Promoting spinel formation and growth for preparation of refractory materials from ferronickel slag
Source abstract
Abstract
Abstract The study provides a method for improving the quality of the refractory material prepared from ferronickel slag by promoting the spinel formation and growth in the slag which was sintered with sintered magnesia and chromium oxide in a broad sintering temperature range from 1200°C to 1500°C. According to the thermodynamic analysis, except for forsterite due to the addition of sintered magnesia, a number of high‐melting point spinel phases can also be formed in the presence of chromium oxide and this trend becomes more apparent with increasing sintering temperature, along with declined presence of low‐melting point clinopyroxene, mainly enstatite. This expectation was verified by conversion of a part of the original phase of ferronickel slag, olivine, to two main spinel phases, including magnesium aluminate spinel and donathite which was produced by the replacement of nontoxic Cr 3+ ions with Fe 3+ ions in the octahedral vacancies of magnesium chromate spinel. The formation and growth of these spinel phases were promoted by elevating temperature from 1200°C to 1500°C, which accelerated the transition of initially generated enstatite to a glassy phase, in favor of densification. The formation and growth of spinel during sintering contributed to high refractoriness and compressive strength of the resulting refractory materials
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Recycling and utilization of industrial and municipal waste in materials production · Microwave Dielectric Ceramics Synthesis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Minerals Processing and Bioengineering Central South University Changsha Hunan China
Guangdong Guangqing Metal Technology Co. Ltd. Yangjiang Guangdong China
Department of Materials Science and Engineering Korea University Seoul South Korea
References (45)
Show source-provided references
1. 10.1016/j.ceramint.2018.05.04910.1016/j.ceramint.2018.05.049 ↗
2. Outlook of China ferroalloy industry development trend for “the 12th five‐year”
3. Yu J · 2017 · 1
4. 10.1007/s11837-018-3250-010.1007/s11837-018-3250-0 ↗
5. 10.1016/j.conbuildmat.2017.09.03810.1016/j.conbuildmat.2017.09.038 ↗
6. 10.1021/acs.iecr.8b0049910.1021/acs.iecr.8b00499 ↗
7. 10.1016/j.resconrec.2018.02.03410.1016/j.resconrec.2018.02.034 ↗
8. 10.1016/j.powtec.2017.08.04110.1016/j.powtec.2017.08.041 ↗
9. 10.1016/j.jhazmat.2019.04.00210.1016/j.jhazmat.2019.04.002 ↗
10. 10.1016/j.conbuildmat.2018.12.06810.1016/j.conbuildmat.2018.12.068 ↗
11. 10.1016/j.conbuildmat.2017.02.02310.1016/j.conbuildmat.2017.02.023 ↗
12. 10.1016/j.conbuildmat.2018.08.18210.1016/j.conbuildmat.2018.08.182 ↗
13. 10.1016/j.conbuildmat.2015.09.03910.1016/j.conbuildmat.2015.09.039 ↗
14. 10.1007/s10853-006-0529-210.1007/s10853-006-0529-2 ↗
15. 10.1016/j.matlet.2018.04.03610.1016/j.matlet.2018.04.036 ↗
16. 10.1016/j.ceramint.2015.05.09810.1016/j.ceramint.2015.05.098 ↗
17. 10.1016/j.seppur.2015.10.05110.1016/j.seppur.2015.10.051 ↗
18. 10.1016/j.jhazmat.2007.07.05210.1016/j.jhazmat.2007.07.052 ↗
19. 10.1016/j.jhazmat.2018.06.06110.1016/j.jhazmat.2018.06.061 ↗
20. 10.1080/08827508.2016.118163010.1080/08827508.2016.1181630 ↗
21. 10.1021/acssuschemeng.8b0188210.1021/acssuschemeng.8b01882 ↗
22. https://www.china.cn/subject/sanyanghuage.htmlAccessed November 4 2019.
23. 10.1007/s12613-013-0720-910.1007/s12613-013-0720-9 ↗
24. 10.1021/acs.iecr.5b0344210.1021/acs.iecr.5b03442 ↗
25. 10.1016/j.cej.2018.06.07210.1016/j.cej.2018.06.072 ↗
26. 10.1111/ijac.1270110.1111/ijac.12701 ↗
27. Effects of Cr2O3 addition on property improvement of magnesia‐spinel refractories used in RH snorkel10.1016/j.ceramint.2016.08.200 ↗
28. 10.1016/j.jeurceramsoc.2016.07.00110.1016/j.jeurceramsoc.2016.07.001 ↗
29. 10.1111/ijac.1302610.1111/ijac.13026 ↗
30. 10.1016/j.ceramint.2018.07.05210.1016/j.ceramint.2018.07.052 ↗
31. 10.1016/j.jeurceramsoc.2016.02.03610.1016/j.jeurceramsoc.2016.02.036 ↗
32. 10.1016/j.jeurceramsoc.2016.02.00410.1016/j.jeurceramsoc.2016.02.004 ↗
33. 10.1016/j.engfailanal.2014.09.00310.1016/j.engfailanal.2014.09.003 ↗
34. 10.1021/acssuschemeng.7b0433610.1021/acssuschemeng.7b04336 ↗
35. 10.1007/978-3-319-72484-3_6710.1007/978-3-319-72484-3_67 ↗
36. 10.1111/ijac.1275910.1111/ijac.12759 ↗
37. 10.1016/j.powtec.2017.03.01210.1016/j.powtec.2017.03.012 ↗
38. Xue Q · 2013
39. 10.1002/cite.20130018510.1002/cite.201300185 ↗
40. Gao Z · 2002
41. 10.1007/s10853-017-1617-110.1007/s10853-017-1617-1 ↗
42. 10.1016/j.matchar.2014.11.02010.1016/j.matchar.2014.11.020 ↗
43. 10.1007/s10853-017-1761-710.1007/s10853-017-1761-7 ↗
44. National Refractory Standardization Technical Committee of China · 2002
45. http://www.nhclsq.com/cpsb.php?zycp=%C3%BE%D7%A9Accessed November 4 2019.