Stress corrosion cracking of type 304 austenitic stainless steel in sulphuric acid solution including sodium chloride and chromate

Abstract The stress corrosion cracking (SCC) of a commercial austenitic stainless steel type 304 was investigated as functions of chloride concentration, chromate concentration and test temperature under a constant applied stress condition in 0.82 kmol/m3 sulphuric acid solution by using a constant load method. From the dependence of the three parameters ( l ss , steady state elongation rate; tss, transition time; tf, time to failure) obtained from corrosion elongation curve on chloride/chromate concentrations and test temperature, a parameter for predicting time to failure and critical values of chromate concentration and test temperature, below which little SCC takes place, were estimated. In addition, a transgranular SCC mechanism was qualitatively inferred and then the effect of chromate and chloride on SCC behavior was discussed.