Study on corrosion behavior of 40Cr steel in 3.5 % NaCl solution under the synergistic effect of UV illumination and strain
Source abstract
Abstract
The corrosion behavior of 40Cr steel under the synergistic effect of plastic tensile strain and UV was investigated. The results show that the corrosion current density increases under the synergistic effect of strain and illumination. Before the formation of the complete rust layer, it is mainly attributed to the variation of the electric double layer, and the strain can enhance the effect of illumination on the electric double layer. After the formation of the complete rust layer, the increase in corrosion current density was mainly related to the change in the inner rust layer composition. Data availability The data that has been used is confidential.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Hydrogen embrittlement and corrosion behaviors in metals · Corrosion Behavior and Inhibition · Concrete Corrosion and Durability
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (49)
Show source-provided references
1. Fatigue behavior of high-strength steel S135 under coupling multi-factor in complex environments10.1016/j.msea.2018.03.093 ↗
2. The corrosion behavior of 316 stainless steel under the cooperative effect of plastic stress and UV illumination in 3.5 wt% NaCl solution10.1016/j.corsci.2023.111466 ↗
3. Synergistic acceleration effects of ultraviolet and salt spray on the degradation and failure of electromagnetic wave-absorbing coatings
4. Effects of chloride and oxygen on stress corrosion cracking of cold worked 316/316L austenitic stainless steel in high temperature water10.1016/j.corsci.2016.04.035 ↗
5. Adsorption of water on copper, nickel and iron10.5006/1.3280431 ↗
6. The evolution of the adsorbed solution layer during atmospheric corrosion and its effects on the corrosion rate of copper10.1149/1.2220734 ↗
7. Electrochemical measurement of time-of-wetness and atmospheric corrosion rates10.5006/0010-9312-33.1.13 ↗
8. A study of the wetting of metal surface in order to understand the process controlling atmospheric corrosion10.1149/1.1809596 ↗
9. Comparative study on corrosion behavior of Cu and Sn under UV light illumination in chloride-containing borate buffer solution10.1016/j.corsci.2021.109471 ↗
10. Atmospheric corrosion of Cu during constant deposition of NaCl10.1149/2.037308jes ↗
11. Illumination effects on the stability of the passive film on iron10.1016/0013-4686(94)00341-W ↗
12. Hole annihilation vs. induced convection: breakdown of different contributions to the photocorrosion mechanism of oxide-covered iron10.1016/j.corsci.2021.109426 ↗
13. Uniform and pitting corrosion events induced by SCN-anions on Al alloys surfaces and the effect of UV light10.1016/j.electacta.2010.12.045 ↗
14. Influence of uv light on passive behavior of the 304 stainless steel in acid solution10.1016/j.jpcs.2013.01.005 ↗
15. Photo-inhibition of pitting corrosion on types 304 and 316 stainless steels in chloride-containing solutions10.1016/0013-4686(96)00178-8 ↗
16. Influence of uv light on the passive behavior of SS316-effect of prior illumination10.1016/0013-4686(96)00177-6 ↗
17. Effect of UV illumination on the NaCl-induced atmospheric corrosion of pure zinc10.1149/2.015406jes ↗
18. Atmospheric corrosion of Cu during constant deposition of NaCl10.1149/2.037308jes ↗
19. Study on the mechanism of the photoelectrochemical effect on the initial NaCl-induced atmospheric corrosion process of pure copper exposed in humidified pure air10.1149/2.0771810jes ↗
20. The role of UV illumination on the initial atmospheric corrosion of 09CuPCrNi weathering steel in the presence of NaCl particles10.1016/j.corsci.2014.07.013 ↗
21. The role of the photovoltaic effect of γ-FeOOH and β-FeOOH on the corrosion of 09CuPCrNi weathering steel under visible light10.1016/j.corsci.2015.01.019 ↗
22. Models for the discussion of the photo-electrochemical response of oxide layers on metals10.1016/0010-938X(89)90034-6 ↗
23. Corrosion trend on Q450 weathering steel deposited with Na2SO4, NaCl under ultraviolet light illumination10.1016/j.jiec.2021.07.013 ↗
24. Effect of UV Illumination on the NaCl-induced atmospheric corrosion of pure zinc10.1149/2.015406jes ↗
25. Comparative study on corrosion behavior of Cu and Sn under UV light illumination in chloride-containing borate buffer solution10.1016/j.corsci.2021.109471 ↗
26. Investigation of photo-induced corrosion of copper in aqueous solution based on point defect model10.1016/j.matchemphys.2020.123648 ↗
27. Photo-induced corrosion or protection: determining the charge transfer in the semiconductor-metal heterojunction10.1016/j.jallcom.2019.152746 ↗
28. Physicochemical and photocatalytic activity of needle-like γ-FeOOH/Halloysite10.1016/j.inoche.2023.111033 ↗
29. Effect of γ-FeOOH and γ-Fe2O3 on the corrosion of Q235 carbon steel under visible light10.1149/2.0301503jes ↗
30. The evolution of the corrosion mechanism of structural steel exposed to the urban industrial atmosphere for seven years10.3390/app13074500 ↗
31. The influence of copper and chromium on the semiconducting behaviour of passive films formed on weathering steels10.1016/j.tsf.2006.05.011 ↗
32. The function of Cr on the rust formed on weathering steel performed in a simulated tropical marine atmosphere environment10.1016/j.conbuildmat.2021.122298 ↗
33. Corrosion of high-strength steel in 3.5% NaCl solution under hydrostatic pressure: understanding electrochemical corrosion with tensile stress coupling10.1016/j.corsci.2023.111204 ↗
34. Corrosion of high-strength steel in 3.5% NaCl solution under hydrostatic pressure: initial corrosion with tensile stress coupling10.1016/j.corsci.2023.111229 ↗
35. Elastic stress impacting on the rust layer of S450EW weathering steel through magnetomechanical effect10.1016/j.corsci.2021.109242 ↗
36. Effect of Cl− and rust layer on stress corrosion cracking behavior of X100 steel base metal and heat-affected zone in marine alternating wet/dry environment10.1016/j.matchemphys.2021.124826 ↗
37. Semiconducting properties of passive films and corrosion layers on weathering steel10.1016/j.electacta.2020.136697 ↗
38. The influence of copper and chromium on the semiconducting behaviour of passive films formed on weathering steels10.1016/j.tsf.2006.05.011 ↗
39. Bainitic reaction and microstructure evolution in two normalized and tempered steels designed for service at elevated temperatures10.1515/adms-2017-0019 ↗
40. Photo-electrochemical studies of the local dissolution of a hydrogen-charged X80 steel at crack-tip in a near-neutral pH solution10.1016/j.electacta.2010.05.002 ↗
41. ASTM Standart G30, Standard Practice for Making and Using U-Bend Stress Corrosion Test Specimens, West Conshohocken, PA, 2009. Reference to a chapter in an edited book:
42. Bard · 2012
43. Bard · 2001
44. The function of Cr on the rust formed on weathering steel performed in a simulated tropical marine atmosphere environment10.1016/j.conbuildmat.2021.122298 ↗
45. Influence of outer rust layers on corrosion of carbon steel and weathering steel during wet – dry cycles10.1016/j.corsci.2014.01.016 ↗
46. The atmospheric corrosion kinetics of low carbon steel in a tropical marine environment10.1016/j.corsci.2010.01.022 ↗
47. The role of rusts in corrosion and corrosion protection of iron and steel10.1016/j.corsci.2008.03.008 ↗
48. Cao · 2008 · 258
49. Morphology controlled synthesis of Co(OH)2/TiO2 p-n heterojunction photoelectrodes for efficient photocathodic protection of 304 stainless steel10.1016/j.apsusc.2020.148002 ↗