Two distinct fracture modes of copper alloys in fluoride environments
Source abstract
Abstract
The susceptibility of aluminum brass and aluminum bronze to stress corrosion cracking (SCC) was evaluated in fluoride environments by means of the slow strain rate technique. The effects of fluoride concentration and applied electrochemical potential on the SCC susceptibility were investigated. The SCC mechanism of aluminum brass was found to be dependent upon the de-alloying phenomenon while that of aluminum bronze on the film rupture mechanism occurring within a certain range of applied electrochemical potentials. For aluminum brass, both the stress ratio and the time-to-fracture ratio were closely related to the logarithmic concentration of F-ions. The fracture modes were ductile dimpled tearing fracture for the aluminum brass at the corrosion potential while intergranular for the aluminum bronze at various anodic potentials. The micro-galvanic effects of the constituent elements were used to estimate the anodic equilibrium potentials of the two alloys.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Metallurgy and Material Science · Aluminum Alloy Microstructure Properties · Microstructure and mechanical properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (30)
Show source-provided references
1. Parkins · Corros. Sci · 1980 · 20 · 14710.1016/0010-938X(80)90128-6 ↗
2. Parker · Corrosion · 1974 · 30 · 1810.5006/0010-9312-30.1.18 ↗
3. Parkins · Corrosion · 1982 · 38 · 24510.5006/1.3577346 ↗
4. Gouda · Br. Corros. J · 1983 · 18 · 4010.1179/000705983798274146 ↗
5. Pourbaix · 1974
6. Torchio · Corros. Sci · 1981 · 21 · 42510.1016/0010-938X(81)90041-X ↗
7. Mazza · Corros. Sci · 1983 · 23 · 105310.1016/0010-938X(83)90088-4 ↗
8. Torchio · Corros. Sci · 1981 · 21 · 5910.1016/0010-938X(81)90064-0 ↗
9. Finnegan · Corrosion · 1981 · 37 · 25610.5006/1.3621680 ↗
10. Verink · Corrosion · 1970 · 26 · 21410.5006/0010-9312-26.5.214 ↗
11. Shih · Corrosion · 1990 · 45 · 91310.5006/1.3580858 ↗
12. Shih · Corros. Sci · 1993 · 35 · 47910.1016/0010-938X(93)90180-O ↗
13. H.C. Shih, R.J. Tzou, International Conference on Environment-Induced Cracking of Metals, Kohler, Wisconsin, USA, 2–7 October 1989, pp. 389–395
14. Lee · J. Electrochem. Soc · 1995 · 142 · 73110.1149/1.2048526 ↗
15. ASTM G49-85, Annual Book of ASTM Standards, Philadelphia, PA, 1982
16. Congleton · Corros. Sci · 1985 · 25 · 76910.1016/0010-938X(85)90010-1 ↗
17. Bradford · Corrosion · 1978 · 34 · 9610.5006/0010-9312-34.3.96 ↗
18. Birley · Met. Trans · 1981 · 12A · 121510.1007/BF02642335 ↗
19. Environment-sensitive fracture: evaluation and comparison of test methods
20. ASTM G5-82, Annual Book of ASTM Standards, Philadelphia, PA, 1982
21. Jones · 1996
22. Parkins · Corrosion · 1978 · 34 · 25310.5006/0010-9312-34.8.253 ↗
23. Jones · 1996
24. Smart · Corros. Sci · 1990 · 30 · 87710.1016/0010-938X(90)90011-S ↗
25. Oung · Corros. Prevent. Control · 1997 · 106
26. Valand · Corros. Sci · 1977 · 17 · 44910.1016/0010-938X(77)90001-4 ↗
27. Shih · J. Electrochem. Soc · 1991 · 138 · 985
28. Strehblow · Corros. Sci · 1977 · 17 · 46110.1016/0010-938X(77)90002-6 ↗
29. Matamala · Corrosion · 1987 · 43 · 9710.5006/1.3583124 ↗
30. Fratesi · Corrosion · 1985 · 41 · 11410.5006/1.3581972 ↗