High‐Temperature Shear Strength and Bonding Mechanism of the Mullite Ceramic/Fiber Brick Component Joined by Phosphate Adhesive
Source abstract
Abstract
The mullite ceramic/fiber brick system was bonded by two kinds of phosphate adhesives. The specimens were treated from 200 to 1400°C. The mechanical properties were tested at room temperature and at high temperature, and the relevant bonding mechanism was also discussed. The results show that the addition of silicon can greatly improve the adhesive's mechanical properties. The room‐temperature shear strength of the component bonded by adhesive with the silicon calcined at 800°C can reach 6.58 MPa. The shear strength of the adhesive with silicon tested at 800°C can reach 0.42 MPa.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Advanced ceramic materials synthesis · MXene and MAX Phase Materials · Microwave Dielectric Ceramics Synthesis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Materials Science and Engineering, Key Lab of Advanced Ceramics and Machining Technology of Ministry of Education Tianjin University Tianjin 300072 People's Republic of China
References (20)
Show source-provided references
1. 10.1016/j.jeurceramsoc.2007.03.01710.1016/j.jeurceramsoc.2007.03.017 ↗
2. 10.1016/j.scriptamat.2010.03.00710.1016/j.scriptamat.2010.03.007 ↗
3. 10.1016/j.ijadhadh.2005.01.00510.1016/j.ijadhadh.2005.01.005 ↗
4. 10.1007/s10971-009-2106-z10.1007/s10971-009-2106-z ↗
5. 10.1016/S0921-5093(01)01367-310.1016/S0921-5093(01)01367-3 ↗
6. 10.1016/j.ceramint.2007.11.00710.1016/j.ceramint.2007.11.007 ↗
7. 10.1016/j.jpowsour.2008.10.11710.1016/j.jpowsour.2008.10.117 ↗
8. 10.1016/j.scriptamat.2009.03.05310.1016/j.scriptamat.2009.03.053 ↗
9. 10.1023/A:102108763215510.1023/A:1021087632155 ↗
10. 10.1016/j.ijadhadh.2005.01.00610.1016/j.ijadhadh.2005.01.006 ↗
11. 10.1007/s10853-005-3311-y10.1007/s10853-005-3311-y ↗
12. Shear and Bending Strength of SiC/SiC Joined by a Modified Commercial Adhesive
13. 10.1016/S0022-3115(98)00176-710.1016/S0022-3115(98)00176-7 ↗
14. 10.1007/s10853-010-4647-510.1007/s10853-010-4647-5 ↗
15. 10.1016/S0022-3115(99)00268-810.1016/S0022-3115(99)00268-8 ↗
16. 10.1016/j.ijadhadh.2011.03.00610.1016/j.ijadhadh.2011.03.006 ↗
17. 10.1016/j.surfcoat.2012.02.03110.1016/j.surfcoat.2012.02.031 ↗
18. 10.1016/j.dental.2012.01.00810.1016/j.dental.2012.01.008 ↗
19. 10.1016/j.msea.2011.11.07910.1016/j.msea.2011.11.079 ↗
20. 10.1016/j.tox.2006.07.01410.1016/j.tox.2006.07.014 ↗