Creep rupture of a Ni-Fe based model alloy under simulated fireside corrosion in coal-fired boilers
Source abstract
Abstract
The influence of fireside corrosion on creep rupture of a Ni-Fe based model alloy was investigated by comparing the rupture life, fractography and microstructure of specimens in fireside corrosion and air. Results showed that the rupture life at 140 MPa in fireside corrosion is only 40% of that in air. The internal sulfidation along grain boundaries promoted the initiation of intergranular cracks, and was responsible for the premature rupture. The surface collapse in fireside corrosion was attributed to the outward propagation of internal cracks, while surface cracks in air originated from the formation of recrystallized grains in the surface layer.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High Temperature Alloys and Creep · High-Temperature Coating Behaviors · Advanced Materials Characterization Techniques
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (62)
Show source-provided references
1. U.S. Program on materials technology for ultra-supercritical coal power plants10.1361/10599490524039 ↗
2. Overview of the efficient tehnologies for power generation based on coal
3. Behaviour of alloy 617 OCC under hot corrosion conditions encountered in boilers in A-USC power plants10.1007/s12666-018-1543-1 ↗
4. Creep and fatigue behavior in micro-alloyed steels - a review10.1515/htmp-2012-0177 ↗
5. Fireside and steamside corrosion of alloys for USC plants10.1016/j.ijhydene.2006.08.038 ↗
6. The dynamic creep rupture of a secondary superheater tube in a 43MW coal-fired boiler by the decarburization and multilayer oxide scale buildup on both sides10.1016/j.engfailanal.2015.03.018 ↗
7. Research and development of heat-resistant materials for advanced USC power plants with steam temperatures of 700 °C and above10.15302/J-ENG-2015031 ↗
8. Weldability and weld performance of candidate nickel base superalloys for advanced ultrasupercritical fossil power plants part I: fundamentals10.1179/1362171815Y.0000000035 ↗
9. Development of strong, oxidation and corrosion resistant nickel-based superalloys: critical review of challenges, progress and prospects10.1080/09506608.2018.1516713 ↗
10. Creep and LCF behaviors of newly developed advanced heat resistant austenitic stainless steel for A-USC
11. Investigation on high-temperature corrosion behavior of Inconel 600 under So2-Bearing Gas at 650°C
12. Development of creep-resistant steels and alloys for use in power plants
13. Microstructural evolution and mechanical properties of Grades 23 and 24 creep strength enhanced ferritic steels10.1080/09506608.2016.1207008 ↗
14. The effect of service on microstructure and mechanical properties of HR3C heat-resistant austenitic stainless steel10.3390/ma13061297 ↗
15. Long term creep properties and microstructure of SUPER304H, TP347HFG and HR3C for A-USC boilers10.1179/174892408X382860 ↗
16. A newly developed wrought Ni–Fe–Cr-based superalloy for advanced ultra-supercritical power plant applications beyond 700 °C10.1007/s40195-015-0298-5 ↗
17. Microstructure stability and mechanical properties of a new low cost hot-corrosion resistant Ni-Fe-Cr based superalloy during long-term thermal exposure10.1016/j.matdes.2014.12.030 ↗
18. Microstructural stability and tensile properties of a new gamma'-hardened Ni-Fe-base superalloy10.1016/j.mtla.2021.101061 ↗
19. Evolution of the microstructure and microhardness of a new wrought Ni-Fe based superalloy during high temperature aging10.1016/j.jallcom.2015.04.184 ↗
20. Microstructural stability of long-term aged wrought Ni-Fe-based superalloys10.1080/02670836.2017.1282668 ↗
21. Creep deformation and rupture mechanism of an advanced wrought Ni-Fe-based superalloy for 700 degrees C class A-USC steam turbine rotor application10.1016/j.jallcom.2016.06.120 ↗
22. Microstructure and properties of Ni-Fe-base Superalloy for 700 ℃ advanced ultra supercritical unit final superheater
23. Microstructural evolution and compressive deformation of a new Ni-Fe base superalloy after long term thermal exposure at 700 degrees C10.1016/j.msea.2014.09.095 ↗
24. Tensile and creep deformation of a newly developed Ni-Fe-based superalloy for 700 degrees C advanced ultra-supercritical boiler applications10.1007/s12540-015-4627-z ↗
25. Creep deformation behavior of a novel precipitate-hardened Ni-Fe-base superalloy at 750 degrees C10.1007/s11661-019-05611-4 ↗
26. Investigation on the tensile deformation mechanisms in a new Ni-Fe-base superalloy HT700T at 750 degrees C10.1016/j.jallcom.2020.154012 ↗
27. A new wrought NiFe-base superalloy for advanced ultra-supercritical power plant applications beyond 700 degrees C10.1016/j.matlet.2013.07.060 ↗
28. Effect of steamside oxidation and fireside corrosion degradation processes on creep life of service exposed boiler tubes10.1016/j.ijpvp.2016.05.001 ↗
29. Effect of sulfur and chlorine on fireside corrosion behavior of Inconel 740H superalloy10.1515/htmp-2016-0186 ↗
30. (!!! INVALID CITATION !!! [11, 29, 30]).
31. The influence of iron and cobalt on the type II hot corrosion behavior of NiCr model alloys10.1002/maco.201911376 ↗
32. Severe Hot Corrosion of the Superalloy IN718 in Mixed Salts of Na2SO4 and V2O5 at 700 °C10.1007/s11665-018-3501-9 ↗
33. Investigation of fireside corrosion of austenitic heat-resistant steel 10Cr18Ni9Cu3NbN in ultra-supercritical power plants10.1016/j.engfailanal.2019.02.048 ↗
34. Corrosion behavior of the Ni–Cr–Fe base superalloy GH984G in a synthetic coal ash and flue gas environment10.1007/s40195-017-0614-3 ↗
35. The transition from internal to external oxidation and the formation of interruption bands in silver-indium alloys10.1016/0001-6160(61)90103-1 ↗
36. Hot corrosion of a single crystal Ni-base superalloy by Na-Salts at 900°C10.1007/s11085-006-9004-3 ↗
37. Hot corrosion of metals and alloys10.1007/s11085-011-9254-6 ↗
38. Corrosion and creep behavior of a Ni-base alloy in supercritical-carbon dioxide environment at 650 °C10.1016/j.corsci.2020.108843 ↗
39. Interaction of hot corrosion and creep in Alloy 61710.1016/j.engfailanal.2016.03.012 ↗
40. An investigation of oxidation/hot corrosion-creep interaction at 800 °C in a Ni-base superalloy coated with salt mixture deposits of Na2SO4-NaCl-NaVO310.1016/j.corsci.2018.11.029 ↗
41. Subsurface microstructural degeneration of Super304H boiler tube under the synergy of fireside corrosion and creep stress10.1016/j.corsci.2022.110250 ↗
42. Impact of fireside corrosion on creep rupture life and oxide scale structure of Super304H boiler tube10.5006/4277 ↗
43. Effect of isothermal compression and subsequent heat treatment on grain structures evolution of Al-Mg-Si alloy10.1007/s11771-021-4801-z ↗
44. Effects of temperature and load on fretting fatigue induced geometrically necessary dislocation distribution in titanium alloy10.1016/j.msea.2020.140308 ↗
45. Influence of γ’ precipitate on deformation and fracture during creep in PM nickel-based superalloy10.1016/j.pnsc.2020.12.008 ↗
46. Modelling creep-corrosion interactions in nickel-base superalloys10.1080/02670836.1987.11782266 ↗
47. Static and dynamic aspects of coupling between creep behavior and oxidation on MC2 single crystal superalloy at 1150 °C10.1016/j.actamat.2005.05.018 ↗
48. Reid · 1971
49. Effect of temperature on coal ash hot corrosion resistance of Inconel 740 superalloy10.1016/j.corsci.2014.01.020 ↗
50. Simulated fireside corrosion behavior of a wrought Ni-Fe-based superalloy for 700 degrees C-Class ultra-supercritical power plant applications10.1007/s11665-019-04515-z ↗
51. Precipitate evolution during aging and its individual role on high-temperature hot corrosion response in Alloy 61710.1016/j.jallcom.2021.159499 ↗
52. On the mechanism of the oxidation of nicral-base alloys in air and air containing sulfur-dioxide10.1007/BF00664494 ↗
53. Effect of special grain boundary on hot corrosion path in Incoloy825 alloy10.1007/s10853-022-07580-3 ↗
54. Short-term corrosion behavior of polycrystalline Ni3Al-based superalloy in sulfur-containing atmosphere10.1016/j.intermet.2021.107446 ↗
55. The effect of cooling rate on the γ' composition, morphology and corrosion behaviour of IN738LC10.1016/j.corsci.2018.12.036 ↗
56. Oxidation behavior of the directionally solidified Ni-base superalloy DS951 in air10.1007/s11085-005-8529-1 ↗
57. Influence of stress and secondary orientation on the oxidation-induced dynamic recrystallization behavior of a Ni-based single crystal superalloy10.1016/j.jallcom.2017.02.251 ↗
58. Environmental effect on mechanical properties of a gamma-prime strengthened nickel-based alloy: effect of the surface oxidation and formation of gamma-prime free zones10.1016/j.msea.2019.03.013 ↗
59. Effects of corrosion in supercritical CO2 on the microstructural evolution in 800H alloy10.1007/s11085-018-9852-7 ↗
60. Effect of surface finishing on the oxidation characteristics of a Fe-21Cr-32Ni alloy in supercritical carbon dioxide10.1016/j.corsci.2021.110019 ↗
61. Analysis of creep behavior of welded joints of P91 steel at 600 °C10.1016/j.ijpvp.2019.02.008 ↗
62. Isothermal oxidation behavior of micro-regions in multiphase Ni3Al-based superalloys10.1016/j.matchar.2020.110748 ↗