/S0925-8388(02)01120-9 ↗
4. 10.1016/j.scriptamat.2008.09.03410.1016/j.scriptamat.2008.09.034 ↗
5. 10.4028/www.scientific.net/MSF.710.29110.4028/www.scientific.net/MSF.710.291 ↗
6. 10.1016/j.surfcoat.2008.03.00110.1016/j.surfcoat.2008.03.001 ↗
7. 10.1016/j.apcata.2010.11.01310.1016/j.apcata.2010.11.013 ↗
8. 10.1016/j.scriptamat.2010.12.04210.1016/j.scriptamat.2010.12.042 ↗
9. 10.1016/j.jallcom.2007.05.04310.1016/j.jallcom.2007.05.043 ↗
10. 10.1111/j.1151-2916.1997.tb02956.x10.1111/j.1151-2916.1997.tb02956.x ↗
11. 10.1016/j.pmatsci.2006.09.00310.1016/j.pmatsci.2006.09.003 ↗
12. 10.1016/j.ceramint.2015.07.04410.1016/j.ceramint.2015.07.044 ↗
13. 10.1007/BF0117841710.1007/BF01178417 ↗
14. 10.1016/j.jeurceramsoc.2014.06.02310.1016/j.jeurceramsoc.2014.06.023 ↗
15. 10.1111/j.1151-2916.1996.tb08561.x10.1111/j.1151-2916.1996.tb08561.x ↗
16. 10.1016/j.jcrysgro.2008.09.05210.1016/j.jcrysgro.2008.09.052 ↗
17. 10.1111/jace.1547210.1111/jace.15472 ↗
18. 10.2109/jcersj2.1811910.2109/jcersj2.18119 ↗
19. 10.1111/jace.1626410.1111/jace.16264 ↗
20. 10.1016/j.msea.2014.11.05810.1016/j.msea.2014.11.058 ↗
21. Impact of grain boundary character on grain rotation
22. 10.1016/j.ceramint.2018.07.05410.1016/j.ceramint.2018.07.054 ↗
23. 10.1016/j.jallcom.2015.06.09310.1016/j.jallcom.2015.06.093 ↗
24. 10.1016/j.ceramint.2011.05.12310.1016/j.ceramint.2011.05.123 ↗
25. 10.1016/j.jallcom.2014.08.00710.1016/j.jallcom.2014.08.007 ↗
26. 10.1016/S0272-8842(98)00033-910.1016/S0272-8842(98)00033-9 ↗
27. 10.1016/j.jallcom.2015.10.04310.1016/j.jallcom.2015.10.043 ↗
28. 10.1016/j.jallcom.2020.15542710.1016/j.jallcom.2020.155427 ↗
29. 10.1007/BF0072562510.1007/BF00725625 ↗
30. 10.4028/www.scientific.net/KEM.115.110.4028/www.scientific.net/KEM.115.1 ↗
31. 10.1111/j.1151-2916.1969.tb09195.x10.1111/j.1151-2916.1969.tb09195.x ↗
32. 10.1111/j.1744-7402.2012.02828.x10.1111/j.1744-7402.2012.02828.x ↗
33. 10.1016/S0955-2219(01)00528-310.1016/S0955-2219(01)00528-3 ↗
34. 10.1016/S0272-8842(02)00225-010.1016/S0272-8842(02)00225-0 ↗
35. 10.1016/S0040-6090(99)00352-110.1016/S0040-6090(99)00352-1 ↗
36. 10.1016/S0926-860X(02)00233-810.1016/S0926-860X(02)00233-8 ↗
37. Thermodynamic assessment and microstructure of the ZrO2‐CeO2‐A12O3 system
38. 10.1063/1.482525610.1063/1.4825256 ↗
39. 10.12693/APhysPolA.127.113310.12693/APhysPolA.127.1133 ↗
40. Courtney TH · 2005 · 283
41. Harris B · 2004 · 141
42. 10.1016/S1359-6462(98)00147-X10.1016/S1359-6462(98)00147-X ↗