Effect of rapid solidification on the microstructure and corrosion behaviour of Al–Zn–Mg based material

The corrosion behaviour of Al-5Zn-3Mg-0.6Cu-0.8Zr-0.25Cr-0.15Ni-0.15Ti alloys, produced by traditional and powder technologies, with similar thermo-mechanical treatments, in 3% sodium chloride solution, has been examined by electrochemical methods, scanning electron microscopy, transmission electron microscopy and X-ray microanalysis. The alloys reveal similar precipitation but of different shape, size and distribution; further, both alloys experience localized corrosion. Copper-rich precipitates initiate the dissolution of surrounding particles, enriched in Zn and Mg. As a result, the surface is enriched with other alloying elements after a full polarisation run. Cast material has lower corrosion properties because of the higher heterogeneity of the structure. The structure heterogeneity of the cast material involves a more non-uniform distribution of the precipitates, larger Zn- and Mg-rich particles, and depletion of the matrix and areas around the precipitates by alloying elements compared with the powder material. © 2006 Elsevier Ltd. All rights reserved.