Evaluation of electrodeposited Mn‐Co protective coatings on Crofer 22 APU steel
Source abstract
Abstract
Abstract Interconnects used in Solid Oxide Cells stacks require protective coatings to lower their parabolic rate constant and block chromium evaporation (on the air side). In this work four different protective coatings on steel are evaluated for their high temperature corrosion resistance and electrical conductivity. A commercial electroplating process was used for the preparation of coatings with different Mn/Co ratios on Crofer 22 APU steel. Oxidation of samples was performed in air at 800°C for 1000 hours. Postmortem analysis of the coated samples was performed by scanning electron microscopy and x‐ray diffractomettry. Based on the results, influence of the Co/Mn ratio on the resulting corrosion properties are discussed. Parabolic rate constant of the coated samples is the lowest for the MnCo sample, whereas electrical resistance is the lowest for the Co sample, which has a corrosion rate similar to the not‐coated alloys.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Advancements in Solid Oxide Fuel Cells · Metal and Thin Film Mechanics · Hydrogen embrittlement and corrosion behaviors in metals
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Energy Conversion and Storage Technical University of Denmark Roskilde Denmark
References (47)
Show source-provided references
1. 10.1016/j.jpowsour.2005.02.08410.1016/j.jpowsour.2005.02.084 ↗
2. 10.1016/S0167-2738(01)00863-310.1016/S0167-2738(01)00863-3 ↗
3. 10.1111/j.1744-7402.2004.tb00151.x10.1111/j.1744-7402.2004.tb00151.x ↗
4. 10.1111/j.1744-7402.2010.02564.x10.1111/j.1744-7402.2010.02564.x ↗
5. 10.1111/j.1744-7402.2012.02753.x10.1111/j.1744-7402.2012.02753.x ↗
6. 10.1016/S0921-5093(02)00736-010.1016/S0921-5093(02)00736-0 ↗
7. 10.1016/j.msea.2005.02.04710.1016/j.msea.2005.02.047 ↗
8. 10.1016/j.jpowsour.2007.06.25510.1016/j.jpowsour.2007.06.255 ↗
9. 10.1590/S1516-1439200400010002710.1590/S1516-14392004000100027 ↗
10. 10.1149/1.159565910.1149/1.1595659 ↗
11. 10.1016/j.corsci.2010.06.00610.1016/j.corsci.2010.06.006 ↗
12. 10.1007/s10008-008-0635-y10.1007/s10008-008-0635-y ↗
13. 10.1016/j.jpowsour.2009.09.06910.1016/j.jpowsour.2009.09.069 ↗
14. 10.1016/j.ijhydene.2012.07.03810.1016/j.ijhydene.2012.07.038 ↗
15. 10.1016/j.jpowsour.2013.09.10010.1016/j.jpowsour.2013.09.100 ↗
16. Mn‐Co spinel protective‐conductive coating on AL453 ferritic stainless steel for IT‐SOFC interconnect applications10.1007/s10008-012-1952-8 ↗
17. 10.1016/j.jpowsour.2017.04.02310.1016/j.jpowsour.2017.04.023 ↗
18. 10.1149/1.139389110.1149/1.1393891 ↗
19. 10.1149/1.185412210.1149/1.1854122 ↗
20. 10.1016/j.matlet.2012.12.07910.1016/j.matlet.2012.12.079 ↗
21. 10.1016/j.jpowsour.2016.11.01110.1016/j.jpowsour.2016.11.011 ↗
22. 10.1016/j.tsf.2015.07.02310.1016/j.tsf.2015.07.023 ↗
23. 10.1016/j.ceramint.2014.05.10610.1016/j.ceramint.2014.05.106 ↗
24. 10.1111/jace.1225410.1111/jace.12254 ↗
25. 10.1016/j.ijhydene.2006.08.04810.1016/j.ijhydene.2006.08.048 ↗
26. 10.1111/j.1551-2916.2011.04749.x10.1111/j.1551-2916.2011.04749.x ↗
27. Electrical properties of transition metal‐doped (Mn, Co)3O4 spinels and their interaction with chromia for SOFC interconnect coatings10.1149/1.3701333 ↗
28. 10.3390/cryst707018510.3390/cryst7070185 ↗
29. 10.1016/j.jpowsour.2016.09.13610.1016/j.jpowsour.2016.09.136 ↗
30. 10.1016/j.jpowsour.2012.07.09110.1016/j.jpowsour.2012.07.091 ↗
31. 10.1016/j.matlet.2012.04.07210.1016/j.matlet.2012.04.072 ↗
32. 10.1088/1757-899X/104/1/01201710.1088/1757-899X/104/1/012017 ↗
33. 10.1016/j.jpowsour.2007.11.07510.1016/j.jpowsour.2007.11.075 ↗
34. 10.1111/ijac.1262110.1111/ijac.12621 ↗
35. 10.1111/ijac.1267510.1111/ijac.12675 ↗
36. 10.1111/ijac.1201310.1111/ijac.12013 ↗
37. 10.1111/j.1744-7402.2012.02789.x10.1111/j.1744-7402.2012.02789.x ↗
38. 10.1111/j.1744-7402.2010.02600.x10.1111/j.1744-7402.2010.02600.x ↗
39. 10.1111/j.1744-7402.2009.02430.x10.1111/j.1744-7402.2009.02430.x ↗
40. 10.1016/S1005-0302(10)60049-710.1016/S1005-0302(10)60049-7 ↗
41. 10.1016/j.electacta.2008.06.05710.1016/j.electacta.2008.06.057 ↗
42. 10.1016/j.jpowsour.2008.12.07910.1016/j.jpowsour.2008.12.079 ↗
43. WeiP.Spinel coatings for Solid Oxide Fuel Cell interconnects and crystal structure of Cu‐Mn‐O. PhD thesis.Canada:McMaster University;2009.
44. High temperature oxidation of ferritic steels for solid oxide electrolysis stacks10.1149/05030.0011ecst ↗
45. 10.1007/978-0-387-68815-2_1210.1007/978-0-387-68815-2_12 ↗
46. Long term (4 years) performance of Co/Ce Coated 441 for SOFC interconnect applications10.1149/07801.1675ecst ↗
47. 10.1016/j.jallcom.2011.12.09510.1016/j.jallcom.2011.12.095 ↗