Effect of oxide film on oxygen reduction current for the platinum–cobalt alloy electrodes in PEFC

Effect of surface oxide on Pt–Co alloy electrodes on the oxygen reduction reaction (ORR) was investigated in 0.5 M sulfuric acid solution by electrochemistry, ellipsometry, laser Raman scattering spectroscopy, and XPS. The oxide as thick as 1–2 nm increases the overpotential of ORR and falls down efficiency of PEFC. The thickness of the oxide films is precisely determined by ellipsometry. The oxide film 1.9 nm thick was formed on Pt–50 mol% Co electrode by constant potential oxidation at 1.20 V and the film 1.5 nm thick remains on the electrode at 0.6 V at which ORR already starts. The remaining oxide decreases the current density of ORR and increases the overpotential. On pure Pt electrode, the similar influence of the oxide film was observed.