Corrosion and hydrogen absorption of commercially pure zirconium in acid fluoride solutions

Ken’ichi Yokoyama, Daisuke Yamada, Jun’ichi Sakai

Corrosion Science· Volume 73
Publisher page

Abstract

Abstract The corrosion and hydrogen absorption of commercially pure zirconium have been investigated in acidulated phosphate fluoride (APF) solutions. Upon immersion in 2.0% APF solution of pH 5.0 at 25 °C, a granular corrosion product (Na 3 ZrF 7 ) deposits over the entire side surface of the specimen, thereby inhibiting further corrosion. In 0.2% APF solution, marked corrosion is observed from the early stage of immersion; no deposition of the corrosion product is observed by scanning electron microscopy. A substantial amount of hydrogen absorption is confirmed in both APF solutions by hydrogen thermal desorption analysis. The amount of absorbed hydrogen of the specimen immersed in the 2.0% APF solution is smaller than that in the 0.2% APF solution in the early stage of immersion. The hydrogen absorption behavior is not always consistent with the corrosion behavior. Hydrogen thermal desorption occurs in the temperature range of 300–700 °C for the specimen without the corrosion product. Under the same immersion conditions, the amount of absorbed hydrogen in commercially pure zirconium is smaller than that in commercially pure titanium as reported previously. The present results suggest that commercially pure zirconium, compared with commercially pure titanium, is highly resistant to hydrogen absorption, although corrosion occurs in fluoride solutions.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Nuclear Materials and Properties · Fusion materials and technologies · Hydrogen embrittlement and corrosion behaviors in metals

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (60)

Show source-provided references
1. Accelerated oxide grown on titanium implants during autoclaving caused by fluorine contamination10.1016/0142-9612(85)90033-X ↗
2. The effect of oral topical fluorides on the surface of commercially pure titanium
3. Effect of fluoride concentration and pH on corrosion behavior of titanium for dental use10.1177/00220345990780091201 ↗
4. Electrochemical impedance spectroscopy study of strained titanium in fluoride media10.1016/S0013-4686(02)00079-8 ↗
5. Effects of fluoride concentration and elastic tensile strain on the corrosion resistance of commercially pure titanium10.1016/S0142-9612(01)00079-5 ↗
6. Influence of fluoride content and pH on the corrosion resistance of titanium and its alloys10.1016/S0142-9612(01)00328-3 ↗
7. Fracture associated with hydrogen absorption of sustained tensile-loaded titanium in acid and neutral fluoride solutions10.1002/jbm.a.20067 ↗
8. Hydrogen absorption of titanium in acidic fluoride solutions10.1016/j.msea.2004.05.059 ↗
9. Hydrogen absorption of titanium and nickel–titanium alloys during long-term immersion in neutral fluoride solution10.1002/jbm.b.30485 ↗
10. Effects of potential on hydrogen absorption and desorption behaviors of titanium in neutral fluoride solutions10.1016/j.jallcom.2006.05.036 ↗
11. Cytotoxicity evaluation of 43 metal salts using murine fibroblasts and osteoblastic cells10.1002/(SICI)1097-4636(199802)39:2<331::AID-JBM22>3.0.CO;2-E ↗
12. Compositional change in surface of Ti–Zr alloys in artificial bioliquid10.2320/jinstmet1952.56.10_1168 ↗
13. Surface oxide films on titanium alloys regeneration in Hanks’ solution10.2320/matertrans.43.3000 ↗
14. Apatite formation on zirconium metal treated with aqueous NaOH10.1016/S0142-9612(01)00110-7 ↗
15. Corrosion behavior of zirconium based alloys in simulated body fluids10.4028/www.scientific.net/MSF.561-565.1489 ↗
16. Difference in surface reactions between titanium and zirconium in Hanks’ solution to elucidate mechanism of calcium phosphate formation on titanium using XPS and cathodic polarization10.1016/j.msec.2009.01.016 ↗
17. Cathodic alkaline treatment of zirconium to give the ability to form calcium phosphate10.1016/j.actbio.2010.05.010 ↗
18. The influence of surface energy of titanium–zirconium alloy on osteoblast cell functions in vitro10.1002/jbm.a.33013 ↗
19. Pore structures and mechanical properties of the porous Zr–Ti implants10.4012/dmj.6.175 ↗
20. Mechanical properties of the binary titnaium–zirconium alloys and their potential for biomedical materials10.1002/jbm.820290805 ↗
21. Tissue integration of a new titanium–zirconium dental implant: a comparative histologic and radiographic study in the canine10.1902/jop.2010.100737 ↗
22. A pilot study to evaluate the success and survival rate of titanium–zirconium implants in partially edentulous patients: results after 24months of follow-up10.1111/j.1600-0501.2011.02231.x ↗
23. Titanium–zirconium alloy narrow diameter implants (Straumann Roxolid®) for the rehabilitation of horizontally deficient edentulous ridges: prospective study on 18 consecutive patients10.1111/j.1600-0501.2011.02296.x ↗
24. Evaluation of a new titanium–zirconium dental implant: a biomechanical and histological comparative study in the mini pig10.1111/j.1708-8208.2010.00289.x ↗
25. SCC of zirconium and its alloys in nitric acid10.5006/1.3580832 ↗
26. Zirconium alloy corrosion
27. The hydrogen embrittlement of α-zirconium – a review10.1016/0022-5088(66)90003-8 ↗
28. Hydrides and delayed hydrogen cracking in zirconium and its alloys10.1179/imr.1983.28.1.92 ↗
29. Environmentally-induced cracking of zirconium alloys – a review10.1016/0022-3115(90)90321-D ↗
30. Some thoughts on the mechanisms of in-reactor corrosion of zirconium alloys10.1016/j.jnucmat.2004.09.029 ↗
31. Corrosion of Zirconium and Zirconium Alloys
32. A reaction rate study of the corrosion of low-hafnium zirconium in aqueous hydrofluoric acid solutions10.1149/1.2428774 ↗
33. The electrochemistry of the dissolution of zirconium in aqueous solutions of hydrofluoric acid10.1149/1.2426074 ↗
34. The anodic polarization behavior of metals in hydrogen fluoride10.1016/S0010-938X(67)80068-4 ↗
35. Untersuchungen über periodischepotentialschwankungen des zirkons in NaF-Lösungen – I. Experimentelle ergebnisse10.1016/S0010-938X(70)80062-2 ↗
36. Dissolution of zirconium in aqueous solutions of ammonium fluoride and hydrofluoric acid
37. Halogen stress corrosion cracking of zircaloy-4 tubing10.1016/0022-3115(75)90137-3 ↗
38. Anomalous corrosion of Zr in boiling hydrochloric acid solutions
39. Evaluation of hydrogen absorption properties of Ti-0.2 mass% Pd alloy in fluoride solutions10.1016/j.jallcom.2005.03.048 ↗
40. Fracture of sustained tensile-loaded Ti-0.2% Pd alloy in acid and neutral fluoride solutions10.1016/j.msea.2005.12.006 ↗
41. The crystal structures of Na3ZrF7 and Na3HfF710.1107/S0365110X59000470 ↗
42. Susceptibility to delayed fracture of alpha–beta titanium alloy in fluoride solutions10.1016/j.corsci.2004.08.007 ↗
43. Relationship between hydrogen absorption and corrosion behavior of Ti–6Al–4V alloy immersed in acidic fluoride solutions10.2320/matertrans.MRA2008481 ↗
44. Zirconium–hydrogen phase system
45. The precipitation of zirconium hydride in zirconium and zircaloy-210.1016/0022-3115(72)90021-9 ↗
46. In situ synthesis of zirconia nanotube crystallines by direct anodization10.1016/j.corsci.2008.01.026 ↗
47. Enhancement of the capability of hydroxyapatite formation on Zr with anodic ZrO2 nanotubular arrays via an effective dipping pretreatment10.1002/jbm.b.31898 ↗
48. Distribution and thermal desorption behavior of hydrogen in titanium alloys immersed in acidic fluoride solutions10.1016/j.jallcom.2004.12.041 ↗
49. Hydride formation by high temperature cathodic hydrogen charging method and its effect on the corrosion behavior of zircaloy-4 tubes in acid solution10.1016/S0022-3115(98)00180-9 ↗
50. Hydride dissociation and hydrogen evolution behavior of electrochemically charged pure titanium10.1016/0925-8388(95)01565-5 ↗
51. An anelastic study of the diffusion coefficient of hydrogen in α-zirconium10.1016/0022-5088(76)90044-8 ↗
52. Fracture initiation at hydrides in zirconium10.1007/BF02664999 ↗
53. Arsene · Metall. Mater. Trans. A · 2003 · 34A · 55310.1007/s11661-003-0091-3 ↗
54. Hydride formation during cathodic polarization of Ti – I. Effect of current density on kinetics of growth and composition of hydride10.1016/S0010-938X(72)80014-3 ↗
55. Hydride formation during cathodic polarization of Ti – II. Effect of temperature and pH of solution on hydrogen growth10.1016/S0010-938X(74)80063-6 ↗
56. The effect of Pt and Pd alloying additions on the corrosion behavior of titanium in fluoride-containing environments10.1016/j.biomaterials.2004.07.022 ↗
57. Corrosion behavior and surface characterization of Ti–20Cr alloy in a solution containing fluoride10.4012/dmj.23.379 ↗
58. Corrosion resistance of titanium–silver alloys in an artificial saliva containing fluoride ions10.1002/jbm.b.30206 ↗
59. Ti–Ge binary alloy system developed as potential dental materials10.1002/jbm.b.32793 ↗
60. Inhibition of hydrogen embrittlement of Ni–Ti superelastic alloy in acid fluoride solution by hydrogen peroxide addition10.1002/jbm.a.33124 ↗