Effect of MgSO4 addition on alkali sulphates induced hot corrosion of a β-NiAl coating

The effect of MgSO 4 addition on alkali sulphates induced hot corrosion of a β-NiAl coating was studied by performing a series of tests with deposits of Na 2 SO 4 , Na 2 SO 4 -20 %K 2 SO 4 and Na 2 SO 4 -12 %K 2 SO 4 -35 %MgSO 4 (mol.% for all) at 700 °C in air with addition of SO 2 . For elucidating the observed corrosion phenomena, various salt-oxide/NiAl powder mixtures were exposed to the same hot corrosion test conditions. Two pseudo-binary phase diagrams of the Na, K, Mg-sulphate systems were calculated using an in-house developed thermodynamic database. Addition of MgSO 4 to Na 2 SO 4 -20 %K 2 SO 4 deposit salt inhibited the hot corrosion attack during 24 h exposure, which is related to consumption of aggressive K 2 SO 4 by the formation of solid K 2 Mg 2 (SO 4 ) 3 . However, extending the exposure with Na 2 SO 4 -12 %K 2 SO 4 -35 %MgSO 4 deposit to 100 h resulted in severe corrosion attack. The latter observation is explained by a reaction between K 2 Mg 2 (SO 4 ) 3 and NiAl causing formation of a Mg, Ni and Al containing spinel accompanied by release of the aggressive K 2 SO 4 into the liquid phase. • Addition of MgSO 4 to Na 2 SO 4 -K 2 SO 4 deposit inhibited initially hot corrosion of a NiAl-coating at 700°C in air – 300 ppm SO 2 . • The effect is related to formation of K 2 Mg 2 (SO 4 ) 3 , which effectively binds aggressive K 2 SO 4 . • After extended exposure the beneficial Mg-effect is lost due to formation of a Mg-Al spinel and release of K into the melt.