Reply to “Notes on the discussion concerning ‘surface mobility mechanism’ of stress corrosion cracking”, by E.M. Gutman
Source abstract
Abstract
Abstract The reply to the criticisms made by Gutman to the surface mobility stress corrosion cracking (SCC) model is used as an opportunity to discuss areas that are considered obscure or underdeveloped in the present day SCC literature. One of the major limitations is the absence of a reliable description, at a molecular level, of the tip of the cracks. This description should include not only the stressed metal, but also the environment.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Corrosion Behavior and Inhibition · Hydrogen embrittlement and corrosion behaviors in metals · Material Properties and Failure Mechanisms
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (31)
Show source-provided references
1. Vacancies in stress corrosion cracking mechanisms
2. E.M. Gutman, Some notes on the discussion concerning surface mobility mechanism of SCC as proposed by J.R. Galvele in many papers and criticized by K. Sieradzki and F.J. Friedersdorf in Corrosion Science, 15th International Corrosion Congress, Granada, Spain, 22–27 September 2002, Poster no. 835
3. Sieradzki · Corrosion Science · 1994 · 36 · 66910.1016/0010-938X(94)90072-8 ↗
4. Galvele · Corrosion Science · 1994 · 36 · 90110.1016/0010-938X(94)90178-3 ↗
5. Electrochemical aspects of stress corrosion cracking
6. Galvele · Corrosion · 1999 · 55 · 72310.5006/1.3284027 ↗
7. Galvele · Corrosion Science · 1987 · 27 · 110.1016/0010-938X(87)90117-X ↗
8. Montoto · Corrosion Science · 2001 · 43 · 75510.1016/S0010-938X(00)00112-8 ↗
9. Giordano · Corrosion Science · 1997 · 39 · 191510.1016/S0010-938X(97)00085-1 ↗
10. Galvele · Corrosion Science · 1997 · 39 · 60510.1016/S0010-938X(97)00001-2 ↗
11. Duffó · Corrosion Science · 1990 · 30 · 24910.1016/0010-938X(90)90078-J ↗
12. Bianchi · Corrosion Science · 1987 · 27 · 63110.1016/0010-938X(87)90035-7 ↗
13. Bianchi · Corrosion Science · 1993 · 34 · 141110.1016/0010-938X(93)90237-B ↗
14. Galvele · Journal of Electrochemical Society · 1986 · 133 · 95310.1149/1.2108773 ↗
15. Van Bueren · 1960
16. Hirth · Acta Metallurgica · 1985 · 33 · 35910.1016/0001-6160(85)90078-1 ↗
17. Galvele · Corrosion Science · 1993 · 35 · 41910.1016/0010-938X(93)90175-G ↗
18. Gjostein · 1967 · 271
19. Rhead · Surface Science · 1969 · 15 · 35310.1016/0039-6028(69)90160-5 ↗
20. Rhead · Surface Science · 1970 · 22 · 22310.1016/0039-6028(70)90036-1 ↗
21. Thomas · Corrosion · 2000 · 56 · 57210.5006/1.3280561 ↗
22. J.R. Galvele, The trend in SCC studies in recent times, 15th International Corrosion Congress, Granada, Spain, 22–27 September 2002. Key Note Lecture
23. Magdowski · Metallurgical Transactions A · 1988 · 19A · 158310.1007/BF02674033 ↗
24. H. Vogt, Temperature Dependency of Stress Corrosion Cracking, Doctor of Technical Sciences thesis, Swiss Federal Institute of Technology, 1997. Supervisor Prof. Dr. M.O. Speidel, Diss. ETH no. 12238
25. Vogt · Corrosion Science · 1998 · 40 · 25110.1016/S0010-938X(97)00132-7 ↗
26. Prediction of stress corrosion crack growth in service based on laboratory data
27. Galvele · Journal of Nuclear Materials · 1996 · 229 · 13910.1016/0022-3115(95)00208-1 ↗
28. Delamare · Surface Science · 1971 · 28 · 26710.1016/0039-6028(71)90099-9 ↗
29. Gutman · 1969 · vol. 2 · 377
30. Silcock · 1979 · 133
31. R.B. Rebak, Z. Szklarska-Smialowska, Mechanism of stress corrosion cracking of alloy 600 in high temperature water, in: G. Airey et al. (Eds.), Seventh International Symposium on Environmental Degradation of Materials in Nuclear Power Systems––Water Reactors, NACE, Houston, TX, 1995, pp. 855–86510.1016/0010-938X(96)00183-7 ↗