Corrosion of Al–Sn–Bi alloys in alcohols at high temperatures. Part II: Effect of anodizing on corrosion

Nine kinds of Al alloys were anodized to form porous anodic oxide films, and then anodized specimens were immersed in 2-(2-(2-methoxyethoxy)ethoxy)ethanol (MEEE) and 2-(2-(2-butoxyethoxy)ethoxy)ethanol (BEEE) at 415 K. Al-1.0%Sn-1.0%Bi alloy was corroded severely in both BEEE and MEEE, whereas other 8 alloys showed no corrosion. The corrosion proceeded under the anodic oxide films through cracks formed in the film. Cathodic polarization in Cu electroplating solution after corrosion suggested that the crack formation during immersion in hot MEEE is due to thermal expansion of the substrate and Sn and Bi containing particles included in the anodic oxide film.