A Calcium Coordination Framework Having Permanent Porosity and High CO2/N2 Selectivity
Source abstract
Abstract
A thermally stable, microporous calcium coordination network shows a reversible 5.75 wt % CO 2 uptake at 273 K and 1 atm pressure, with an enthalpy of interaction of ∼31 kJ/mol and a CO 2 /N 2 selectivity over 45 under ideal flue gas conditions. The absence of open metal sites in the activated material suggests a different mechanism for selectivity and high interaction energy compared to those for frameworks with open metal sites.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Metal-Organic Frameworks: Synthesis and Applications · Covalent Organic Framework Applications · Carbon Dioxide Capture Technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Chemistry, Stony Brook University, Stony Brook, New York 11794-3400, United States
Department of Chemistry and Chemical Biology, Rutgers University, Piscataway, New Jersey 08854, United States
Department of Geosciences, Stony Brook University, Stony Brook, New York 11794-2100, United States
Photon Source Division, Brookhaven National Laboratory, Upton, New York 11973, United States
References (62)
Show source-provided references
1. 10.1021/cr200327210.1021/cr2003272 ↗
2. 10.1039/c1cs15221a10.1039/c1cs15221a ↗
3. Saha D. · Environ. Sci. Technol. · 2010 · 44 · 182010.1021/es9032309 ↗
4. White J. C. · Langmuir · 2010 · 26 · 1028710.1021/la100463j ↗
5. Liu Q. L. · Chem. Commun. · 2010 · 46 · 450210.1039/c000900h ↗
6. Ho M. T. · Ind. Eng. Chem. Res. · 2008 · 47 · 156210.1021/ie070541y ↗
7. Caro J. · Microporous Mesoporous Mater. · 2000 · 38 · 310.1016/S1387-1811(99)00295-4 ↗
8. Breck D. W. · 1984
9. Barrer R. M. · 1978
10. Long J. R. · Chem. Soc. Rev. · 2009 · 38 · 121310.1039/b903811f ↗
11. Banerjee D. · Cryst. Growth Des. · 2011 · 11 · 470410.1021/cg2008304 ↗
12. Murray L. J. · Chem. Soc. Rev. · 2009 · 38 · 129410.1039/b802256a ↗
13. 10.1021/cr200274s10.1021/cr200274s ↗
14. 10.1021/cr200216x10.1021/cr200216x ↗
15. Li J. R. · Chem. Soc. Rev. · 2009 · 38 · 147710.1039/b802426j ↗
16. 10.1021/cr200190s10.1021/cr200190s ↗
17. Ma L. Q. · Chem. Soc. Rev. · 2009 · 38 · 124810.1039/b807083k ↗
18. 10.1021/cr200314710.1021/cr2003147 ↗
19. Caskey S. R. · J. Am. Chem. Soc. · 2008 · 130 · 1087010.1021/ja8036096 ↗
20. Dinca M. · J. Am. Chem. Soc. · 2005 · 127 · 937610.1021/ja0523082 ↗
21. Dietzel P. D. C. · Eur. J. Inorg. Chem. · 2008 · 362410.1002/ejic.200701284 ↗
22. Mallick A. · J. Mater. Chem. · 2010 · 20 · 907310.1039/c0jm01125h ↗
23. Britt D. · Proc. Natl. Acad. Sci. U. S. A. · 2009 · 106 · 2063710.1073/pnas.0909718106 ↗
24. Lee J. D. · 1991
25. Volkringer C. · Cryst. Growth Des. · 2008 · 8 · 68510.1021/cg700685g ↗
26. Miller S. R. · CrystEngComm · 2011 · 13 · 189410.1039/C0CE00450B ↗
27. Platero-Prats A. E. · Chem.—Eur. J. · 2010 · 16 · 1163210.1002/chem.201001218 ↗
28. Liang P. C. · Cryst. Growth Des. · 2011 · 11 · 69910.1021/cg101114h ↗
29. Yeh C.-T. · CrystEngComm · 2012 · 14 · 121910.1039/c2ce05875h ↗
30. Spek A. L. · J. Appl. Cryst. · 2003 · 36 · 710.1107/S0021889802022112 ↗
31. Rowsell J. L. C. · J. Am. Chem. Soc. · 2006 · 128 · 130410.1021/ja056639q ↗
32. Zhou W. · J. Phys. Chem. C · 2007 · 111 · 1613110.1021/jp074889i ↗
33. Ma S. Q. · J. Am. Chem. Soc. · 2008 · 130 · 1589610.1021/ja803492q ↗
34. Wang Q. M. · Microporous Mesoporous Mater. · 2002 · 55 · 21710.1016/S1387-1811(02)00405-5 ↗
35. Millward A. R. · J. Am. Chem. Soc. · 2005 · 127 · 1799810.1021/ja0570032 ↗
36. 10.1021/ja211340t10.1021/ja211340t ↗
37. Abrahams B. F. · Angew. Chem., Int. Ed. · 2010 · 49 · 108710.1002/anie.200906322 ↗
38. Myers A. L. · AIChE. J. · 1965 · 11 · 12110.1002/aic.690110125 ↗
39. Babarao R. · Langmuir · 2006 · 23 · 65910.1021/la062289p ↗
40. Krishna R. · Sep. Purif. Technol. · 2003 · 33 · 21310.1016/S1383-5866(03)00008-X ↗
41. Goj A. · J. Phys. Chem. B · 2002 · 106 · 836710.1021/jp025895b ↗
42. Challa S. R. · J. Chem. Phys. · 2002 · 116 · 81410.1063/1.1423665 ↗
43. Peng J. · Chem. Phys. Lett. · 2005 · 401 · 9410.1016/j.cplett.2004.11.036 ↗
44. Bae Y.-S. · Langmuir · 2008 · 24 · 859210.1021/la800555x ↗
45. Babarao R. · Langmuir · 2009 · 25 · 523910.1021/la803074g ↗
46. Bae Y.-S. · Chem. Commun. · 2008 · 413510.1039/b805785k ↗
47. Bae Y.-S. · J. Mater. Chem. · 2009 · 19 · 213110.1039/b900390h ↗
48. Mason J. A. · Energy Environ. Sci. · 2011 · 4 · 303010.1039/c1ee01720a ↗
49. 10.1002/anie.20110596610.1002/anie.201105966 ↗
50. Yang Q. · J. Phys. Chem. B · 2006 · 110 · 1777610.1021/jp062723w ↗
51. Krishna R. · Phys. Chem. Chem. Phys. · 2011 · 13 · 1059310.1039/c1cp20282k ↗
52. Dietzel P. D. C. · J. Mater. Chem. · 2009 · 19 · 736210.1039/b911242a ↗
53. Yang Q. · AIChE J. · 2007 · 53 · 283210.1002/aic.11298 ↗
54. Belmabkhout Y. · Chem. Eng. Sci. · 2009 · 64 · 372910.1016/j.ces.2009.05.039 ↗
55. Liu B. · Langmuir · 2009 · 25 · 591810.1021/la900823d ↗
56. Dreisbach F. · Adsorption · 1999 · 5 · 21510.1023/A:1008914703884 ↗
57. Wu H. · Chem.—Eur. J. · 2010 · 16 · 1395110.1002/chem.201002683 ↗
58. Czepirski L. · Chem. Eng. Sci. · 1989 · 44 · 79710.1016/0009-2509(89)85253-4 ↗
59. Rowsell J. L. C. · J. Am. Chem. Soc. · 2006 · 128 · 130410.1021/ja056639q ↗
60. Lee J. Y. · Adv. Funct. Mater. · 2007 · 17 · 125510.1002/adfm.200600944 ↗
61. Zhang J. · Chem. Commun. · 2010 · 46 · 915210.1039/c0cc02942d ↗
62. Liu H. · Adv. Funct. Mater. · 2011 · 21 · 475410.1002/adfm.201101479 ↗