Impact of temperature excursion on stress corrosion cracking of stainless steels in chloride solution

The impact of a temperature excursion on the subsequent stress corrosion crack growth at the normal operating temperature has been investigated for 321 stainless steel (UNS32100) and 316L stainless steel (UNS31603) using precracked compact tension specimens. Although the data are preliminary the indication is that once crack growth has initiated in 321 SS at the elevated temperature, 130 °C in this study, the crack growth may be sustained at the lower temperature (40 °C), at least over the exposure time of about 700 h. However, the growth rate of 316L SS at the lower temperature was significantly lower than for 321 SS and tended to zero after 2000 h. For the 316 SS a temperature transient should not impact on structural integrity, provided it is short in duration.