Metal dusting and coking of alloy 803

Abstract Investigation was made by SEM examination on metal dusting and coking behaviours of alloy 803 in a flowing gas mixture of H2–CO–H2O. It was found that an oxide scale arisen on the sample surface at the beginning of exposure. Metal dusting started when graphite deposition occurred earlier at the local defects in the oxide scale than the defects were repaired by enough supply of chromium from the interior of alloy matrix. Coke consisted of graphite filaments and metallic particles produced by disintegrating of alloy matrix, and grew up from the defects in the oxide scale with pit left in the sample surface. Increasing chromium content, doping a small amount of silicon and reducing grain size to create fast diffusion paths for chromium and silicon to alloy surface, all promote the formation of a dense oxide scale and favor early self-repairing of the defects in the oxide scale before occurrence of graphite deposition. The resistance of an alloy to metal dusting can be improved generally by means of these methods.