Estimation of hydrogen embrittlement process using statistical analysis method
Source abstract
Abstract
Abstract We propose a statistical analysis method to estimate the progress of the hydrogen embrittlement process by obtaining the transition probability λi that represents the average transition rate of the hydrogen embrittlement state. The estimation results are verified by Monte Carlo simulation. As an application of the proposed method, we evaluate the temperature dependence of the hydrogen embrittlement process and find that the threshold of the fracture decreases as temperature decreases. We also suggest that the rate-limiting process of the hydrogen embrittlement can be estimated by evaluating the apparent activation energy Ea of the state transition using the proposed method.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Hydrogen embrittlement and corrosion behaviors in metals · Nuclear Materials and Properties · Fatigue and fracture mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (36)
Show source-provided references
1. Nagumo · 2016
2. Hydrogen embrittlement understood10.1007/s11661-015-2836-1 ↗
3. The synergistic action and interplay of hydrogen embrittlement mechanisms in steels and iron: localized plasticity and decohesion10.1016/j.engfracmech.2019.106528 ↗
4. The role of hydrogen and other interstitials in the mechanical behavior of metals
5. Non-destructive characterization of hydrogen-embrittlement cracking by acoustic emission techniques10.1016/0013-7944(71)90021-X ↗
6. Monitoring hydrogen embrittlement cracking using acoustic emission technique10.1007/BF00542897 ↗
7. T. Kamisho, R. Ishii, M. Tsuda, Evaluating temperature dependence of hydrogen embrittlement process using statistical process model, in: Proc. JSCE Mater. Environ. 2020, Japan Society of Corrosion Engineering, Tokyo, 2020: pp. 183–186. (in Japanese).
8. Fatigue fracture from the standpoint of the stochastic theory10.1143/JPSJ.8.265 ↗
9. A kinetic approach to fatigue crack propagation
10. A new cumulative damage model: part 110.1115/1.3424282 ↗
11. Bogdanoff · 1985
12. Pitting corrosion as a stochastic process10.1038/260315a0 ↗
13. Stochastic theory of pitting corrosion10.5006/0010-9312-33.7.243 ↗
14. Part I: development of a markov description of pitting corrosion10.5006/1.3577840 ↗
15. Stochastic studies of passivity breakdown10.1016/0010-938X(90)90140-Z ↗
16. A spectrum analysis of potential fluctuation during passive film breakdown and repair on iron10.1016/0010-938X(92)90055-8 ↗
17. Stochastic modeling of pitting corrosion: a new model for initiation and growth of multiple corrosion pits10.1016/j.corsci.2006.05.049 ↗
18. Markov chain modelling of pitting corrosion in underground pipelines10.1016/j.corsci.2009.06.014 ↗
19. Stochastic approach to pitting-corrosion-extreme modelling in low-carbon steel10.1016/j.corsci.2009.11.011 ↗
20. Stochastic modelling of corrosion damage propagation in active sites from field inspection data10.1016/j.corsci.2008.03.005 ↗
21. Stochastic process corrosion growth models for pipeline reliability10.1016/j.corsci.2013.04.011 ↗
22. An investigation of hydrogen-induced delayed failure in unnotched specimens of 0.9%C steel strip
23. A new statistical model of the hydrogen embrittlement of steel10.1007/BF00700797 ↗
24. Evaluating the susceptibility of steels to hydrogen embrittlement using statistical analyses10.1007/BF00540515 ↗
25. A statistical failure distribution and lifetime assessment of the HSLA steel plates in H2S containing environments10.1016/0010-938X(96)00160-6 ↗
26. Hydrogen transport and embrittlement in 300 M and AerMet100 ultra high strength steels10.1016/j.corsci.2010.01.001 ↗
27. A statistical aspect of stress corrosion cracking of a high strength steel in NaCl solution10.1007/BF00016592 ↗
28. Dependence of distribution of stress corrosion cracking life of a high strength steel on various factors (prediction based on statistical natures of crack initiation and propagation lives and its experimental examination)10.1299/jsme1958.26.2039 ↗
29. Evaluation of hydrogen embrittlement susceptibility of high strength steel based on local approach10.2207/qjjws.22.125 ↗
30. A new evaluation method of hydrogen embrittlement fracture for high strength steel by local approach10.2355/isijinternational.45.263 ↗
31. Bazovsky · 1961
32. A statistical distribution function of wide applicability10.1115/1.4010337 ↗
33. Formation of hydrogen-assisted intergranular cracks in high strength steels10.1111/j.1460-2695.1995.tb00884.x ↗
34. Mass spectrometer measurements of the diffusion coefficient of hydrogen in steel in the temperature range of 25 °C–90 °C10.1063/1.1723324 ↗
35. 1976
36. Hydrogen thermal desorption relevant to delayed-fracture susceptibility of high-strength steels10.1007/s11661-001-0265-9 ↗