Influence of current density in anodizing of an Al–W alloy

Abstract The influences of current density in development of amorphous, barrier anodic films on a metastable, solid solution, Al–6.5at.%W alloy is examined, with focus on enrichments in the alloy, oxidation processes at the alloy/film interface and migration of species in the film. The films were formed at current densities between 0.01–100 mA cm −2 in sodium tungstate electrolyte and examined by transmission electron microscopy and Rutherford backscattering spectroscopy. Enrichments of tungsten in the alloy develop at each of the selected current densities, with enrichments in the range 2–4×10 15 W atoms cm −2 . Incorporation of tungsten species into the films at the alloy/film interface proceeds non-uniformly, with cycles of local enrichment of the alloy, oxidation of the enriched tungsten and subsequent depletion of the alloy. The tungsten species migrate more slowly than Al 3+ ions, leading to layering of the film composition. The cyclic incorporation of tungsten species into the film and the migration of tungsten species within the film are similar for the selected current densities, at the resolution of the experiments.