High temperature oxidation of Fe-Cr alloys in atmospheres containing 2.0 % SO2 + 5.0 % O2
Source abstract
Abstract
Abstract In this study, we examined the microstructure and composition of the scales formed after exposures from 825 °C through to 950 °C for 60 min in the atmosphere containing 2.0 % SO2 + 5.0 % O2 gas. The scale composition after oxidation mainly depends on temperature but not on the Cr content. The FeS formation temperature was 915 ℃, while its melting temperature was 925 ℃. Two mechanisms of the FeS formation are proposed. The eutectic transformation of molten FeS occurred during the subsequent cooling process, resulting in lamellar FeS + Fe-S-O compounds. The study indicated that Cr exhibits oxidation but not sulfidation resistance.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Metallurgical Processes and Thermodynamics · Thermal and Kinetic Analysis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (44)
Show source-provided references
1. Young · 2016
2. Factors affecting the oxidation mode of stainless steels10.1179/mht.2000.17.2.016 ↗
3. Temperature and water vapour effects on the cyclic oxidation behaviour of Fe–Cr alloys10.1016/j.corsci.2010.04.026 ↗
4. Breakaway oxidation of austenitic stainless steels induced by alloyed sulphur10.1016/j.corsci.2015.01.007 ↗
5. Oxidation of a Fe–18Cr–8Ni austenitic stainless steel at 850°C in O2: microstructure evolution during breakaway oxidation10.1016/j.corsci.2016.10.029 ↗
6. Characterization of refractory steel oxidation at high temperature10.1016/j.corsci.2017.12.029 ↗
7. Influence of oxidation temperature and Cr content on the ddhesion and microstructure of scale on low Cr steels10.1007/s11085-009-9167-9 ↗
8. Phase transformation behavior of oxide scale on plain carbon steel containing 0.4 wt.% Cr during continuous cooling10.2355/isijinternational.ISIJINT-2018-365 ↗
9. Oxide scales on hot-rolled steel strips
10. Relationship between entry temperature and properties of thermal oxide scale on low carbon steel strips
11. Effects of process parameters on mechanical adhesion of thermal oxide scales on hot-rolled low carbon steels10.1007/s11085-013-9370-6 ↗
12. The effect of water vapour on the oxidation of high speed steel, kinetics and scale adhesion10.1007/s11085-010-9220-8 ↗
13. Water vapour effects on Fe–Cr alloy oxidation10.1007/s11085-009-9183-9 ↗
14. Enhanced oxidation of the 9%Cr steel P91 in water vapour containing environments10.1016/j.corsci.2006.02.002 ↗
15. Chromium Volatilization rates from Cr2O3 scales into flowing gases containing water vapor10.1007/s11085-006-9030-1 ↗
16. Effect of SO2 on oxidation of metallic materials in CO2/H2-rich gases relevant to oxyfuel environments10.1002/maco.201307306 ↗
17. Real time observation of high temperature oxidation and sulfidation of Fe-Cr model alloys10.1002/maco.201709892 ↗
18. Elucidation of orientation relations between Fe-Cr alloys and corrosion products after high temperature SO2 corrosion10.1016/j.corsci.2020.108809 ↗
19. Oxidation of iron in atmospheres containing sulphur dioxide
20. Corrosion of iron in sulfur dioxide at 0.1 MPa10.1007/BF01046847 ↗
21. The influence of chromium on early high temperature corrosion of ferritic alloys under SO2 atmosphere10.1080/09603409.2018.1446705 ↗
22. High temperature corrosion of iron in O2 + 4% SO2/SO3 at 500–800°C10.1016/0921-5093(89)90725-9 ↗
23. Effect of sulphur on the oxidation behaviour of possible construction materials for heat exchangers in oxyfuel plants in the temperature range 550–700°C10.1007/s11085-017-9809-2 ↗
24. High temperature corrosion of Fe-Cr-(Mn/Si) alloys in CO2-H2O-SO2 gases10.1016/j.corsci.2016.07.026 ↗
25. Differential scanning calorimetry study of peritectic steel grades10.1007/s10973-014-4302-5 ↗
26. The problem of sulfur in high-temperature corrosion10.1007/BF01046727 ↗
27. Self-diffusion of iron and sulfur in ferrous sulfide10.1007/BF00603390 ↗
28. In situ observation of whiskers, pyramids and pits during the high-temperature oxidation of metals10.1007/BF00659470 ↗
29. The growth of ferrous sulfide on iron10.5006/0010-9312-13.10.79 ↗
30. Hauffe · 1965
31. C.W. Bale, A.D. Pelton, W.J. Thompson, G. Eriksson, K. Hack, P. Chartrand, S. Decterov, I.H. Jung, J. Elancon, S. Petersen, FactSage 6.4 (database: FACT), Copyright Thermfact and GTT-Technologies 1976–2013.
32. Influence of SO2 on the oxidation of 304L Steel in O2+40%H2O at 600℃10.1007/s11085-008-9096-z ↗
33. The Effect of traces of SO2 on iron oxidation: a microstructural study10.1007/s11085-007-9051-4 ↗
34. Mechanism of simultaneous sulphidation and oxidation of Fe-20Cr and Fe-20Cr-12Ni and the failure of protective chromia scales10.1016/0921-5093(89)90729-6 ↗
35. High temperature reaction of Fe in SO210.1016/0010-938X(75)90029-3 ↗
36. Birks · 2006 · 16
37. Influence of Cr and Ni on high-temperature corrosion behavior of ferritic ductile cast iron in air and exhaust gases10.1007/s11085-013-9389-8 ↗
38. Oxidation after breakdown of the chromium-rich scale on stainless steels at high temperature: internal oxidation10.1007/s11085-016-9610-7 ↗
39. Oxidation behavior of high-speed steel used for hot rolls10.1007/s11085-016-9618-z ↗
40. The mechanical property of the oxide scale on Fe-Cr alloy steels10.1016/j.jallcom.2012.09.064 ↗
41. Effects of cerium and manganese on corrosion of Fe–Cr and Fe–Cr–Ni alloys in Ar–20CO2 gas at 818°C10.1016/j.corsci.2013.06.046 ↗
42. Effects of cerium and manganese on corrosion of Fe-Cr and Fe-Cr-Ni alloys in Ar-20CO2 and Ar-20CO2-20H2O gases at 650℃10.1016/j.corsci.2015.08.012 ↗
43. The influence of chromium on early high temperature corrosion of ferritic alloys under SO2 atmosphere10.1080/09603409.2018.1446705 ↗
44. Corrosion of Fe-9Cr-(Mn/Si) alloys in CO2-H2O-SO2 gases10.1016/j.corsci.2015.05.040 ↗