Effect of silane treatment on adhesion of adhesive-bonded carbon fiber reinforced nylon 6 composite
Source abstract
Abstract
Abstract In this study, a silane coating, KH560, along with an abrasion pretreatment procedure for carbon fiber reinforced PA 6 composite with 30% mass fiber (Cf/PA6) and AA6061-T4 was developed. Composition and structure of this silane coating and effect of this coating on the strength and water resistance of the adhesive-bonded Cf/PA6 and AA6061 were investigated. Test results revealed that silane pretreatment improved the static strengths of the adhesive-bonded Cf/PA6-Cf/PA6 and Cf/PA6-AA6061 by 23% and 21%, respectively. X-ray photoelectron spectroscopy (XPS) analysis of the adhesive-bonded treated Cf/PA6 indicated that the improvement in strength was primarily attributed to the formation of Si-O-Si and Si-N covalent bonds on the surface of Cf/PA6, which enhanced the bond adhesion between the silane coating, adhesive, and adherends. In addition, abrasion of adherends prior to silane pretreatment further improved the strengths of the adhesive-bonded Cf/PA6-Cf/PA6 by another 20%. While silane and abrasion-silane treatment improved the strength of the adhesive-bonded Cf/PA6-Cf/PA6 and Cf/PA6-AA6061 in ambient conditions, the strength of water immersed silane coated joints with and without abrasion was decreased by about 50% (i.e., immersed in water at 54 °C for one week). All tested bare and treated joints with and without water immersion exposure were fractured in adhesive mode. Analyses of the test results revealed that to improve the failure mode and bond strength it is necessary to form a Si-N functional group in the silane coating by thoroughly cleaning and removing the contaminants and weak layers on the surface of Cf/PA6.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Mechanical Behavior of Composites · Fiber-reinforced polymer composites · Advanced ceramic materials synthesis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (57)
Show source-provided references
1. Alternative lightweight materials and component manufacturing technologies for vehicle frontal bumper beam [J]10.1016/j.compstruct.2014.10.007 ↗
2. Recent development in aluminum alloys for the automotive industry10.1016/S0921-5093(99)00653-X ↗
3. Experimental estimation of the mechanical and fracture properties of a new epoxy adhesive [J]10.1186/s40563-015-0056-y ↗
4. Adhesion of polymers [J]10.1016/j.progpolymsci.2009.04.007 ↗
5. Thermoplastic-epoxy interactions and their potential applications in joining composite structures - a review [J]10.1016/j.compositesa.2014.09.027 ↗
6. Testing of adhesives for bonding of polymer composites [J]10.1016/S0143-7496(02)00006-4 ↗
7. Adhesively-bonded joints and repairs in metallic alloys, polymers and composite materials: adhesives, adhesion theories and surface pretreatment [J]10.1023/B:JMSC.0000007726.58758.e4 ↗
8. Adhesively bonded joints in composite materials: an overview [J]
9. Principles and practice of adhesive bonded structural joints and repairs [J]10.1016/S0143-7496(98)00026-8 ↗
10. Review of surface pretreatments for aluminum alloys [J]10.1016/0143-7496(95)91627-I ↗
11. Influence of the polymer surface layer on the adhesion of polymer matrix composites [J]10.1177/0892705708091606 ↗
12. Correlating thermodynamic and mechanical adhesion phenomena for thermoplastic polyolefins [J]10.1007/s11998-007-9017-0 ↗
13. Contact angles and adhesive bonding [J]10.1016/0143-7496(92)90045-W ↗
14. Adhesion phenomena in bonded joints [J]10.1016/j.ijadhadh.2012.04.007 ↗
15. Effect of various surface treatment on repair strength of composite resin [J]
16. Adhesion bonding techniques for highly loaded parts of continuous carbon-fiber reinforced polyetherketone (CF-PEEK/APC02)
17. Effect of different surface pre-treatments and luting materials on shear bond strength to PEEK [J]10.1016/j.dental.2010.02.003 ↗
18. The peel ply surface treatment for adhesive bonding of composites: a review [J]10.1016/j.ijadhadh.2013.01.014 ↗
19. A review of electrochemical pretreatments of polymers [J]10.1016/S0143-7496(01)00017-3 ↗
20. Effect of plasma surface pretreatment on Ce3+-doped gptms-ZrO2 self-healing coatings on aluminum alloy [J]10.5402/2012/506560 ↗
21. Surface modification of polymer fiber by the new atmospheric pressure cold plasma jet [10.1016/j.surfcoat.2005.09.033 ↗
22. Activated gas plasma surface treatment of polymers for adhesive bonding [J]10.1002/app.1969.070131006 ↗
23. Plasma surface modification of glass fiber-reinforced nylon-6, 6 thermoplastic composites for improved adhesive bonding [J]10.1023/A:1008779728985 ↗
24. Short-time plasma pre-treatment of polytetrafluoroethylene for improved adhesion [J]10.1016/S0257-8972(01)01209-9 ↗
25. Adhesive bonding and wettability of plasma treated, glass fiber-reinforced nylon-6, 6 composites [J]10.1023/A:1006706826209 ↗
26. Flame treatment of polypropylene: a study by electron and ion spectroscopies [J]10.1016/j.ijadhadh.2015.07.009 ↗
27. Laser surface modification of poly(etheretherketone) to enhance surface free energy, wettability and adhesion [J]10.1016/j.ijadhadh.2015.06.005 ↗
28. Laser ablation surface preparation for adhesive bonding of carbon fiber reinforced epoxy composites [J]10.1016/j.ijadhadh.2016.02.007 ↗
29. Effect of bifunctional organosilane on the joint strength of some natural rubber compounds to nylon 6,6[J]10.1016/S0143-7496(03)00010-1 ↗
30. Principles and practices of adhesive bonded structural joints and repairs [J]10.1016/S0143-7496(98)00026-8 ↗
31. Adhesion improvement between epoxy and stainless steel using a silane coupling agent in an atmospheric plasma process [10.1002/ppap.201400106 ↗
32. Effect of silane-based treatment on the adhesion strength of acrylic lacquers on the PP surfaces [J]10.1016/j.ijadhadh.2006.09.012 ↗
33. A novel silane system as a primer for orthodontic bonding—a pilot study [J]10.1016/j.ijadhadh.2015.07.006 ↗
34. Kohan · 1995
35. Polyamide 6 surface layer following ozone treatment [J]10.1016/j.ijadhadh.2015.10.017 ↗
36. Thermoplastic-epoxy interactions and their potential applications in joining composite structures - a review [J]10.1016/j.compositesa.2014.09.027 ↗
37. Moisture sorption in polyamide 6.6: experimental investigation and comparison to four physical-based models [J]10.1016/j.polymertesting.2015.02.004 ↗
38. Lowering curing temperature in adhesive bonding of aluminum AA6061-T410.1080/00218464.2017.1377077 ↗
39. Development of two-component structural adhesive for bonding of metal and polymeric composite10.1016/j.ijadhadh.2019.01.018 ↗
40. Review Adhesively-bonded joints in metallic alloys, polymers and composite materials: mechanical and environmental durability performance [J]10.1023/B:JMSC.0000035317.87118.ab ↗
41. Improvement of adhesive bonding in aluminum alloys using a laser surface texturing process [J]10.1016/S0924-0136(96)02687-8 ↗
42. Corrosion protection behavior of AZ31 magnesium alloy with cathodic electrophoretic coating pretreated by silane [J]10.1016/j.porgcoat.2009.09.001 ↗
43. Effects of phosphate pretreatment and hot-humid environmental exposure on static strength of adhesive-bonded magnesium AZ31 sheets [J]10.1016/j.surfcoat.2012.02.031 ↗
44. A new phosphate pretreatment process for adhesive bonding of magnesium AZ31 sheets [J]10.1007/s11998-012-9451-5 ↗
45. Effect of surface pretreatment on corrosion resistance and bond strength of magnesium AZ31 alloy [J]10.1016/j.corsci.2012.08.051 ↗
46. Effect of Na2MoO4 on bond strength of adhesive-bonded phosphate coated magnesium AZ31 sheets [J]10.1016/j.ijadhadh.2012.07.011 ↗
47. Effect of phosphate-silane pretreatment on the corrosion resistance and adhesive-bonded performance of the AZ31 magnesium alloys [J]10.1016/j.porgcoat.2013.01.010 ↗
48. Petrie · 2006
49. Adhesion performance of an epoxy clear coat on aluminum alloy in the presence of vinyl and amino-silane primers [J]10.1016/j.porgcoat.2006.09.007 ↗
50. Wettability of silicone and polyether impression materials: characterization by surface tension and contact angle measurements10.1016/j.colsurfa.2007.11.046 ↗
51. The interaction of a commercial dry film adhesive with aluminum and organosilane treated aluminum surfaces: a study by XPS and ToF-SIMS [J]10.1016/S0143-7496(01)00056-2 ↗
52. Jill Chastain · 1992
53. Sadek · 1987
54. Norbert Seyr, Andreas Obieglo, Marc Erdmann, Jochen Holzleitner, an overview of the polymer-to-metal direct-adhesion hybrid technologies for load-bearing automotive components [J]10.1016/j.jmatprotec.2007.06.058 ↗
55. The role of water in polyamides [J]10.1007/BF01746685 ↗
56. The development of a low temperature cure modified epoxy resin system for aerospace composites10.1016/S1359-835X(02)00115-X ↗
57. Effect of moisture on the ultrasonic welding of carbon fiber reinforced Nylon 66 composite [J]