Recent advances in gum metal: Synthesis, performance and application
Source abstract
Abstract
The development of prosthesis implantation as a means to treat bone defects in the field of orthopedic surgery is booming. Some materials with excellent biocompatibility are available for practical application, while new materials are being continuously developed. Gum metal is a new type of multifunctional β-type titanium alloy, and its basic composition can be expressed as Ti-24(Ta + Nb + V)-(Zr, Hf)-O. Gum metal has a good combination of a low elastic modulus and high strength, which promotes its emergence in the biological field. Moreover, gum metal combines the advantages of nonlinear elasticity, low work hardening rate and nontoxicity, making it a new material with potential in the future. This review begins with the design origin of gum metal and the influence of various elements on this kind of alloy. Second, the fabrication process and deformation mechanism of gum metal are summarized. Finally, the properties and current application fields of gum metal are introduced.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Titanium Alloys Microstructure and Properties · Advanced materials and composites · Bone Tissue Engineering Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan, Shanxi, China
Key Laboratory of Education Ministry for Modern Design and Rotor-Bearing System, Xìan Jiaotong University, Xìan, Shaanxi, China
Key Laboratory of Interface Science and Engineering of New Materials, Ministry of Education, Taiyuan University of Technology, Taiyuan, Shanxi, China
National-Local Joint Engineering Research Centre of Nonferrous Metals and Processing Technology, Hefei University of Technology, Hefei, Anhui, China
Funding
National Natural Science Foundation of China · China Postdoctoral Science Foundation · Natural Science Foundation of Shanxi Province · Transformation of Scientific and Technological Achievements Program of Higher Education Institutions in Shanxi · Research Project Supported by Shanxi Scholarship Council of China
References (98)
Show source-provided references
1. 10.1016/S0043-1648(99)00359-210.1016/S0043-1648(99)00359-2 ↗
2. 10.1016/S1359-0286(96)80022-210.1016/S1359-0286(96)80022-2 ↗
3. 10.1016/j.jallcom.2008.04.02410.1016/j.jallcom.2008.04.024 ↗
4. 10.1016/j.mser.2004.11.00110.1016/j.mser.2004.11.001 ↗
5. 10.1007/s11837-001-0139-z10.1007/s11837-001-0139-z ↗
6. 10.2478/v10147-010-0035-z10.2478/v10147-010-0035-z ↗
7. Zhang X. Y. · 2005
8. 10.1016/j.jmrt.2020.03.06110.1016/j.jmrt.2020.03.061 ↗
9. 10.1016/j.surfcoat.2019.04.03810.1016/j.surfcoat.2019.04.038 ↗
10. 10.1016/j.corsci.2018.03.01210.1016/j.corsci.2018.03.012 ↗
11. Zhang L. C. · Adv. Eng. Mater. · 2020 · 1
12. 10.1016/j.matdes.2019.10806410.1016/j.matdes.2019.108064 ↗
13. 10.1016/j.scriptamat.2018.03.03310.1016/j.scriptamat.2018.03.033 ↗
14. 10.1016/j.dental.2014.10.00210.1016/j.dental.2014.10.002 ↗
15. 10.1016/j.msea.2013.11.03810.1016/j.msea.2013.11.038 ↗
16. 10.1016/j.jallcom.2019.04.07910.1016/j.jallcom.2019.04.079 ↗
17. 10.1016/j.matdes.2019.10789110.1016/j.matdes.2019.107891 ↗
18. 10.1016/j.scriptamat.2018.05.01010.1016/j.scriptamat.2018.05.010 ↗
19. Leyens C. · 2005
20. Zhang Y. M. · J. Biomed. Eng. · 2000 · 17 · 206
21. 10.1016/S0921-5093(97)00806-X10.1016/S0921-5093(97)00806-X ↗
22. 10.1002/adem.20180121510.1002/adem.201801215 ↗
23. 10.1016/j.matdes.2016.09.02910.1016/j.matdes.2016.09.029 ↗
24. Zhao Y. · Ceram. Int. · 2021 · 1 · 1
25. Liu Y. · Ordnance. Mater. Sci. Eng. · 2005 · 28 · 47
26. Ewart P. · Technol. Lightweight Struct. · 2019 · 3 · 60
27. Yang J. · Aviat. Manuf. Technol. · 2006 · 11 · 41
28. 10.1097/BOT.0b013e3181cec4a110.1097/BOT.0b013e3181cec4a1 ↗
29. 10.1097/SCS.0b013e318241dcba10.1097/SCS.0b013e318241dcba ↗
30. 10.2147/IJN.S31100110.2147/IJN.S311001 ↗
31. Ramezannejad A. · Curr. Opin. Solid. St. M · 2019 · 1
32. 10.1016/j.cossms.2018.05.00210.1016/j.cossms.2018.05.002 ↗
33. 10.1016/j.msec.2018.03.01110.1016/j.msec.2018.03.011 ↗
34. 10.1016/j.biomaterials.2003.08.01510.1016/j.biomaterials.2003.08.015 ↗
35. 10.1111/j.1600-0501.2005.01197.x10.1111/j.1600-0501.2005.01197.x ↗
36. 10.1016/j.ceramint.2017.12.04010.1016/j.ceramint.2017.12.040 ↗
37. 10.1126/science.108195710.1126/science.1081957 ↗
38. Ye W. J. · Sci. Technol. Rev. · 2008 · 26 · 80
39. Yang Y. · Chin. J. Mater. Res · 2011 · 25 · 1
40. 10.1016/j.scriptamat.2009.02.04410.1016/j.scriptamat.2009.02.044 ↗
41. 10.1016/j.actamat.2010.02.00110.1016/j.actamat.2010.02.001 ↗
42. 10.1007/s10856-012-4569-710.1007/s10856-012-4569-7 ↗
43. 10.1016/j.scriptamat.2008.05.02210.1016/j.scriptamat.2008.05.022 ↗
44. 10.1016/j.actamat.2015.08.04710.1016/j.actamat.2015.08.047 ↗
45. 10.3365/KJMM.2013.51.4.30710.3365/KJMM.2013.51.4.307 ↗
46. 10.1016/j.matlet.2018.08.15110.1016/j.matlet.2018.08.151 ↗
47. 10.2320/jinstmet.70.57910.2320/jinstmet.70.579 ↗
48. 10.2320/matertrans.46.300110.2320/matertrans.46.3001 ↗
49. 10.1016/j.actamat.2011.06.00610.1016/j.actamat.2011.06.006 ↗
50. 10.1016/j.scriptamat.2016.05.04310.1016/j.scriptamat.2016.05.043 ↗
51. 10.1016/j.actamat.2015.12.01110.1016/j.actamat.2015.12.011 ↗
52. 10.1016/j.ijhydene.2014.01.10310.1016/j.ijhydene.2014.01.103 ↗
53. 10.1016/j.matdes.2018.10.04010.1016/j.matdes.2018.10.040 ↗
54. 10.4028/www.scientific.net/MSF.426-432.68110.4028/www.scientific.net/MSF.426-432.681 ↗
55. 10.1016/j.scriptamat.2007.09.01010.1016/j.scriptamat.2007.09.010 ↗
56. Aoyama T. · Key Eng. Mater · 2005 · 495 · 297
57. 10.1016/j.msea.2013.03.02910.1016/j.msea.2013.03.029 ↗
58. 10.1007/s11661-012-1598-210.1007/s11661-012-1598-2 ↗
59. 10.1016/j.msea.2016.07.09610.1016/j.msea.2016.07.096 ↗
60. 10.1016/j.surfcoat.2019.01.08610.1016/j.surfcoat.2019.01.086 ↗
61. 10.1361/105994905X7555610.1361/105994905X75556 ↗
62. 10.1016/j.ijplas.2007.09.00910.1016/j.ijplas.2007.09.009 ↗
63. 10.1016/j.actamat.2006.01.02710.1016/j.actamat.2006.01.027 ↗
64. 10.3139/146.11018410.3139/146.110184 ↗
65. 10.1016/j.scriptamat.2011.07.00410.1016/j.scriptamat.2011.07.004 ↗
66. 10.1016/j.actamat.2009.12.05210.1016/j.actamat.2009.12.052 ↗
67. 10.1016/j.msea.2007.07.09710.1016/j.msea.2007.07.097 ↗
68. 10.4028/www.scientific.net/KEM.465.2110.4028/www.scientific.net/KEM.465.21 ↗
69. 10.1016/j.actamat.2018.03.04810.1016/j.actamat.2018.03.048 ↗
70. 10.1016/j.actamat.2008.10.00210.1016/j.actamat.2008.10.002 ↗
71. 10.1103/PhysRevLett.98.10550310.1103/PhysRevLett.98.105503 ↗
72. 10.1016/j.scriptamat.2013.01.03410.1016/j.scriptamat.2013.01.034 ↗
73. 10.1016/j.jmst.2020.03.04210.1016/j.jmst.2020.03.042 ↗
74. 10.1016/S1003-6326(07)60294-510.1016/S1003-6326(07)60294-5 ↗
75. 10.1016/j.actamat.2008.11.01310.1016/j.actamat.2008.11.013 ↗
76. 10.1016/j.actamat.2017.06.05110.1016/j.actamat.2017.06.051 ↗
77. 10.1016/j.colsurfb.2016.07.00710.1016/j.colsurfb.2016.07.007 ↗
78. 10.1177/204173141877417810.1177/2041731418774178 ↗
79. 10.1016/j.msec.2014.08.00310.1016/j.msec.2014.08.003 ↗
80. 10.1016/j.jmbbm.2020.10428910.1016/j.jmbbm.2020.104289 ↗
81. Golasiński K. M. · Quant. Infr. Therm. J · 2017 · 1284295 · 1
82. 10.3390/ma1104056710.3390/ma11040567 ↗
83. 10.1016/j.msea.2018.03.06210.1016/j.msea.2018.03.062 ↗
84. 10.1016/j.msea.2017.06.09910.1016/j.msea.2017.06.099 ↗
85. Golasiński K. · Mater. Sci. Tech · 2019 · 1
86. 10.1016/j.mspro.2014.06.17610.1016/j.mspro.2014.06.176 ↗
87. 10.1016/j.msea.2005.12.08910.1016/j.msea.2005.12.089 ↗
88. 10.1016/j.actamat.2015.01.03310.1016/j.actamat.2015.01.033 ↗
89. 10.1016/j.ijplas.2019.02.01710.1016/j.ijplas.2019.02.017 ↗
90. 10.1016/j.electacta.2019.02.02410.1016/j.electacta.2019.02.024 ↗
91. 10.1007/s10856-020-06428-z10.1007/s10856-020-06428-z ↗
92. 10.1016/j.kjms.2018.01.01010.1016/j.kjms.2018.01.010 ↗
93. 10.3390/ma1411293410.3390/ma14112934 ↗
94. 10.1007/s10856-013-5101-410.1007/s10856-013-5101-4 ↗
95. 10.1299/jmmp.2.49610.1299/jmmp.2.496 ↗
96. 10.1016/B0-08-043152-6/02131-810.1016/B0-08-043152-6/02131-8 ↗
97. Zhang X. M. · Titanium Industry Progress · 2005 · 22 · 5
98. 10.1016/j.jmrt.2020.03.12310.1016/j.jmrt.2020.03.123 ↗