Validating corrosion models: Influence of physical properties

In chloride containing environments, two metals in physical contact can undergo galvanic corrosion limiting the lifetime of components. Being able to accurately predict galvanic corrosion damage distributions over time has not been widely presented. Therefore, Finite Element Method (FEM) corrosion models were experimentally validated for two galvanic couples as a function of governing equations, environment, anode material, anode:cathode ratio, and time. Carbon steel/stainless steel (CS/SS) and zinc/stainless steel (Zn/SS) galvanic couples were exposed to NaCl solutions at room temperatures for up to 14 days. For the galvanic couples and environments, the Laplace equation with variable conductivity with reactions was sufficient to model the experimental corrosion damage. Increasing the chloride concentration for the CS/SS galvanic couple, regardless of the anode:cathode ratio, decreased the observed and modeled corrosion damage. Decreasing the anode:cathode ratio ( i.e. , increasing the cathode length), increased the experimentally observed and modeled corrosion damage. For small anode:cathode ratios, the governing equations deviate over long time periods with the Nernst-Plank equation being conservative. For the Zn/SS galvanic couple, the cathode length controls the dominant cathodic reduction reaction. For small cathode lengths, the hydrogen evolution reaction is dominant. For larger cathode lengths, the oxygen reduction reaction is dominant. The results are discussed with regard to the influence of solution chemistry, ohmic drop, and governing reactions. Overall, validated FEM models were presented, and the resultant models, physics, and mechanisms can be applied to other corrosion scenarios with confidence. • Governing physics equations validated for explored galvanic couples over time • Increasing chloride concentration decreased modeled and experimental damage • Oxygen reduction reaction controls decrease in damage with increased chloride • Decreasing anode:cathode ratio increased modeled and experimental damage • Dominant cathodic reaction influenced by anode:cathode ratio and anode material