Spalling degradation of Cr 2 O 3 ‐Al 2 O 3 ‐ZrO 2 refractories for coal‐water slurry gasifier linings: Role of phosphate
Source abstract
Abstract
Abstract Two kinds of high chromia bricks with and without phosphate as gasifier linings were postmortem analyzed during their whole service life. The effect of phosphate on the microstructure and phase composition of refractory sections was analyzed. The dense phosphate enrichment layer was observed between the slag penetration layer and the virgin layer, which was considered to reduce the damage of gasifier lining caused by spalling. Phosphate could decompose and migrate slowly under suitable temperature gradient existing in the bricks in service, which would result in the densification of the microstructure earlier than slag penetration. The phosphate in high chromia bricks reduced frequency of spalling due to penetration, which would lead to the lower early wear rate and longer lifetime.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Metallurgical Processes and Thermodynamics · Advanced materials and composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Materials Science and Engineering University of Science and Technology Beijing Beijing China
State Key Laboratory of Advanced Refractories Sinosteel Luoyang Institute of Refractories Research Co., Ltd. Luoyang China
Sinosteel Luonai Materials Technology Corporation Luoyang China
References (29)
Show source-provided references
1. 10.1016/B978-0-12-373611-6.00011-210.1016/B978-0-12-373611-6.00011-2 ↗
2. 10.1016/j.ceramint.2007.08.01110.1016/j.ceramint.2007.08.011 ↗
3. 10.1016/j.egypro.2017.12.36110.1016/j.egypro.2017.12.361 ↗
4. KwongK BennettJ NakanoJ.Gasifier refractories coal slags and their interaction. In:the Ninth International Conference on Molten Slags Fluxes and Salts (MOLTEN 2012) Beijing China May 27–30 2012: 403–417
5. 10.1016/S0272-8842(96)00059-410.1016/S0272-8842(96)00059-4 ↗
6. 10.1016/j.ceramint.2017.11.02310.1016/j.ceramint.2017.11.023 ↗
7. 10.1016/j.corsci.2019.10825010.1016/j.corsci.2019.108250 ↗
8. 10.1016/j.ijheatmasstransfer.2020.12085210.1016/j.ijheatmasstransfer.2020.120852 ↗
9. 10.1016/j.corsci.2018.03.03910.1016/j.corsci.2018.03.039 ↗
10. SunH LiH LiP ZhaoS.Research on slag resistance of Al2O3‐Cr2O3refractories under temperature flucation condition. In:The Unified International Technical Conference on Refractories (UNITECR 2017) Santiago Chile Sep. 26~29 2017: 630–633.
11. Thermodynamic evaluation of Cr2O3‐Al2O3 refractory corrosion by smelting reduction ironmaking slag
12. Refractories for gasifecation
13. Engineered refractories for slagging gasifiers
14. 10.1111/jace.1700110.1111/jace.17001 ↗
15. 10.1016/j.ces.2019.11522710.1016/j.ces.2019.115227 ↗
16. 10.1007/s11661-011-0635-x10.1007/s11661-011-0635-x ↗
17. 10.1016/j.ceramint.2021.09.20510.1016/j.ceramint.2021.09.205 ↗
18. 10.1016/j.ceramint.2021.07.24210.1016/j.ceramint.2021.07.242 ↗
19. 10.1016/j.ceramint.2013.08.02310.1016/j.ceramint.2013.08.023 ↗
20. Bennett JP, · 2004 · 783
21. Effects of firing and operating atmospheres on microstructure and properties of phosphate bonded Cr2O3‐Al2O3‐ZrO2 bricks
22. KwongKS DoganCP BennettJP ChinnRE PettyAV.Use of phosphates to reduce slag penetration in Cr2O3‐based refractories. US Patent 6815386B1 2004.
23. J Bennett A Nakano J Nakano H Thomas
24. JP Bennett BW Riggs KS Kwong J Nakano
25. Field test results and postmortem analyses of high chrome refractories with phosphate additions in coal‐water slurry gasifier
26. 10.4028/www.scientific.net/AST.92.24810.4028/www.scientific.net/AST.92.248 ↗
27. 10.1016/j.surfcoat.2006.08.06310.1016/j.surfcoat.2006.08.063 ↗
28. BennettJ NakanoA NakanoJ ThomasH. Aluminum phosphate phase changes caused by the exposure environment. In: Proceedings of the Unified International Technical Conference on Refractories (UNITECR 2019); October 13–16 2019;Yokohamo Japan.
29. 10.1111/j.1151-2916.1956.tb15630.x10.1111/j.1151-2916.1956.tb15630.x ↗