Steric hindrance as a rate controlling step in stress corrosion cracking
Source abstract
Abstract
Abstract The effect of steric hindrance in the stress corrosion cracking (SCC) of Ag-15Pd (a/o) in AgI forming solutions was studied at room temperature. The solutions used were 1 M KI at a potential higher than that of AgI formation, and iodine dissolved in different n-alcohols. It was found that Ag-15Pd (a/o) is susceptible to intergranular stress corrosion cracking in those solutions. The SCC susceptibility measured as percentage of elongation to rupture and crack propagation rate is related to the size of the active species. While in KI aqueous solutions, as well as in iodine saturated benzene or iodine saturated toluene, the rate controlling step (RCS) was the reaction at the tip of the crack, in alcoholic-iodine solutions, the diffusion rate of the iodine containing molecules became the RCS.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Corrosion Behavior and Inhibition · Crystallography and molecular interactions · Crystallization and Solubility Studies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (19)
Show source-provided references
1. Stress corrosion cracking of α-brass in aliphatic amine solutions10.1179/000705974798321594 ↗
2. S.Shiga, M. Hoshino, A comprehensive investigation of chemical environments for stress corrosion cracking of α-brass: characteristics and practical meanings of non-ammoniacal activities, in: Conference on Environmental Degradation of Engineering Materials in Aggressive Environments, Blacksburg, VA, September 1981, pp. 201–209.
3. J.R. Galvele, G.S. Duffó, M.L. Montoto, M. Giordano, Effect of molecular size and exchange current density on the SCC of copper ans silver alloy, in: Corrosion/95, NACE International, Houston, Tx, Paper 128, 1995.
4. Experimental confirmation of the surface mobility-stress corrosion cracking mechanism: Ag-15Pd, Ag-15Au and Ag-30Cd alloys in halide and sulphate containing solutions10.1016/0010-938X(90)90078-J ↗
5. A stress corrosion mechanism based on surface mobility10.1016/0010-938X(87)90117-X ↗
6. Recent developments in the surface-mobility stress–corrosion–cracking mechanism10.1016/S0013-4686(00)00436-9 ↗
7. Molecular complexes in halogens10.1016/S0065-2792(08)60238-1 ↗
8. Bailar · 1973 · vol. 3
9. On the structure of iodine charge transfer complexes in solution10.1016/0009-2614(95)00683-U ↗
10. A spectroscopic study of the ethanol–iodine complex10.1021/ja01053a005 ↗
11. The color of iodine solutions10.1021/ja01931a005 ↗
12. Critical potential for localized corrosion of aluminum
13. Surface self-diffusion in FCC and BCC metals: a comparison of theory and experiment
14. On surface diffusion and the existence of “two-dimensional” liquids10.1016/0039-6028(69)90160-5 ↗
15. Reply to comment of H.P. Bonzel and N.A. Gjostein on “On surface diffusion and the existence of two-dimensional liquids”10.1016/0039-6028(70)90036-1 ↗
16. 1998
17. Pauling · 1960
18. Diffusional control in the intergranular corrosion of some hcp metals in iodine alcoholic solutions10.1016/j.corsci.2004.07.039 ↗
19. Electrochemical aspects of stress corrosion cracking