Ultrasonic fatigue of laser beam powder bed fused metals: A state-of-the-art review
Bibliographic record
Abstract
No abstract is available for this record. The assistant can identify its topic from the title, but cannot infer the study’s results.
Source: Not provided · Quality: missing
Research context
OpenAlex topics: Additive Manufacturing Materials and Processes · Additive Manufacturing and 3D Printing Technologies · Welding Techniques and Residual Stresses
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (100+)
Show source-provided references
1. Gigacycle fatigue of ferrous alloys10.1046/j.1460-2695.1999.t01-1-00185.x ↗
2. Gigacycle fatigue of metallic aircraft components10.1016/j.ijfatigue.2009.03.015 ↗
3. Subsurface crack initiation and propagation mechanisms in gigacycle fatigue10.1016/j.actamat.2010.07.022 ↗
4. Nicholas · 2006
5. Bathias · 2004
6. An understanding of very high cycle fatigue of metals10.1016/S0142-1123(03)00147-6 ↗
7. Very high cycle fatigue behaviors of a turbine engine blade alloy at various stress ratios10.1016/j.ijfatigue.2016.11.032 ↗
8. Very high cycle fatigue measuring techniques10.1016/j.ijfatigue.2012.11.016 ↗
9. Mean stress sensitivity and crack initiation mechanisms of spring steel for torsional and axial VHCF loading10.1016/j.ijfatigue.2016.04.017 ↗
10. Fatigue assessment of laser additive manufactured AlSi12 eutectic alloy in the very high cycle fatigue (VHCF) range up to 1E9 cycles
11. Redesigning axial-axial (biaxial) cruciform specimens for very high cycle fatigue ultrasonic testing machines10.1016/j.heliyon.2017.e00466 ↗
12. R.D. Pollak, Analysis of methods for determining high cycle fatigue strength of a material with investigation of Ti-6Al-4V gigacycle fatigue behavior, AIR FORCE INST OF TECH WRIGHT-PATTERSON AFB OH SCHOOL OF ENGINEERING AND MANAGEMENT, 2005.
13. Kazymyrovych · 2009
14. Review of multiaxial testing for very high cycle fatigue: From ‘conventional’to ultrasonic machines10.3390/machines8020025 ↗
15. How and why the fatigue S-N curve does not approach a horizontal asymptote10.1016/S0142-1123(01)00123-2 ↗
16. A review on the fatigue behavior of Ti-6Al-4V fabricated by electron beam melting additive manufacturing10.1016/j.ijfatigue.2018.09.022 ↗
17. Additive manufacturing of fatigue resistant materials: Challenges and opportunities10.1016/j.ijfatigue.2017.01.001 ↗
18. Effects of post-processing on the surface finish, porosity, residual stresses, and fatigue performance of additive manufactured metals: a review10.1007/s11665-021-06021-7 ↗
19. Fatigue failure predictions for steels in the very high cycle region–A review and recommendations10.1016/j.engfailanal.2014.07.015 ↗
20. Stepwise SN curve and fish-eye failure in gigacycle fatigue10.1046/j.1460-2695.1999.00206.x ↗
21. Course of SN-curves especially in the high-cycle fatigue regime with regard to component design and safety10.1016/j.ijfatigue.2006.11.015 ↗
22. Factors That Affect SN Fatigue Curves, Fatigue and Corrosion in Metals
23. Stephens · 2000
24. Specific features and mechanisms of fatigue in the ultrahigh-cycle regime10.1016/j.ijfatigue.2005.05.018 ↗
25. Very high cycle fatigue–Is there a fatigue limit?10.1016/j.ijfatigue.2010.05.009 ↗
26. There is no infinite fatigue life in metallic materials10.1046/j.1460-2695.1999.00183.x ↗
27. Gigacycle fatigue behavior of high strength aluminum alloys10.1016/j.proeng.2010.03.007 ↗
28. Fatigue crack initiation detection by an infrared thermography method10.1111/j.1460-2695.2009.01410.x ↗
29. Subsurface crack initiation and propagation mechanism in high-strength steel in a very high cycle fatigue regime10.1016/j.ijfatigue.2005.08.015 ↗
30. Very high cycle fatigue and fatigue crack propagation behavior of selective laser melted AlSi12 alloy10.1016/j.ijfatigue.2016.06.003 ↗
31. Effect of microstructure on ultra-high cycle fatigue behavior of Ti–6Al–4V10.1016/j.msea.2007.04.062 ↗
32. C. Bathias, Gigacycle fatigue of high strength steels prediction and mechanisms, European Structural Integrity Society, Elsevier, 2000, pp. 163-171.10.1016/S1566-1369(00)80048-5 ↗
33. A tribute to claude bathias-highlights of his pioneering work in gigacycle fatigue10.1016/j.ijfatigue.2016.04.020 ↗
34. H. Kitagawa, Applicability of fracture mechanics to very small cracks or the cracks in the early stage, Proc. of 2nd ICM, Cleveland, 1976 (1976) 627-631.
35. Fatigue testing and properties of hardmetals in the gigacycle range10.1016/j.ijrmhm.2016.07.004 ↗
36. Fatigue crack initiation mechanisms
37. The physics of fatigue crack initiation10.1016/j.ijfatigue.2012.10.009 ↗
38. M. Zimmermann, Very High Cycle Fatigue, in: H.C.e. al. (Ed.), Handbook of Mechanics of Materials, Springer, Singapore, 2018.10.1007/978-981-10-6855-3_43-1 ↗
39. On the mechanism of fatigue failure in the superlong life regime (N> 10^7 cycles). Part 1: influence of hydrogen trapped by inclusions10.1046/j.1460-2695.2000.00328.x ↗
40. T. Sakai, H. Harada, N. Oguma, Crack initiation mechanism of bearing steel in very high cycle fatigue, Proceedings of ECF-16, CD-ROM, 2006.
41. Mechanism of fatigue crack initiation and propagation in the very high cycle fatigue regime of high-strength steels10.1016/j.scriptamat.2012.07.049 ↗
42. Mechanisms and modeling of subsurface fatigue cracking in metals10.1016/j.engfracmech.2013.05.013 ↗
43. On the formation mechanisms of fine granular area (FGA) on the fracture surface for high strength steels in the VHCF regime10.1016/j.ijfatigue.2015.08.021 ↗
44. Effects of inclusion size and location on very-high-cycle fatigue behavior for high strength steels10.1016/j.msea.2012.07.118 ↗
45. Microscopic damage evolution during very-high-cycle fatigue (VHCF) of tempered martensitic steel10.1111/ffe.12685 ↗
46. Effects of inclusions on the very high cycle fatigue behaviour of steels10.1111/ffe.12649 ↗
47. The nature and the mechanism of crack initiation and early growth for very-high-cycle fatigue of metallic materials–An overview10.1016/j.tafmec.2017.05.002 ↗
48. Subsurface inclusion-induced crack nucleation and growth behaviors of high strength steels under very High cycle fatigue: Characterization and microstructure-based modeling10.1016/j.msea.2015.06.037 ↗
49. Interior failure mechanism and life prediction of surface-treated 17Cr-Ni steel under high and very high cycle fatigue10.1111/ffe.12774 ↗
50. Review and prospects for current studies on very high cycle fatigue of metallic materials for machine structural use10.1299/jmmp.3.425 ↗
51. TEM/SEM investigation of microstructural changes within the white etching area under rolling contact fatigue and 3-D crack reconstruction by focused ion beam10.1016/j.scriptamat.2007.06.024 ↗
52. Fatigue crack propagation behaviour derived from S-N data in very high cycle regime10.1046/j.1460-2695.2002.00547.x ↗
53. Fatigue crack growth from small to large cracks on very high cycle fatigue with fish-eye failures10.1016/j.engfracmech.2007.05.015 ↗
54. Propensities of crack interior initiation and early growth for very-high-cycle fatigue of high strength steels10.1016/j.ijfatigue.2013.02.023 ↗
55. A cumulative damage model for fatigue life estimation of high-strength steels in high-cycle and very-high-cycle fatigue regimes10.1111/j.1460-2695.2011.01658.x ↗
56. Effects of intermittent loading on fatigue life of a high strength steel in very high cycle fatigue regime10.1016/j.ijfatigue.2018.07.033 ↗
57. Effect of inclusion on subsurface crack initiation and gigacycle fatigue strength10.1016/S0142-1123(02)00037-3 ↗
58. The formation mechanism of characteristic region at crack initiation for very-high-cycle fatigue of high-strength steels10.1016/j.ijfatigue.2015.11.029 ↗
59. Effects of microstructure on the fatigue crack growth behavior of light metals and design considerations10.1590/S1517-70762010000200033 ↗
60. Interior crack initiation and growth behaviors and life prediction of a carburized gear steel under high cycle fatigue and very high cycle fatigue10.1557/jmr.2015.182 ↗
61. Piezoelectric driven testing facilities to research the very high cycle fatigue regime10.3139/120.110388 ↗
62. A.S.M. Handbook, mechanical testing and evaluation, vol. 8, Materials Park, OH: ASM International, 2000.
63. Recent advances in very high cycle fatigue behavior of metals and alloys—a review10.3390/met10091200 ↗
64. S. Japan Welding Engineering, Standard test method for ultrasonic fatigue testing of metallic materials, Standard No. WES 1112, 2017.
65. Gigacycle fatigue behaviour of austenitic stainless steels used for mercury target vessels10.1016/j.jnucmat.2015.07.040 ↗
66. P. Wen-jie, X. Huan, The influential factors on very high cycle fatigue testing results, EDP Sciences 20002.10.1051/matecconf/201816520002 ↗
67. Very high cycle and gigacycle fatigue of fiber-reinforced composites: A review on experimental approaches and fatigue damage mechanisms10.1016/j.pmatsci.2020.100762 ↗
68. Very high cycle fatigue property of high-strength austempered ductile iron at conventional and ultrasonic frequency loading10.1016/j.ijfatigue.2014.09.021 ↗
69. Piezoelectric fatigue testing machines and devices10.1016/j.ijfatigue.2005.09.020 ↗
70. M.W. Tofique, Initiation and Early Crack Growth in VHCF of Stainless Steels: Experimental and Theoretical Analysis, Doctoral Thesis, Karlstad University, 2016.
71. M.M.T. Very High Cycle Fatigue (VHCF). https://3r-labo.com/en/mechanical-engineering/very-high-cycle-fatigue-vhcf/.
72. USF-2000A Ultrasonic Gigacycle Fatigue Testing System https://www.ssi.shimadzu.com/products/fatigue-testing/usf-2000a.html.
73. Ultrasonic Fatigue Evaluation System at High Temperature. http://www.mbrosia.co.kr/en/product/product0103.php.
74. K. Solberg, F. Berto, What is going on with fatigue of additively manufactured metals?, Mater. Design & Process. Commun. 1(5) (2019) e84.10.1002/mdp2.84 ↗
75. Fatigue of additive manufacturing specimens: a comparison with casting processes
76. Fatigue characteristics of steels manufactured by selective laser melting10.1016/j.ijfatigue.2018.12.029 ↗
77. Fatigue characterization of titanium Ti-6Al-4V samples produced by additive manufacturing10.1016/j.prostr.2016.06.395 ↗
78. Very-high-cycle fatigue behavior of AlSi10Mg manufactured by selected laser melting: Crystal plasticity modeling10.1016/j.ijfatigue.2020.106109 ↗
79. Technical note High-cycle fatigue crack initiation and propagation behaviour of high-strength sprin steel wires
80. Micro-crack initiation and propagation in a high strength aluminum alloy during very high cycle fatigue10.1016/j.msea.2018.01.008 ↗
81. Investigation of small fatigue crack initiation and growth behaviour of nickel base superalloy GH416910.1111/ffe.12430 ↗
82. Prediction of fretting fatigue crack initiation in double lap bolted joint using continuum damage mechanics10.1016/j.ijfatigue.2014.11.012 ↗
83. A comparison of fatigue strength sensitivity to defects for materials manufactured by AM or traditional processes10.1016/j.ijfatigue.2016.06.020 ↗
84. Roles of microstructure in fatigue crack initiation10.1016/j.ijfatigue.2009.10.005 ↗
85. E. Brandl, U. Heckenberger, V. Holzinger, D.J.M. Buchbinder, Design, Additive manufactured AlSi10Mg samples using Selective Laser Melting (SLM): Microstructure, high cycle fatigue, and fracture behavior 34 (2012) 159–169.10.1016/j.matdes.2011.07.067 ↗
86. Microstructure and fatigue behavior of a laser additive manufactured 12CrNi2 low alloy steel10.1016/j.msea.2019.138685 ↗
87. The effect of manufacturing defects on the fatigue life of selective laser melted Ti-6Al-4V structures10.1016/j.matdes.2020.108708 ↗
88. A review on selective laser sintering/melting (SLS/SLM) of aluminium alloy powders: Processing, microstructure, and properties10.1016/j.pmatsci.2015.03.002 ↗
89. Laser powder bed fusion of potential superalloys: a review10.3390/met11010058 ↗
90. Processing parameters in laser powder bed fusion metal additive manufacturing10.1016/j.matdes.2020.108762 ↗
91. In situ monitoring systems of the SLM process: On the need to develop machine learning models for data processing10.3390/cryst10060524 ↗
92. Effects of defects on mechanical properties in metal additive manufacturing: A review focusing on X-ray tomography insights10.1016/j.matdes.2019.108385 ↗
93. Selective laser melting of nano-TiB2 decorated AlSi10Mg alloy with high fracture strength and ductility10.1016/j.actamat.2017.02.062 ↗
94. Strength and strain hardening of a selective laser melted AlSi10Mg alloy10.1016/j.scriptamat.2017.07.025 ↗
95. An overview of very high cycle fatigue behavior of additively manufactured Ti-6Al-4V10.62704/10057/24248 ↗
96. Correlation between porosity and processing parameters in TiAl6V4 produced by selective laser melting10.1016/j.matdes.2016.05.070 ↗
97. Crack initiation behavior and fatigue performance up to very-high-cycle regime of AlSi10Mg fabricated by selective laser melting with two powder sizes10.1016/j.ijfatigue.2020.106013 ↗
98. Defects in additive manufactured metals and their effect on fatigue performance: A state-of-the-art review10.1016/j.pmatsci.2020.100724 ↗
99. Analysis of the effect of internal defects on fatigue performance of additive manufactured metals10.1016/j.msea.2020.139385 ↗
100. X-ray microcomputed tomography in additive manufacturing: a review of the current technology and applications10.1089/3dp.2018.0060 ↗